The present research investigates hydrodesulfurization (HDS) and hydrodearomatization (HAD) of raw kerosene with 0.364 wt. % sulfur and 16.498 wt. % aromatics supplied from Al-Dura Refinery. Hydrotreating reactions were carried out in one stage reactor over high metal  Ni W/γ-Al2O3 prepared catalyst at different temperatures 275-350oC, pressures 32-62 bar, LHSV 1-4 hr-1, and H2/HC ratios 200-500. The prepared catalyst was pre-sulfided remarkably at low temperature and high pressure to avoid risky of sintering associated with gaining the active sulfide phase at high temperatures.  Results showed an obvious differences between HDS and HAD rates due to difficulty of polyaromatics saturation compared with desulfurization. Sulfur and

The impact of decorating Fe, Ru, Rh, and Ir metals upon the sensing capability of a gallium nitride nanotube (GaNNT) in detecting chlorine trifluoride (CT) was scrutinized using the density functionals B3LYP and B97D. The interaction of the pristine GaNNT with CT was a physical adsorption with the sensing response (SR) of approximately 6.9. After decorating the above-mentioned metals on the GaNNT, adsorption energy of CT changed from −5.8 to −18.6, −18.9, −19.4, and −20.1 kcal/mol by decorating the Fe, Ru, Rh, and Ir metals into the GaNNT surface, respectively. Also, the corresponding SR dramatically increased to 39.6, 52.3, 63.8, and 106.6. This shows that the sensitivity of the metal-decorated GaNNT (metal@GaNNT) increased by in

    In the drilling and production operations, the effectiveness of cementing jobs is crucial for efficient progress. The compressive strength of oil well cement is a key characteristic that reflects its ability to withstand forceful conditions over time. This study evaluates and improves the compressive strength and thickening time of Iraqi oil well cement class G from Babylon cement factory using two types of additives (Nano Alumina and Synthetic Fiber) to comply with the American Petroleum Institute (API) specifications. The additives were used in different proportions, and a set of samples was prepared under different conditions. Compressive strength and thickening time measurements were taken under different conditions. The amoun

The current study was conducted in Baghdad governorate (Karkh and Al-Rasafa regions) which included collecting 50 samples of freshly slaughtered sheep meat randomly collected from local slaughter areas and approved governmental slaughterhouses (25 liver and 25 ulna muscles). The results of the aflatoxin B1 detection showed that all samples were contaminated with this toxin at different concentrations ranging from 25–422 ppb and 65–492 ppb for each ulna muscles and liver, respectively. The histopathological and immunological study was conducted in meat samples containing higher and lower concentrations of the toxin. The results of the pathological study in the liver revealed that the concentration (492 ppb) caused thickening of t

Polycyclicacetal was prepared by the reaction of PEG with 4-nitrobenzaldehyde. Cobalt was used for producing a polymer metal complex and solution casting was used to produce a polymer blend including nano chitosan. All produced compounds have been characterized by FT-IR, DSC/ TGA, and SEM techniques as well as biological activity. The production of polyacetal is illustrated by the FT-IR analysis. The DSC/TGA results indicate the prepared polymer blends' thermal stability. Staphylococcus aureas, Klebsiella pneumoniae, Bacillus subtilis, and Escherichia coli were the four types of bacteria selected to study and evaluate the antibacterial activity of produced polyacetal, its metal complex, and polymer blend. Results indicates that ther