The present study revealed a low-cost process for utilizing desert sand for preparing nanosilica by sol-gel technique. This work required sodium hydroxide, concentrated hydrochloric acid, distillate water as raw materials, and Iraqi sand. Nanosilica sample was characterized by X-Ray Diffraction (XRD), scanning electron microscopy analysis (SEM), atomic force microscope(AFM), surface area (BET) method, and fourier transform infrared (FTIR). The XRD result of produced sample is referred to as amorphous silica, and it has a broad peak at 2Θ= 22° – 22.5 º. SEM showed spherical, agglomerated silica particles with a diameter range of 26.57–28.93 nm. In addition, the average particle size was 76.35nm, with a dimension range of 40-11

Undoped and Co-doped zinc oxide (CZO) thin films have been prepared by spray pyrolysis technique using solution of zinc acetate and cobalt chloride. The effect of Co dopants on structural and optical properties has been investigated. The films were found to exhibit maximum transmittance (~90%) and low absorbance. The structural properties of the deposited films were examined by x-ray diffraction (XRD). These films, deposited on glass substrates at (400? C), have a polycrystalline texture with a wurtzite hexagonal structure, and the grain size was decreased with increasing Co concentration, and no change was observed in lattice constants while the optical band gap decreased from (3.18-3.02) eV for direct allowed transition. Other parameters

This paper reports the effect of Mg doping on structural and optical properties of ZnO prepared by pulse laser deposition (PLD). The films deposited on glass substrate using Nd:YAG laser (1064 nm) as the light source. The structure and optical properties were characterized by X-ray diffraction (XRD) and transmittance measurements. The films grown have a polycrystalline wurtzite structure and high transmission in the UV-Vis (300-900) nm. The optical energy gap of ZnO:Mg thin films could be controlled between (3.2eV and 3.9eV). The refractive index of ZnO:Mg thin films decreases with Mg doping. The extinction coefficient and the complex dielectric constant were also investigate.

Ketoprofen is a non-steroidal anti-inflammatory (NSAID) drug with analgesic, anti-inflammatory, and antipyretic effects. It is widely used in the treatment of inflammation and pain associated with rheumatic disorders such as rheumatoid arthritis, osteoarthritis, and in soft tissue injury. The purpose of this study was to prepare an  oral disintegrating tablets of ketoprofen by simple method. The tablets were prepared by direct compression method and different ratios of various subliming agents or superdisintegrants were incorporated. Then these tablets were evaluated for hardness, friability, weight variation, water absorption ratio, disintegrating time and dissolution time. The results showed that Formula F11 batch had short disint

This work investigates the properties of polyvinyl alcohol (PVA) nanocomposite films with varying multi-walled carbon nanotube (MWCNT) content, ranging from 2 to 8 wt.%. The films were prepared using a solution casting method and characterized using UV-visible spectroscopy, optical microscopy, X-ray diffraction, and tensile tests. The prepared PVA/MWCNT nanocomposite films exhibited optical band gap values ranging from 3.5 eV to 5.3 eV. XRD analysis confirmed the semi-crystalline nature of these nanocomposites. Mechanical properties, including hardness, yield strength, ultimate tensile strength, and Young's modulus, were enhanced by increasing MWCNT content by up to 8%. Contact angle measurements showed an increase in hydrophobicity with in

In this work preparation of antireflection coating with single layer of MgO using pulsed laser deposition (PLD) method which deposit on glass substrate with different thicknesses (90 and 100) nm annealed at temperature 500 K was done.
The optical and structural properties (X-ray diffraction) have been determined. The optical reflectance was computed with the aid of MATLAB over the visible and near infrared region. Results shows that the best result obtained for optical performance of AR'Cs at 700 shots with thickness 90 nm nanostructure single layer AR'Cs and low reflection at wavelength 550 nm.