A tunable band pass filter based on fiber Bragg grating sensor using an in-fiber Mach-Zender interferometer with dual micro-cavities is presented. The micro-cavity was formed by splicing together a conventional single-mode fiber and a solid core photonic crystal fiber (SCPCF) with simple arc discharge technique. Different parameters such as arc power, length of the SCPCF and the overlap gap between samples were considered to control the fabrication process. The ellipsoidal air-cavity between the two fibers forms Fabry-Perot cavity. The diffraction loss was very low due to short cavity length. Ellipsoidal shape micro-cavities were experimentally achieved parallel to the propagation axis having dimensions of (24.92 – 62.32) μm of width

Air pollution from various sources is one of the most serious environmental problems, especially after pollutants are deposited on the surface of the soil and leaves of the plants and then transferred to the rest of the plant and entering food chains. The present study was conducted to determine the effects of air pollution on different biochemical parameters in Eucalyptus sp. and calculation the Air Pollution Tolerance Index. The selected plant leaves were collected from five sites, four of them within the city of Baghdad, namely Al-Jadriya, Al-Andlous, Al-Doura and close to the private generators to represent the urban areas and Abu Ghraib site to represent the rural area. The leaves were taken on a seasonal basis for the period from Octo

Sol-gel derived CuCo-oxide coatings as solar selective surfaces, synthesized onto aluminium substrates at various annealing temperatures, are analysed by correlating their structural, chemical bonding states, and surface morphological topographies. As the annealing progressed, all the coatings displayed a Cu0.56Co2.44O4 (ICSD 78-2175) phase with preferential orientation along (400) reflection plane. Rietveld refinement of X-ray diffraction (XRD) data indicate that residual stress and microstrains developed around the coating surfaces are reduced resulting in mechanically stable thin films. Enhancement of the crystallite size and preferred orientation of the surface were confirmed via XRD, field emission scanning electron microscopy (FESEM),

Iron-Epoxy composite samples were prepared by added
different weight percentages (0, 5, 10, 15, and 20 wt %) from Iron
particles in the range of (30-40μm) as a particle size. The contents
were mixed carefully, and placed a circular dies with a diameter of
2.5 cm. Different mechanical tests (Shore D Hardness, Tensile
strength, and Impact strength ) were carried out for all samples. The
samples were immersed in water for ten weeks, and after two weeks
the samples were take-out and drying to conducting all mechanical
tests were repeated for all samples. The hardness values increased
when the Iron particle concentration increased while the Impact
strength is not affected by the increasing of Iron particles
c

In this research a study of the effect of quality, sequential and directional layers for three types of fibers are:(Kevlar fibers-49 woven roving and E- glass fiber woven roving and random) on the fatigue property using epoxy as matrix. The test specimens were prepared by hand lay-up method the epoxy resin used as a matrix type (Quick mast 105) in prepared material composit . Sinusoidal wave which is formed of variable stress amplitudes at 15 Hz cycles was employed in the fatigue test ( 10 mm )and (15mm) value 0f deflection arrival to numbers of cycle failure limit, by rotary bending method by ( S-N) curves this curves has been determined ( life , limit and fa