Nano-crystalline iron oxide nanoparticles (magnetite) was synthesized by open vessel ageing process. The iron chloride solution was prepared by mixing deionized water and iron chloride tetrahydrate. The product was characterized by X-Ray, Surface area and pore volume by Brunauer-Emmet-Teller, Atomic Force Microscope (AFM) and Fourier Transform Infrared Spectroscopy(FTIR)  .  The results showed that the XRD in compatibility of the prepared iron oxide (magnetite) with the general  structure of standard iron oxide, and in Fourier Transform Infrared Spectroscopy, it is strong crests in 586 bands, because of  the expansion vibration manner related to the metal oxygen absorption band (Fe–O bonds in the crystals of iron ox

New Schiff base ligand (E)-6-(2-(4-(dimethylamino)benzylideneamino)-2-(4-hydroxyphenyl)acetamido)-3,3- dimethyl-7-oxo-4-thia-1- azabicyclo[3.2.0]heptane-2-carboxylic acid = (HL) was synthesized via condensation of Amoxicillin and 4(dimethylamino)benzaldehyde in methanol. Figure -1 Polydentate mixed ligand complexes were obtained from 1:1:2 molar ratio reactions with metal ions and HL, 2NA on reaction with MCl2 .nH2O salt yields complexes corresponding to the formulas [M(L)(NA)2Cl],where M=Fe(II),Co(II),Ni(II),Cu(II),and Zn(II), A=nicotinamide .

Complexes of Co(II),Ni(II),Cu(II)and Zn(II) with mixed ligand of 4 tributylphosphine (PBu3) were prepared in aqueous ethanol with (1:2:2) (M:L:PBu3)The prepared

The (E)-4-chloro-N-(2-(dimethylamino)ethyl)-5-((8-hydroxy quinolin-5-yl)diazenyl)-2-methoxybenzamide azo ligand (L) has been synthesized through the reaction of diazonium salt for 5-amino-4-chloro-N-(2-(dimethylamino) ethyl)-2-methoxybenzamide with 8-hydroxyquinoline and identified azo ligand (L) using spectroscopic studies (FTIR, UV-Vis, 1H and 13CNMR, mass), and micro-elemental analysis (C.H.N). Metal chelates of Co(II), Ni(II), Cu(II), as well as Zn(II) have been completed as well as characterized using mass spectra, flame atomic absorption, elemental analysis (C.H.N), infrared, UV-Vis spectroscopy, as well as conductivity, magnetic measurements. The metal-to-ligand ratio in all complexes, as determined by analytical data, was 1:2 and ex

This research set out to provide a faster, easier, and more efficient process for nanoparticle (NP) synthesis of aluminum oxide NPs preparation by microwave irradiation, using plant extracts separately and in the same way (tea, coffee, rosemary), which is an easy-to-use and inexpensive method. The structural properties were investigated by X-ray diffractometer analysis technique (XRD). The X-ray analysis shows the structure has a polycrystalline nature with a hexagonal phase. The optical properties were studied using ultraviolet visible (UV-Vis) spectrometer, where the energy gap was determined. The surface morphology properties of the prepared aluminum NPs were examined by atomic force microscope (AFM). The Fourier transform infra

   A new nano-sized NiMo/TiO₂-γ-Al₂O₃ was prepared as a Hydrodesulphurization catalyst for Iraqi gas oil with sulfur content of 8980 ppm, supplied from Al-Dura Refinery. Sol-gel method was used to prepare TiO₂- γ-Al₂O₃ nano catalyst support with 64% TiO_2, 32% Al₂O₃, Ni-Mo/TiO-γ-Al₂O₃ catalyst was prepared under vacuum impregnation conditions to loading metals with percentage 3.8 wt.% and 14 wt.% for nickel and molybdenum respectively while the percentage for alumina, and titanium became 21.7, and 58.61 respectively. The synthesized TiO₂- γ-Al₂O₃ nanocomposites and Ni-Mo /TiO₂

The reaction of 2, 4, 6-trihydroxyactophenonemonohydrate with hydrazine monohydrate was realized under reflux in methanol and a few drops of glacial acetic acid were added to give the (intermediate) 2-(1-hydrazono-ethyl)-benzene-1, 3, 5-triol, which reacted with salicylaldehyde in methanol to give a new type (NO) ligand [HL][(2-1-[(2-hydroxy-benzyliidene)-hydrazono]-ethyl) benzene-1, 3, 5-triol. The ligand was reacted with Mcl.(where M-Co, Ni, Cu, and Zn) under reflux in methanol with (l: 1) ratio to give complexes of the general formula [M (HL)]. All compounds have been characterized by spectroscopic methods I" H NMR, IR. UV-Vis, HPLC, atomic absorption] microanalysis along with conductivity measurement. From the above data the proposed mo

Mixed ligand complexes of bivalent metal ions, viz; Co(II), Ni(II), Cu(II) and Zn(II) of the composition [M(A)2((PBu3)2]in(1:2:2)(M:A:(PBu3). molar ratio, (where A- Anthranilate ion ,(PBu3)= tributylphosphine. M= Co(II),Ni(II),Cu(II) and Zn(II). The prepared complexes were characterized using flame atomic absorption, by FT-IR, UV/visible spectra methods as well as magnetic susceptibility and conductivity measurements. The metal complexes were tested in vitro against three types of pathogenic bacteria microorganisms: (Staphylococcus, Klebsiella SPP .and Bacillas)to assess their antimicrobial properties. Results. The study shows that all complexes have octahedral geometry; in addition, it has high activity against tested bacteria. Based on th

Mixed ligand complexes of bivalent metal ions, viz; Co(II), Ni(II), Cu(II) and Zn(II) of the composition [M(A)2((PBu3)2]in(1:2:2)(M:A:(PBu3). molar ratio, (where A- Anthranilate ion ,(PBu3)= tributylphosphine. M= Co(II),Ni(II),Cu(II) and Zn(II). The prepared complexes were characterized using flame atomic absorption, by FT-IR, UV/visible spectra methods as well as magnetic susceptibility and conductivity measurements. The metal complexes were tested in vitro against three types of pathogenic bacteria microorganisms: (Staphylococcus, Klebsiella SPP .and Bacillas)to assess their antimicrobial properties. Results. The study shows that all complexes have octahedral geometry; in addition, it has high activity against tested bacteria. Based on th