The existing investigation explains the consequence of irradiation of violet laser on the structure properties of MawsoniteCu6Fe2SnS8 [CFTS] thin films. The film was equipped by the utilization of semi-computerized spray pyrolysis technique (SCSPT), it is the first time that this technique is used in the preparation and irradiation using a laser. when the received films were processed by continuous red laser (700 nm) with power (>1000mW) for different laser irradiation time using different number of times a laser scan (0, 6, 9, 12, 15 and 18 times) with total irradiation time (0,30,45,60,75,90 min) respectively at room temperature.. The XRD diffraction gave polycrystalline nature with tetragonal crystal system.The result was that the structure properties of MawsoniteCu6Fe2SnS8thin films affected by laser irradiation where the XRD measurement the result was the grain size and stress values that decrease with increasing irradiation time, whereas the values of intensity , FWHM and d-spacing for the largest peak increase with a slight increase with the increase in the irradiation time and slight increase in growth of some peaks with increasing irradiation time.. While not affected EDX and FTIR measurements by laser irradiation, the result was the same for all samples.As for AFM measurement showed that the surface roughness, root mean square and average diameter values that decrease with increasing irradiation time. Note from SEM measurement that the surface topography affected with different time of irradiation red laser. This result due to laser irradiation worked like annealing temperature to enhance the crystallization of the deposited films. As the results showed that the laser irradiation method has a clear change in the structure properties with less time and energy than the traditional annealing methods which is the aim of this study. Keywords: red laser irradiation, semi-computerized spray technique, Structure properties of Mawsonite, Cu6Fe2S8Sn.
Development of NSAIDS based on inhibiting cyclooxygenase activity. However, the different physiological consequences arrised by appearance of new drugs with different selectivity to COX-2 enzyme upon their administration with their relevant affects on some cardiovascular risk factors. To study the potential effects of relatively diclofenac and highly specific celecoxib COX-2 inhibitors on lipid profile and serum C-reactive protein in type 2 diabetes, whom have hyperlipidemia to be compared by their effects with normolipidemic patients. A total number of 34 type 2 diabetics (14 normolipidemics and 20 hyperlipidemics) treated with either diclofenac 100mg/day or celecoxib 200mg/day for eight weeks. Analysis of results indi
... Show MoreThis work includs synthesis of several Schiff bases by condensation of 6- methoxy – 2- amino benzothiazole with some aldehydes and ketones (2- hydroxyl benzaldehyde, 4- hydroxyl benzaldehyde, 4- N,N –dimethy amino acetophenone, benzophenone) to abtain schiff bases (1-5). These schiff bases were found to react with phthalate anhydride to give oxazepine derivatives (6-10) that were reacted with primary aromatic amines to give Diazepine derivatives (11-15). Besides, we prepared new tetrazole derivatives (16-20) from the reaction of the prepared Schiff bases with sodium azide in the prepared compounds that were characterized by physical properties, FT-IR and some of the 1H-NMR and 13C –NMR spectroscopy.
The Atoms in Molecules (AIM) analysis for triosmium cluster, which contains trihydridede, carbon, carbonyl and 2-methylbenzothiazolide ligands, [Os3(µ-H)3(µ3-ɳ2-CC7H3(2-CH3)NS)(CO)8] is reported. Bonding features in this cluster has been analyzed based on QTAIM ("Quantum Theory of Atoms in Molecules") in this work. The topological indices derived from electron density of relevant interactions in triosmium compound have been studied. The major interesting point of the AIM analyses is that the core of part (Os3H3) reveals the absence of any critical points and bond paths connecting any pairs of O
... Show MoreSKF Sami I. Jafar, Mohammad J. Kadhim, Engineering and Technology Journal, 2018 - Cited by 4
The reliability of optical sources is strongly dependent on the degradation and device characteristics are critically dependent on temperature. The degradation behaviours and reliability test results for the laser diode device (Sony-DL3148-025) will be presented .These devices are usually highly reliable. The degradation behaviour was exhibited in several aging tests, and device lifetimes were then estimated. The temperature dependence of 0.63?m lasers was studied. An aging test with constant light power operation of 5mW was carried out at 10, 25, 50 and 70°C for 100hours. Lifetimes of the optical sources have greatly improved, and these optical sources can be applied to various types of transmission systems. Within this degradation range,
... Show MoreAt atmospheric pressure and at a frequency of 9.1 kHz, a constructed magnetically stabilized tornado gliding arc discharge (MSGAD) system was utilized in this study to generate a non-thermal plasma with an alternating voltage source from 2,4,6,8 to 10 kV. Argon gas was used to generate the arc plasma with an adjustable flow rate using a flow meter regulator to stabilize the gas flow rate to 2 L/min. A gliding plasma discharge is achieved by a magnetic field for the purpose of a planned investigation. The influence of the magnetically stabilized tornado gliding arc discharge parameters such as magnetic field and applied voltage on microscopic tornado plasma parameters was studied. The electron temperature1was measured using a Boltzmann plot
... Show MoreA progression of Polyaniline (PANI) and Titanium dioxide (TiO2) nanoparticles (NPs) were prepared by an in-situ polymerization strategy within the sight of TiO2 NPs. The subsequent nanocomposites were analyzed using Fourier-transform infrared spectra (FTIR), X-ray diffraction (XRD), Scanning Electron Microscopy (SEM), and Energy Dispersive X-Ray Analysis (EDX) taken for the prepared samples. PANI/TiO2 nanocomposites were prepared by various compound materials (with H2SO4 0.3 M and without it, to compare the outcome of it) by the compound oxidation technique using ammonium persulfate (APS) as oxidant within the sight of ultrafine grade powder of TiO2 cooled in an ice bath.
... Show MoreFerrite with general formula Ni1-x Cox Fe2O4(where x=0.0.1,0.3,0.5,0.7, and 0.9), were prepared by standard ceramic technique. The main cubic spinel structure phase for all samples was confirmed by x-ray diffraction patterns. The lattice parameter results were (8.256-8.299 °A). Generally, x -ray density increased with the addition of Cobalt and showed value between (5.452-5.538gm/cm3). Atomic Force Microscopy (AFM) showed that the average grain size and surface roughness was decreasing with the increasing cobalt concentration. Scanning Electron Microscopy images show that grains had an irregular distribution and irregular shape. The A.C conductivity was found to increase with the frequency and the addition of Cobal
... Show MoreCompression is the reduction in size of data in order to save space or transmission time. For data transmission, compression can be performed on just the data content or on the entire transmission unit (including header data) depending on a number of factors. In this study, we considered the application of an audio compression method by using text coding where audio compression represented via convert audio file to text file for reducing the time to data transfer by communication channel. Approach: we proposed two coding methods are applied to optimizing the solution by using CFG. Results: we test our application by using 4-bit coding algorithm the results of this method show not satisfy then we proposed a new approach to compress audio fil
... Show More