A field experiment was carried out to find out the effect of some herbicides(Pallas, Crash, U46) on the companion weed to three cultivars of the oat crop (Shefa, Hamel, and Pimula) and the yield and its components of these cultivars. The results showed the superiority of the two treatments of spraying weed herbicides (T1 and T2 ) by giving the best results, as they recorded the lowest number of weed plants after 30 days of spraying reached 1.44 and 1.67 plant/m2 . Besides, the lowest weed dry weight was 0.11 and 0.00 g/m2, and the highest inhibition percentage in dry weight was 98.44% and 100.0% of the two treatments, respectively. The treatment T2 was also superior by giving the highest control percentage of 93.28% compared to the compari

Background:In this study,TiO2 layer was thermally grown as a diffusion barrier on CP Ti substrate prior to electrophoretic deposition of HA coatings, to improve the coating’s compatibility also macro and micro pores in nano Hydroxyapatite dual coatings were created and their effect on the bond strength between the bone and implant was evaluated. Materials and methods: Electrophoretic Deposition technique (EPD) was used to obtain coatings for each one of four types of Hydroxyapatite(HA)on CP Ti screws (micro HA, nano HA, dual nano HA with micro pores, dual nano HA with macro pores) where carbon particles used as fugitive material to be removed by thermal treatment to create porosity.For examination of the changes occurred on the subs

This study included effect of polyherbs mixture treatment of diabetic patients type II for two months. The polyherbs mixture contains Nigella sativa seeds, Boswellia carterri gum, Citrus aurantifolia fruits, Elettaria cardamomum fruits. Also this study included estimation of some biochemical parameters in the serum Diabetes Mellitus (D.M.) patients-type II and knowing the relationship of these parameters with this disease. The parameters are glucose, cholesterol ,High density , Low density lipoproteins( HDL-C, LDL-C) respectively , Triglycerides TG, urea, total protein , albumin , Alkaline phosphatase ALP,Transaminase GOT, GPT enzymes . Take (77) samples of diabetic patients serum type II which included (47) samples for group one: herbs

A comprehensive practical study of typical mechanical properties of welded Aluminum alloy AA7020-T6 (Al-Mg-Zn), adopting friction stir welding (FSW) technique and conventional metal inert gas (MIG) technique, is well achieved in this work for real comparison purposes. The essences of present output findings were concentrated upon the FSW samples in respect to that MIG ones which can be summarized in the increase of the ultimate tensile strength for FSW was 340 MPa while it was 232 MPa for MIG welding, where it was for base metal 400 MPa. The minimum microhardness value for FSW was recorded at HAZ and it was 133 HV0.05 while it was 70 HV0.05 for MIG weld at the welding metal. The FSW produce 2470 N higher than MIG welding in the bending t

When a vehicle is left parked in the sun for an extended period, the gathered heat causes damage to several interiors within the cabin and causes discomfort for people and animals left inside the car. In the present work, the effect of the orientation of a parked white minibus on temperature distribution and cooling load calculation is studied experimentally in an open environment. Two different cases were studied facing south and facing east. For several hours, the temperature inside the car cabin had been monitored and measured at five separate locations. The cooling load calculations are carried out based on the experimental measurements. The results show that the overheating of parked cars always happens as a result

This study focuses on producing wood-plastic composites using unsaturated polyester resin reinforced with Pistacia vera shell particles and wood industry waste powder. Composites with reinforcement ratios of 0%, 20%, 30%, and 40% were prepared and tested for thermal conductivity, impact strength, hardness, and compressive strength. The results revealed that thermal conductivity increases with reinforcement, while maintaining good thermal insulation, reaching a peak value of 0.633453 W/m·K. Hardness decreased with increased reinforcement, reaching a minimum nominal hardness value of 0.9479. Meanwhile, impact strength and compressive strength improved, with peak values of 14.103 k/m² and 57.3864568 MPa, respectively. The main aim is to manu