In this study, the investigation of Local natural Iraqi rocks kaolin with the addition of different proportions of bauxite and its effect on the physical and mechanical properties of the produced refractories was conducted. Kaolin/bauxite mixture was milled and classified into various size fractions, the kaolin (less than 105 μm) and the bauxite (less than 70μm). The specimens were mixed from kaolin and bauxite in ranges B1 (95+5)%, B2 (90+10)%, B3(85+15)%, and B4 (80+20)%  respectively. The green specimens were shaped by the semi-dry method using a hydraulic press and a molding pressure of 7 MPa with the addition of (9-12) %wt. of PVA ratio. After molding and drying, the specimens were fired at (1100, 1200 and 13

The main objective of this study was to evaluate the adsorption efficiency of two adsorbent materials, Iraqi chicken eggshells (ESh) and activated carbon (AC) derived from ESh powder for the removal of a cationic dye (Janus green B; JGD) from aqueous solution. Activated carbon was synthesised from ESh using a simple chemical activation method using phosphoric acid as the activating agent. The physicochemical properties of the adsorbents were characterised by the Brunauer–Emmett–Teller (BET) method, FT-IR spectroscopy, scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), inductively coupled plasma optical emission spectroscopy (ICP-OES), and point of zero charge (pHpzc). The results of BET analysis confirmed th

The main objective of this study was to evaluate the adsorptionefficiency of two adsorbent materials, Iraqi chicken eggshells (ESh)and activated carbon (AC) derived from ESh powder for theremoval of a cationic dye (Janus green B; JGD) from aqueoussolution. Activated carbon was synthesised from ESh usinga simple chemical activation method using phosphoric acid asthe activating agent. The physicochemical properties of the adsor-bents were characterised by the Brunauer–Emmett–Teller (BET)method, FT-IR spectroscopy, scanning electron microscopy(SEM), energy-dispersive X-ray spectroscopy (EDS), inductivelycoupled plasma optical emission spectroscopy (ICP-OES), andpoint of zero charge (pHpzc). The results of BET analysis confirmedthat AC has

Background: The possibility of converting the organic fraction of municipal solid waste to mature compost using the composting bin method was studied. Nine distinct treatments were created by combining municipal solid waste (MSW) with animal waste (3:1, 2:1), poultry manure (3:1, 2:1), mixed waste (2:1:1), agricultural waste (dry leaves), biocont (Trichoderm hazarium), and humic acid. Weekly monitoring of temperature, pH, EC, organic matter (OM percent), and the C/N ratio was performed, and macronutrients (N, P, K) were measured. Trace elements, including heavy metals (Cd and Pb), were tested in the first and final weeks of maturity. Results: Temperatures in the first days of composting reached the thermophilic phase in MSW compost

Background: The possibility of converting the organic fraction of municipal solid waste to mature compost using the composting bin method was studied. Nine distinct treatments were created by combining municipal solid waste (MSW) with animal waste (3:1, 2:1), poultry manure (3:1, 2:1), mixed waste (2:1:1), agricultural waste (dry leaves), biocont (Trichoderm hazarium), and humic acid. Weekly monitoring of temperature, pH, EC, organic matter (OM percent), and the C/N ratio was performed, and macronutrients (N, P, K) were measured. Trace elements, including heavy metals (Cd and Pb), were tested in the first and final weeks of maturity. Results: Temperatures in the first days of composting reached the thermophilic phase in MSW compost

.

Atmospheric residue fluid catalytic cracking was selected as a probe reaction to test the catalytic performance of modified NaY zeolites and prepared NaY zeolites. Modified NaY zeolites have been synthesized by simple ion exchange methods. Three samples of modified zeolite Y have been obtained by replacing the sodium ions in the original sample with lanthanum and the weight percent added are 0.28, 0.53, and 1.02 respectively. The effects of addition of lanthanum to zeolite Y in different weight percent on the cracking catalysts were investigated using an experimental laboratory plant scale of fluidized bed reactor.

The experiments have been performed with weight hourly space velocity (WHSV) range of 6 to 24 h

Halobacterium saccharovorum was isolated from local highsalinity souls named Al-Massab Al-Aam. A growth curve was determined. The average generation time during logarith- mic phase was 17.80±0.62 hr. Bacteriorhodopsin was 1808 lated from the purple membrane, its concentration was 4.8 mg/ml and H.W was 26000. The pattern of other membrane Bpoteins was studied and compared with those of other Boletes. Several unique proteins were isolated and their molecular weights were determined.

   The aim of this work is to detect the best operating conditions that effect on the removal of Cu²⁺, Zn²⁺, and Ni²⁺ ions from aqueous solution using date pits in the batch adsorption experiments. The results have shown that the Al-zahdi Iraqi date pits demonstrated more efficient at certain values of operating conditions of adsorbent doses of 0.12 g/ml of aqueous solution, adsorption time 72 h, pH solution 5.5 ±0.2, shaking speed  300 rpm, and smallest adsorbent particle size needed for removal of metals.  At the same time the particle size of date pits has a little effect on the adsorption at low initial concentration of heavy metals. The adsorption of metals increases with increas