Background: Debonding orthodontic brackets and removal of residual bonding material from the enamel surface include critical steps that may cause enamel damage. The aim of the present study was to evaluate and compare the site of bond failure and enamel surface damage after debonding of three types of esthetic brackets (composite, ceramic, sapphire) bonded with light cure composite and resin-modified glass ionomer adhesive. Materials and methods: Seventy two maxillary premolars teeth were divided into three groups each group consisted of 24 teeth according to the type of brackets. Each group was subdivided into two subgroups (12 teeth for each) according to the bonding material that was used. After 7 days of bonding procedure, the brackets

This study evaluated the structural changes of enamel treated by the Regenerate system and carbon dioxide (CO2) laser against acid challenge. Thirty human enamel slabs were prepared and assigned into three groups: Group I: untreated (control); Group II: treated with the Regenerate system; and Group III exposed to CO2 laser. All specimens were subjected to an acid challenge (pH 4.5–7.0) for 14 days. Specimens were evaluated and compared at 120 points using five Raman microspectroscopic peaks; the phosphate vibrations ν1, ν2, ν3, and ν4 at 960, 433, 1029, and 579 cm−1, respectively, and the carbonate at 1070 cm−1, followed by Vickers microhardness test. The ratio of carbonate to phosphate was correlated to the equivalent mic

Background: Although bleaching is typically considered a safe procedure, various investigations have found minor negative effects and changes in mineral composition. The aim was to Evaluate and compare the efficacy of using Nanohydroxyapatite serum on surface microhardness of enamel surface before and after bleaching with chemically cured Boost bleaching. Material and methods: ten sound human permanent upper and lower premolar teeth were used and their roots were removed 2 mm apically to the cementoenamel junction, the crowns were sectioned mesiodistally into two halves buccal and lingual/palatal, the buccal surface was further subdivided into two halves. The samples were embeded in an acrylic resin, resulting in 30 specimens divide

The study aimed to determine the impact of energy for the north and south magnetic poles on the the growth of bacteria isolated from cases of tooth decay, 68 swabs were collected from surfaces of faulty tooth, the detected of Staphylococcus aureus

Effects of Ozonated Water on Micro Leakage between Enamel and Fissure Sealants Prepared by Different Etching Technique (An in vitro Study), Baraa M Jabar*, Muna S Khalaf

Background: One of the most common and prevalent oral diseases among adolescents is periodontal disease particularly gingivitis, however enamel anomalies and dental trauma could occur. Aims of the study: This study was conducted among 14-15 years intermediate school male students in urban area of Al-Khalis city to assess the oral hygiene (dental plaque) and to estimate the prevalence and severity of gingivitis, enamel anomalies, as well as traumatic dental injuries, furthermore to show the significant difference between these two ages concerning these oral problems. Materials and methods: In this study the total sample consisted of 735 students (397 aged 15 years and 338 aged 14 years ). In present study dental plaque was recorded accord

Background: This in vitro study compares a self-etch primer (SEP) to an etch-and-rinse (EaR) for bonding sapphire brackets by evaluation of the enamel etch-pattern, shear bond strength, amount of remnant adhesive and enamel surface damage following thermal and fatigue cyclic loading. Material and Methods: Ceramic (sapphire) brackets were bonded to 80 extracted human premolars using two enamel etching protocols: conventional EaR using 37% phosphoric acid (PA) gel (control), and a SEP (Transbond Plus). Each group was subdivided into two subgroups (n=20 teeth) according to the time of bracket debonding: after 24 h water storage or following 5000 thermo-cycles plus 5000 cycles fatigue loading, to determine the shear bond strength (SBS), adhesiv

Abstracts:

Background: The oral cavity is a complex environment, both structurally and functionally, the hard and soft tissues are in close a proximity. Oral tissues subjected to wear throughout the life, that threatened the vitality of the pulp or increase the sensitivity of dentinal tubules. One of the common dental problems is loss of enamel or cementum, which stimulate the nerve ending in or near the pulp and manifested as pain sensation. Aim of the study: This study had done to evaluate the effects of 980nm diode Laser in diameters reduction of exposed dentinal tubules analyze the results and morphological changes of irradiated dentine surface by FE-SEM (field emission scann