Abstract : Silicone elastomer is widely used as the material of choice for fabricating maxillofacial prosthesis. However, silicone properties are far from ideal; low tear strength, low tensile strength and insufficient elasticity are the most undesirable properties. The purpose of this study was to evaluate the effect of addition of nano SiO2filler on tear strength, tensile strength, elongation at break, hardness and color of Cosmesil M-511 HTV maxillofacial silicone elastomer. Nano SiO2was added to the silicone base in concentrations of 4%, 5% and 6% by weight. Silicone with 0% nano filler served as a control. Tear test was done according to ISO 34-1. Tensile and elongation test was done according to ISO 37. Shore A hardness test was done

Aim: surface modification of titanium using fiber laser 1064 nm to enhance the bond strength to resin cement. Material and Methods: thirty titanium discs of 0.6 cm x 0.3 cm (diameter and thickness respectively) were categorized after preparation into three groups (n=10) as follows: control group with no surface treatment and two test groups were treated with fiber laser after estimation the appropriate parameters in the pilot study which are 81 ns pulse duration, 30,000 Hz frequency, 50 µm spot size and 10,000 mm/s scanning speed and different average power values (10 W and 20 W) depending on the tested group. Titanium discs surface characterization was performed by scanning electron microscope (SEM), a

Heterocyclic systems, which are essential in medicinal chemistry due to their promising cytotoxic activity, are one of the most important families of organic molecules found in nature or produced in the laboratory. As a result of coupling N-(4-nitrophenyl)-3-oxo-butanamide (3) using thiourea, indole-3-carboxaldehyde, or piperonal, the pyrimidine derivatives (5a and 5b) were produced. Furthermore, pyrimidine 9 was synthesized by reacting thiophene-2-carboxaldehyde with ethyl cyanoacetate and urea with potassium carbonate as a catalyst. The chalcones 11a and 11b were synthesized by reacting equal molar quantities of 1-naphthaldehy

The research work involve preparation of activated carbon from Plant corn grain dry in the presence of some additive Residual of poly ethelenetereaphthalate.and the anather way Carbonization was conducted by mixing a known weight of the feedstock with variable quantity of the additive and fixed ratio of Potassium hydroxide. Carbonization completed using fusion in solid state in the absence of solvents. Feedstock and mainly Remnants of poly ethelenetereaphthalate were decompose thermally in a Small chains containing to naphthoxide radicals, these radicals can be connected with the Chains of activated carbon aiming to increase polarity ,This was found from the reaction it self . this research has been studying the product sample was eva

A new azo dye, 5,5-[1,2-phenylenebis(2,1-biazenediyl)]bis[8-quinolino], was synthesized by reacting the diazonium salt of o-phenylenediamine with 8-hydroxyquinoline. The ligand was subsequently used to prepare a series of metal complexes with V(IV), Fe(III), Cr(III), Mn(II), Mo(VI), and Ru(III). The ligand was characterized using 1H and 3C-NMR spectroscopy, while the metal complexes were analyzed using UV-Vis, FT-IR, and mass spectrometry, along with thermal analysis (TGA, DSC), (C.H.N.), conductivity measurements, magnetic susceptibility, and metal and chlorine content analysis, the results indicated that the ligand exhibits tetracoordination. The complexes predominantly formed octahedral geometries, except for the vanadium complex, which

Objective: Schiff’s and Mannich bases of isatins are an important group of heterocyclic compounds which are of great importance in medicinal chemistry as antimicrobial agents. In the vision of these facts, new bis-Schiff bases and Mannich bases of isatins were synthesized. Methods: Three different bis-Schiff bases (3a-c) have been synthesized by reacting isatin, 5-fluoroisatin and 5-methoxy isatin with thiophene-2- carboxaldehyde using hydrazine hydrate to link between the carbonyl compounds, and then these bis- Schiff bases were condensed with two different secondary amines (piperidine and morpholine) separately, and formaldehyde to form the Mannich bases (4a-c and 5a-f), respectively. Results: The structures of the newly synthesized com

The preparation of a new Azo compounds of highly conjugated dimeric and polymeric liquid crystal to achieve the crystalline characteristics Which have structures assigned based on elemental analysis, IR 1HNMR and CHNS-O while mesogenic properties have been set for DSC and hot-stage polarizing optical microscopy. The compounds show enantiotropicnematic phase being displayed. The compounds show photoluminescence properties in the organic solution at room temperature, with the fluorescence band centered around 400 nm.