This work investigates the use of hydrogenated amorphous silicon (a-Si:H) as a high-refractive-index material for quarter-wave distributed Bragg reflectors (DBRs) in photonic applications. In comparison to Si3N4, a-Si:H enables enhanced optical confinement, broader omnidirectional reflectance, and improved figures of merit, including higher Purcell and quality factors, while minimizing mirror complexity. To evaluate the practical impact of these advantages, a theoretical comparison is conducted between Fabry–Pérot cavities based on a-Si:H/SiO2 and Si3N4/SiO2 DBRs, examining resonance shifts as functions of cavity refractive index (1.0–3.0) and temperature (0–250 °C). The numerical results indicate that Si3N4/SiO2 planar Bragg caviti

In the current endeavor, a new Schiff base of 14,15,34,35-tetrahydro-11H,31H-4,8-diaza-1,3(3,4)-ditriazola-2,6(1,4)-dibenzenacyclooctaphane-4,7-dien-15,35-dithione was synthesized. The new symmetrical Schiff base (Q) was employed as a ligand to produce new complexes comprising Co(II), Ni(II), Cu(II), Pd(II), and Pt(II) metal-ions at a ratio of 2:1 (Metal:ligand). There have been new ligands and their complexes validated by (FTIR), (UV-visible), 1H-NMR, 13C-NMR, CHNS, and FAA spectroscopy, Thermogravimetric analysis (TG), Molar conductivity, and Magnetic susceptibility. The photostabilization technique to enhance the polymer was also used. The ligand Q and its complexes were mixed in 0.5% w/w of polyvinyl chloride in tetrahydrofuran

In this manuscript, the effect of substituting strontium with barium on the structural properties of Tl_0.8Ni_0.2Sr_2-xBr_xCa₂Cu₃O_9-δcompound with x= 0, 0.2, 0.4, have been studied. Samples were prepared using solid state reaction technique, suitable oxides alternatives of Pb₂O₃, CaO, BaO and CuO with 99.99% purity as raw materials and then mixed. They were prepared in the form of discs with a diameter of 1.5 cm and a thickness of (0.2-0.3) cm under pressures 7 tons / cm², and the samples were sintered at a constant temperature o

Background: The adenomatoid odontogenic tumor is a relatively rare benign epithelial odontogenic tumor. It contains both epithelial and mesenchymal components. Few cases presented as an extrafollicular lesion or involve the mandible or associated with other odontogenic lesions. This paper represents a rare case of an extrafollicular AOT. Case presentation: A 24-year-old female had a painless swelling on the right side of the lower jaw since one-month duration. Intraorally there was a well defined fluctuant-blue swelling in the right alveolar premolar region measuring 1×2 cm obliterating the right lower buccal vestibule. Grade II mobility in the vital 44 and 45 teeth were observed. Panoramic radiographs showed a well-defined pear shaped

Ceramic coating compose from a ceramic mixture (MgO, Al₂O₃) and metall (Al-Ni) were produced by Thermal Spray Technique. The mixed ratio of used materials Al:Ni (50%) and 40% of Al₂O₃ and 10% MgO. This mixture was spray on a stainless steel substrate of type (316 L) by using thermal spray with flame method and at spraying distances (8, 12, 16 and 20) cm, then the prepared films were treated by laser and thermal treatment. After that performing a hardness and adhesion tests were eximined. The present study shows that the best value of the thermal treatment is 1000 ℃ for 30 mint; the optimum spray distance is 12 cm and most suitable laser is 500 mJ where the microscopic and mechanical character

في هذا البحث تم تحضير المركبات المعدنية الجديدة لأيونات البلاتين (الرباعي) و الذهب (الثلاثي) مع ليكاند قاعدة مانخ جديد مشتق من السيبروفلوكساسين . تم استخدام المعقدات بعد ذلك كمصدر  لتحضير جزيئات                              عن طريق ترسيب المعقدات على مسام دقائق السيليكا النانوية.                                                                      Si/Au2O3 Si/PtO2  تم تشخيص الليكاند و معقداته

Activated carbon prepared from date stones by chemical activation with ferric chloride (FAC) was used an adsorbent to remove phenolic compounds such as phenol (Ph) and p-nitro phenol (PNPh) from aqueous solutions. The influence of process variables represented by solution pH value (2-12), adsorbent to adsorbate weight ratio (0.2-1.8), and contact time (30-150 min) on removal percentage and adsorbed amount of Ph and PNPh onto FAC was studied. For PNPh adsorption,( 97.43 %) maximum removal percentage and (48.71 mg/g) adsorbed amount was achieved at (5) solution pH,( 1) adsorbent to adsorbate weight ratio, and (90 min) contact time. While for Ph adsorption, at (4) solution pH, (1.4) absorbent to adsorbate weight ratio, and (120 min) contact