This work deals with preparation of zeolite 5A from Dewekhala kaolin clay in Al-Anbar region for drying and desulphurization of liquefied petroleum gas. The preparation of zeolite 5A includes treating kaolin clay with dilute hydrochloric acid 1N, treating metakaolin with NaOH solution to prepare 4A zeolite, ion exchange, and formation. For preparation of zeolite 4A, metakaolin treated at different temperatures (40, 60, 80, 90, and 100 °C) with different concentrations of sodium hydroxide solution (1, 2, 3, and 4 N) for 2 hours. The zeolite samples give the best relative crystallinity of zeolite prepared at 80 °C with NaOH concentration 3N (199%), and at 90 and 100°C with NaOH concentration solution 2N (184% and 189%, respectively). Zeolite 5A was prepared by ion exchange of zeolite 4A prepared at 90°C and 2N NaOH concentration with 1.5 N calcium chloride solution at 90 °C and 5 hours, the ion exchange percentage was 66.6%. The formation experiments included mixing the prepared powder of 5A zeolite with different percentages of kaolin clay, citric acid and tartaric acid to form an irregular shape of zeolite granules. Tartaric acid binder gives higher bulk crushing strength than that obtained by using citric acid binder with no significant difference in the surface area. 7.5 weight% tartaric acid binder has the higher bulk crushing strength 206 newton with surface area 267.4 m2/g. Kaolin clay binder with 15 weight% gives the highest surface area 356 m2/g with bulk crushing strength 123 newton, it was chose as the best binder for zeolite 5A. The prepared granules of 5A zeolite were used for the adsorption experiments of H2O, and H2S contaminants from LPG. Different flow rates of LPG (3, 4, and 5 liter/minute) were studied. It was found that H2O is the strongly adsorbed component and H2S is the weakly adsorbed component. The best flow rate in this work for H2O, and H2S adsorption is 5 liter/minute of LPG. The adsorption capacity for H2O was 7.547 g/g and for H2S was 1.734 g/g.
(13)
Modified unsaturated polyester (MUPE) was blended with Cellulose (Cls) and with ethyl cellulose (ECls) at ambient conditions in the presence of ethyl methyl ketone peroxide (EMKP) as hardener. The blends containing different weight percentages (5-25 %) of Cls or ECls. Mechanical properties (impact strength, hardness, and bending) and dielectric constant were determined. The results observed that Cls increases the impact strength, hardness, and dielectric constant and decreases the bending of the MUPS, while ECls causes an increase in the three mechanical behaviours and a decrease in the dielectric constant of the MU-PS.
Pure and doped barium titanate with Mg2+ ion at two molar ratios x= (5%, 10%) mol. has been synthesized by solid state reaction technique. The powders sintered at two temperatures (1000 °C and 1400 °C). An XRD technique was used in order to study the crystal structure of pure and doped barium titanate, which confirmed the formation of the tetragonal phase of BaTiO3, and then calculate the lattice parameters of pure and doped barium titanate, the addition of magnesium ion Mg2+ can lead to decreases lattice parameters.
Pure and doped barium titanate with Mg2+ ion at two molar ratios x= (5%, 10%) mol. has been synthesized by solid state reaction technique. The powders sintered at two temperatures (1000 °C and 1400 °C). An XRD technique was used in order to study the crystal structure of pure and doped barium titanate, which confirmed the formation of the tetragonal phase of BaTiO3, and then calculate the lattice parameters of pure and doped barium titanate, the addition of magnesium ion Mg2+ can lead to decreases lattice parameters.
The composites were manufactured and study the effect of addition of filler (nanoparticles SiO2 treated with silane) at different weight ratios (1, 2, 3, 4 and 5) %, on electrical, mechanical and thermal properties. Materials were mixed with each other using an ultrasound, and then pour the mixture into the molds to suit all measurements. The electrical characteristics were studied within a range of frequencies (50-1M) Hz at room temperature, where the best results were shown at the fill ratio (1%), and thermal properties at (X=3 %), the mechanical properties at the filler ratio (2%).
(11)
This study examined the adsorption behavior of anionic dye (orange G) from aqueous solution onto the raw and activated a mixture of illite, kaolinite and chlorite clays from area of Zorbatiya (east of Iraq).The chemical treatment involved alkali and acid activation. The alkali activation obtained by treated the raw clay (RC) with 5M NaOH (ACSO) and the acid activation founded by treated it with 0.25M HCl (ACH) and 0.25M (ACS). The thermal treatment carried out by calcination the produce activated clay at 750oC for acid activation and 105oC for alkali activation. Batch
... Show MoreA spectrophotometric determination of azithromycin was optimized using the simplex model. The approach has been proven to be accurate and sensitive. The analyte has been reacted with bromothymol blue (BTB) to form a colored ion pair which has been extracted in chloroform in a buffer medium of pH=4 of potassium phthalate. The extracted colored product was assayed at 415 nm and exhibited a linear quantification range over (1 - 20) g/ml. The excipients did not exhibit any interferences with the proposed approach for assaying azithromycin in pharmaceutical formulations.
Cubosomes are nanosized structures self-assembled nanostructured materials used for controlling the release of the entrapped drug molecule. Lornoxicam (LXM) is a potent analgesic nonsteroidal anti-inflammatory (NSAID) drug with a short half-life (3-4) hours. The present study aims to prepare LXM-loaded cubosomes with well-defined morphology, particle size, PDI, high entrapment efficiency, sustained drug release, and high zeta potential value, as a transdermal drug delivery system.
Twelve formulas of LXM-loaded cubosomal dispersions were prepared by a solvent dilution method using Glyceryl monooleate ( GMO) as polar lipid with different stabilizers as Pluronic® F127 or tween 80 and different types o
... Show More
(25)
(6)
The urban Gentrification is an inclusive global phenomenon to restructure the cities on the overall levels, the research to propose a specific study about the concept of urban Gentrification in the cities and showcasing its, specifications, and results, and how to deal with the variables that occur on cities through improvements as part of urban renewal projects, then the general axis of the research is shrinked, choosing the urban centers as the most important areas that deal with the urban Gentrification process due to its direct connection with indivisuals and social changes, and to process the specific axis of the research theses and studies will be showcased that discuss the topic in different research directions, and emerged