This work was conducted to study the ability of locally prepared Zeolite NaY for the reduction of sulfur compounds from Iraqi natural gas by a continuous mode adsorption unit. Zeolite Y was hydrothermally synthesized using abundant kaolin clay as aluminum precursor. Characterization was made using chemical analysis, XRD and BET surface area. Results of the adsorption experiments showed that zeolite Y is an active adsorbent for removal H2S from natural gas and other gas streams. The effect of temperature was found inversely related to the removal efficiency. Increasing bed height was found to increase the removal efficiency at constant flow rate of natural gas. The adsorption capacity was evaluated and its maximum uptake was 5.345 mg H2S/g z

The use of piezocatalysis with photocatalysis in the degradation of organic pollutants has become an attractive research field due to the enhanced synergistic effect of the two processes. Herein, binary composites of AgBr decorated onto Br-doped g-C3N4 in different weight percentages (AgBr content was varied from 10 wt% to 40 wt%) have been built as heterojunction piezo-photo catalysts with a highly efficient performance. The 20 wt%AgBr/Br-g-C3N4 catalysts showed synergistically improved piezo-photo catalytic decomposition toward Methylene blue (MB) under visible-light and sonication exposure in a simple constructed split-plate airlift contactor, completing 99.7 % degradation of MB within 60 min. The heterogeneous junction established among

The research includes the preparation of a new Schiff base(4-methyl-2-((2-phenyl hydrazineylidene)methyl)naphthalen-1-ol), which was subsequently, used to prepare a series of complexes using chlorides of Mn2+, Co2+, Cu2+, Cr3+, and Fe3+ ions. The synthesized compounds were characterized using various techniques such as elemental microanalysis (C.H.N), chloride content determination using Mohr’s method, FT-IR spectroscopy, UV-Visible, mass spectra, conductivity, DSC (Differential Scanning Calorimetry), and thermogravimetric analysis. Overall, the decay of the ligand and its metal complexes was recorded to determine their thermal stability and weight-loss profiles. The results indicated that ligand acts as a bidentate doner, coordinating wi

   Nanoparticles (NPs) have unique capabilities that make them an eye-opener opportunity for the upstream oil industry. Their nano-size allows them to flow within reservoir rocks without the fear of retention between micro-sized pores. Incorporating NPs with drilling and completion fluids has proved to be an effective additive that improves various properties such as mud rheology, filtration, thermal conductivity, and wellbore stability. However, the biodegradability of drilling fluid chemicals is becoming a global issue as the discharged wetted cuttings raise toxicity concerns and environmental hazards. Therefore, it is urged to utilize chemicals that tend to break down and susceptible to biodegradation. This research presents the pra

In this research prepared two composite materials , the first prepared from unsaturated polyester resin (UP) , which is a matrix , and aluminum oxide (Al2O3) , and the second prepared from unsaturated polyester resin and aluminum oxide and copper oxide (CuO) , the two composites materials (Alone and Hybrid) of percentage weight (5,10,15)% . All samples were prepared by hand layup process, and study the electrical and thermal conductivity. The results showed decrease electrical conductivity from (10 - 2.39) ×10-15 for (Up+ Al2O3) and from (10 - 2.06)×10-15 for (Up+ Al2O3+ CuO) .But increase thermal conductivity from( 0.17 - 0.505) for (Up+ Al2O3) and from (0.17 - 0.489) for (Up+ Al2O3+ CuO).

The DC electrical conductivity properties of Ge60Se40-xTex alloy with x = 0, 5, 10, 15 and 20). The samples were formed in the form of discs with the thickness of 0.25–0.30 cm and the diameter of 1.5 cm. Samples were pressed under a pressure of 6 tons per cm2 , using a ton hydraulic press. They were prepared after being pressed using a ton hydraulic press using a hydraulic press. Melting point technology use to preper the samples. Continuous electrical conductivity properties were recorded from room temperature to 475 K. Experimental data indicates that glass containing 15% Te has the highest electrical conductivity allowing maximum current through the sample compared to Lu with other samples. Therefore, it is found that the DC co

Background: Neutrophils destroy pathogens via phagocytosis. Neutrophils are effective innate and acquired immunity phagocytes. Low-density neutrophils are distinct neutrophil phenotypes linked to several systemic and infectious diseases. To our knowledge, low-density neutrophil phagocytosis in periodontitis has not been examined. Opsonized and non-opsonized fluorescent beads mixed with low-density neutrophils were gated and analyzed by flow cytometry to count cells that consumed at least one bead.

Aims of the Study: To estimate the potential impact of antibody (Ab)-labeled and non-labeled phagocytosis capacity of low-d