Bulk polycrystalline samples have been prepared by the two-step solid state reaction process. It has been observed that as grown Tl2-xHgxSr2Ca2Cu3O10+δ (with x = 0, 0.1, 0.2, 0.3, 0.4, 0.5, 0.6, 0.8, 1) corresponds to the 2223 phase. It has been found that Tc varies with Hg content .The optimum Tc is about 120K for the composition Tl1.6Hg0.4Sr2Ca2Cu3O10+δ.The microstructure for Tl1.6Hg0.4Sr2Ca2Cu3O10+δ observed to be most dense and this phase exhibits the highest stability.

In this research the natural frequency of a cracked simple supported beam (the crack is in many places and in different depths) is investigated analytically, experimentally and numerically by ANSYS program, and the results are compared. The beam is made of iron with dimensions of L*W*H= (0.84*0.02* 0.02m), and density = 7680kg/m³, E=200Gpa. A comparison made between analytical results from ANSYS with experimental results, where the biggest error percentage is about (7.2 %) in crack position (42 cm) and (6 mm) depth. Between Rayleigh method with experimental results the biggest error percentage is about (6.4 %) for the same crack position and depth. From the error percentages it could be concluded that the Rayleigh method gives

In this work, magnesium aluminate spinel (MA) (MgO 28 wt%, Al2O3 72 wt%) stoichiometric compound , were synthesized via solid state reaction (SSR) Single firing stage, and the impact of sintering on the physical properties and thermal properties as well as the fine structure and morphology of the ceramic product were examined. The Spinel samples were pressed at of (14 MPa) and sintering soaking time (2h). The effect of adding oxide titania (TiO2) was studied. The obtained powders were calcined at a temperature range of 1200 and 1400 °C. The calcined samples spinel were characterized by XRD, it showed the presence of developed spinel phase end also showed that the best catalyst is titania. The SEM image showed the high sintering temperat

The field experiment was conducted in garden of Department of Biology, College of Education for Pure Sciences (Ibn- Al-Haitham), University of Baghdad during the season of growth (2014-2015). The experiment aimed to study the effect of citric acid with two concentration 10, 20 mg. L-1 and glutamic acid with two concentration 50, 100 mg. L-1 on growth and yield of broad bean (Vicia faba). The results were showed an increased in plant height, leaves number. Plant dry weight, chlorophyll content flowers number, absolute growth rate, crop growth rate, legume length and dry weight, legumes number, seed dry weight compared with control plants.

CdSe alloy has been prepared successfully from its high purity elements. Thin films of this alloy with different thicknesses (300,700)nm have been grown on glass substrates at room temperature under very low pressure (10-5)Torr with rate of deposition (1.7)nm/sec by thermal evaporation technique, after that these thin films have been heat treated under low pressure (10-2)Torr at (473,673)K for one hour. X-ray patterns showed that both CdSe alloy and thin films are polycrystalline and have the hexagonal structure with preferential orientation in the [100] and [002] direction respectively. The optical measurements indicated that CdSe thin films have allowed direct optical energy band gap, and it increases from (1.77- 1.84) eV and from

The apricot plant was washed, dried, and powdered after harvesting to produce a fine powder that was used in water treatment. created an alcoholic extract from the apricot plant using ethanol, which was then analysed using GC-MS, Fourier transform infrared spectroscopy, and ultraviolet-visible spectroscopy to identify the active components. Zinc nanoparticles were created using an alcoholic extract. FTIR, UV-Vis, SEM, EDX, and TEM are used to characterize zinc nanoparticles. Using a continuous processing procedure, zinc nanoparticles with apricot extract and powder were employed to clean polluted water. Firstly, 2 g of zinc nanoparticles were used with 20 ml of polluted water, and the results were Tetra 44% and Levo 32%; after

THE EFFECT OF SPREACL of KNOWLEDGE ON ETHICS

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