The molar ratio(x) of Li-Ni ferrites in the formula Li0.5-0.5xNixFe2.5-
0.5xO4 was varied in range 0.1-1.0 by hydrothermal process. The
XRD, SEM, and TEM tests were conducted to examine the samples
crystalline phase and to characterize the particles shapes and sizes.
The high purity spinel structure was obtained at med and high x
values. SEM and TEM images showed the existence of different
ferrite particles shapes like nanospheres and nanorods. The
maximum particle size is around (20nm). These size encourage
occurrence of super paramagnetic state. The reflection loss and
insertion loss as microwave losses of Li-Ni ferrite-epoxy composite
of 1mm thickness and mixing ratio 39.4 wt was investigated. The
mini

The thermoelectric power as a function of temperature for the Iron-Manganese-Aluminum, Fe-Mn-Al, alloys for manganese concentrations 0.04, 0.06, 0.08, 0.10 and 0.20 have been investigated in the temperature range 300 K. to 500 K. these results showed that the thermoelectric power coefficient in hot probe measurements showed that the electrons are the majority charge carriers in these alloys.

In this work, we synthesized thirteen compounds of 1-(2-furoyl)thiourea derivatives 1-13 by conversion of 2-furoyl chloride to 2-furoyl isothiocyanate by reacting it with potassium thiocyanate in dry acetone in a quite short reflux time then, in the same pot, different of (primary and secondary amines) were added individually to achieve thiourea derivatives. The products were characterized spectroscopically using (FT-IR, 1H NMR and 13C NMR) techniques. Some of them were evaluated as antioxidant agents using DPPH radical scavenging method, and all were examined theoretically as enzyme inhibitors against Bacillus pasteurii urease (pdb id: 4ubp) and  by studying  molecular docking using Autodock (4.2.6) software.

Cadmium oxide thin films were prepared by D.C magnetron plasma sputtering using different voltages (700, 800, 900, 1000, 1100 and 1200) Volt. The Cadmium oxide structural properties using XRD analysis for just a voltage of 1200 volt at room temperature after annealing in different temperatures (523 and 623) K were studied .The results show that the films prepared at room temperature have some peaks belong to cadmium element along the directions (002), (100), (102) and (103) while the other peaks along the directions of (111), (200) and (222) belong to cadmium oxide. Annealed samples display only cadmium oxide peaks. Also, the spectroscopic properties of plasma diagnostic for CdO thin films were determined and the results show that the el

Four electrodes were synthesized based on molecularly imprinted polymers (MIPs). Two MIPs were prepared by using the diclofenac sodium (DFS) as the template, 2-hydroxy ethyl metha acrylate(2-HEMA) and 2-vinyl pyridine(2-VP) as monomers as well as divinyl benzene and benzoyl peroxide as cross linker and initiator respectively. The same composition used for prepared non-imprinted polymers (NIPs) but without the template (diclofenac sodium). To prepared the membranes electrodes used different plasticizers in PVC matrix such as: tris(2-ethyl hexyl) phosphate (TEHP), tri butyl phosphate (TBP), bis(2-ethyl hexyl) adipate (BEHA) and tritolyl phosphate (TTP). The characteristics studied the slop, detection limit, life time and linearity range of DF

This research presents the kinetics of the saponification reaction using mixed fats of olein and stearin [in the ratio (3:1)] with NaOH solution. In this reaction, excess solution of NaOH was used to ensure the reaction being irreversible. Three parameters were varied to show their effects on the reaction rate .They are: percentage excess of NaOH solution (10 % - 100 %) , temperature (100-150)oC , and stirring speed (400-1100) rpm. It was noticed that increasing the percentage excess of NaOH solution enhances the rate of reaction while increasing temperature decreases the reaction rate since it is exothermic reaction.    Increasing stirring speed also improves the reaction rate because it is mass transfer controlled .Calcu