Background: Although bleaching is typically considered a safe procedure, various investigations have found minor negative effects and changes in mineral composition. The aim was to Evaluate and compare the efficacy of using Nanohydroxyapatite serum on surface microhardness of enamel surface before and after bleaching with chemically cured Boost bleaching. Material and methods: ten sound human permanent upper and lower premolar teeth were used and their roots were removed 2 mm apically to the cementoenamel junction, the crowns were sectioned mesiodistally into two halves buccal and lingual/palatal, the buccal surface was further subdivided into two halves. The samples were embeded in an acrylic resin, resulting in 30 specimens divide

Background: Contact between implant material and bones must be strong and fast creation, to fulfill these properties appropriate surface modifications must apply on used implants. In this contribution; double surface modifications are applied on Ti-6Al-4V alloy to accelerate osseointegration. Materials and methods: Anodic process is utilized to create titania nanotubes (TNTs) on the screws made from Ti-6Al-4V alloy. These implants were coated with nano ZrO2 particles. Second modification was annealing anodized screws at 8000C, and implanted in tibiae of nine adult New Zealand white rabbits. Results: Physical and histological consequences of two surface modifications on Ti-6Al-4V alloy screws were studied. Scanning electron microscope (SEM)

Nanotechnology is a modern and developed technology, which have great importance in many fields of medicine (diagnosis and treatment). Also, it used to prevent and solve many problems related to animal production and health. The Nanosystems are including metallic nanoparticles, liposomes, polymeric Nanospheres, polymeric micelles, carbon nanotubes, functionalized fullerenes, polymer-coated Nanocrystals, dendrimers and Nanoshells. Our review showed a details classification of nanoparticles and their uses. Nanoparticles have several features depended on the size, colossal surface. The development of antibiotics nanoparticle is very important and has an excellent impact in treating bacterial infections wherever the antibiotics nanopar

Hybrid architecture of ZnO nanorods/graphene oxide ZnO-NRs@GO synthesized by electrostatic self-assembly methods. The morphological, optical and luminescence characteristics of ZnO-NRs@GO and ZnO-NRs thin films have been described by FESEM, TEM, HRTEM, and AFM, which refers to graphene oxide have been coated ZnO-NRs with five layers. Here we synthesis ZnO-NRs@GO by simple, cheap and environmentally friendly method, which made it favorable for huge -scale preparation in many applications such as photocatalyst. ZnO-NRs@GO was applied as a photocatalyst Rodamin 6 G (R6G) dye from water using 532 nm diode laser-induced photocatalytic process. Overall degradation of R6G/ ZnO-NRs@GO was achieved after 90 minutes of laser irradiation while it ne

In this research, rabbit femurs were implanted with CP Ti screws coated with a combination of CaCO₃ and nanohydroxyapatite, and the effect on osseointegration was assessed using histological and histomorphometric examination at 2 and 6 weeks. CaCO₃ and nanohydroxyapatite were combined with the EPD to coat the surfaces of the CP Ti screws. The femurs of five male rabbits were implanted with coated and uncoated implant screws. Healing time was divided into two groups (2 and 6 weeks). After 2 and 6 weeks of implantation, the histological examination revealed an increase in the growth of bone cells for coated screws, and the histomorphometric analysis revealed an increase in the percentage of ne

The present study revealed a low-cost process for utilizing desert sand for preparing nanosilica by sol-gel technique. This work required sodium hydroxide, concentrated hydrochloric acid, distillate water as raw materials, and Iraqi sand. Nanosilica sample was characterized by X-Ray Diffraction (XRD), scanning electron microscopy analysis (SEM), atomic force microscope(AFM), surface area (BET) method, and fourier transform infrared (FTIR). The XRD result of produced sample is referred to as amorphous silica, and it has a broad peak at 2Θ= 22° – 22.5 º. SEM showed spherical, agglomerated silica particles with a diameter range of 26.57–28.93 nm. In addition, the average particle size was 76.35nm, with a dimension range of 40-11

This study aimed to investigate the influence of longitudinal steel embedded tubes located at the center of the column cross-section on the behavior of reinforced concrete (RC) columns. The experimental program consisted of 8 testing pin-ended square sectional columns of 150×150 mm, having a total height of 1400 mm, subjected to eccentric load. The considered variables were the steel square tube sizes of 25, 51 and 68 mm side dimensions and the load eccentricity (50 and 150) mm. RC columns were concealed steel tubes with hollow ratios of 3%, 12% and 20% depending on tube sizes used. The experimental results indicated an improvement in the overall behavior of eccentric columns when steel embedded tubes are used. The maximum gain in

Nine new compounds of 2-amino-5-chlorobenzothiazole derivatives were synthesized. These new compounds were formed through the reaction of 2-amino-5-chlorobenzothiazole 1 with ethyl chloroacetate and KOH, which gave an ester derivative 2, followed by refluxing compound 2 with hydrazine hydrate to afford hydrazide derivative 3. The reaction of compound 3 with CS₂ and KOH gave 1,3,4-oxadiazole-2-thiol derivative 4, and then the reaction of compound 2 with thiosemicarbazide to produce compound 5  then treated it with 4%NaOH led to ring closure to provide 1,2,4-triazole-3-thiol derivative

            In this study, pure SnO₂ Nanoparticles doped with Cu were synthesized by a chemical precipitation method. Using SnCl₂.2H₂O, CuCl₂.2H₂O as raw materials, the materials were annealed at 550°C for 3 hours in order to improve crystallization. The XRD results showed that the samples crystallized in the tetragonal rutile type SnO₂ stage. As the average SnO₂ crystal size is pure 9nm and varies with the change of Cu doping (0.5%, 1%, 1.5%, 2%, 2.5%, 3%),( 8.35, 8.36, 8.67, 9 ,7, 8.86)nm respectively an increase in crystal size to 2.5% decreases at this rate and that the crystal of SnO₂ does not change with the introduction of Cu, and S

In this study, zinc oxide was prepared by pulsed laser ablation method (PLAL), which is an easy-to-use and inexpensive physical method. The optical properties were studied using UV-Vis spectrometers, structure properties by (XRD) to calculate the crystalline size, and particle size determination by Field emission scanning electron microscopy (FE-SEM) and (EDS), transmission electron microscopy (TEM) assays and it was proved that they are within the ideal nanoscale for biological application. These ZnO NPs were employed on the inhibitory activity of different types of Gram-positive and Gram-negative bacteria, as well as on fungi, and it was noted their ability to penetrate the bacterial cell wall and inhibit its action.