Effect of the thermal annealing at 400oC for 2 hours and Argon laser radiation for half hour on the optical properties of AgAlS2 thin films, prepared on glass slides by chemical spray pyrolysis at 360oC with (0.18±0.05) μm thickness .The optical characteristics of the prepared thin films have been investigated by UV/Vis spectrophotometer in the wavelength range (300 – 1100)nm .The films have a direct allow electronic transition with optical energy (Eg) values decreased from (2.25) eV for untreated thin films to (2.10) eV for the annealed films and to (2.00) eV for the radiated films. The maximum value of the refractive index (n) for all thin films are given about (2.6). Also the extinction coefficient (K) and the real and imaginary d

As they include both nucleophilic and electrophilic moieties on the same skeleton, enaminones are an important subclass of chemical compounds that contain conjugated NC=CC=O fragments. These active sites aid in the production of organic molecules containing linear or cyclic heteroatoms. Enaminones and the chemica1 compounds produced from them are both biologically active against the most dangerous bacteria. As a result, they have been utilized as starting materials for the synthesis of anti-inf1ammatory, antibacteria1, anticonvulsant, anticancer, anti-urease, anti-malaria1, optically luminescent, corrosion inhibition, and antitumor agents. Their synthesis has usually a terrific deal of interest and a plethora of synthetic paths have been na

Mannich base is a versatile compound that can be easily modified to introduce different functional groups, allowing for the creation diverse selection of items with varying features. Additionally, the Mannich reaction is a valuable tool in organic synthesis, due to the fact it provides an effortless and efficient approach for synthesizing C-N bonds. Overall, The Mannich base and even its derivatives are essential in many aspects of chemistry and its complexes are in the pharmaceutical industry. Studies have revealed that it shows good anti-cancer, anti-mycobacterial, remarkable anti-HIV, anti-tubercular, anti-convulsant, anti-fungal, antiviral, antitumor, cytotoxic activities and in industrial applications such as in the creation of polymer

The lower respiratory tract of sheep was studied to determine the torsion and branching of the bronchial tree. The respiratory system of ruminants and all living organisms is one of the most important organs in the body that controls the amount of gas exchange between the heart and lungs through the airways, it is clear that in sheep it consists of a narrow bronchial tube that reaches the extent of lung tissue repercussions. He used silicon, water, acid, and at room temperature, and the substance was injected with an injection gun through the trachea and was pushed gently to spread and distribute in all parts of the lungs with moderate manual pressure. The results showed that the mold shape in the lung and the bronchial branches of

      Manganese-zinc ferrite Mn_xZn_1-xFe₂O₄ (MnZnF) powder was prepared using the sol-gel method. The morphological, structural, and magnetic properties of MnZnF powder were studied using X-ray diffraction (XRD), atomic force microscopy (AFM), energy dispersive X-ray (EDX), field emission-scanning electron microscopes (FE-SEM), and vibrating sample magnetometers (VSM). The XRD results showed that the MnxZn1-xFe2O4 that was formed had a trigonal crystalline structure. AFM results showed that the average diameter of Manganese-Zinc Ferrite is 55.35 nm, indicating that the sample has a nanostructure dimension. The EDX spectrum revealed the presence of transition metals (Mn, Fe, Zn, and O) in Mang

The aim of this study is to identify the effect of particle size and to increase the concentration of Iraqi bentonite on rheological properties in order to evaluate its performance and to know if it can be used as drilling fluid without additives or not. In this study, Iraqi bentonite was carried out by mineral composition (XRD), chemical composition (XRF) and Particle size distribution (PSD), and its rheological properties were measured at different particle size and concentration. The results showed that when the particle size of Iraqi bentonite decreased, and the rheological properties were increased with increased concentration of Iraqi bentonite. Also, Iraqi bentonite was unable to use as drilling fluid without certain additives.

Colloidal crystals (opals) made of close-packed polymethylmethacrylate (PMMA) were fabricated and grown by Template-Directed methods to obtain porous materials with well-ordered periodicity and interconnected pore systems to manufacture photonic crystals. Opals were made from aqueous suspensions of monodisperse PMMA spheres with diameters between 280 and 415 nm. SEM confirmed the PMMA spheres crystallized uniformly in a face-centered cubic (FCC) array. Optical properties of synthesized pores PMMA were characterized by UV–Visible spectroscopy. It shows that the colloidal crystals possess pseudo photonic band gaps in the visible region. A combination of Bragg’s law of diffraction and Snell’s law of refraction were used to calculate t

This study investigates the possibility of using waste plastic as one of the components of expired lead-acid batteries to produce lightweight concrete. Different percentages of lead-acid battery plastic were used in the production of lightweight concrete. The replacements were (70, 80 and 100%) by volume of the fine and coarse aggregate. Results demonstrated that a reduction of approximately 23.6% to 35% in the wet density was observed when replacement of 70% to 100% of the natural aggregate by lead-acid battery plastic. Also, the compressive strength decreased slightly with the increase in plastic content at different curing ages of 7, 28, 60, 90, 120 days. The lowest value of compressive strength was (20.7 MPa) for (wa

(Cu1-x,Agx)2ZnSnSe4 alloys have been fabricated with different Ag content(x=0, 0.1, and 0.2) successfully from their elements. Thin films of these alloys have been deposited on coring glass substrate at room temperature by thermal evaporation technique under vacuum of 10-5Torr with thickness of 800nm and deposition rate of 0.53 nm/sec. Later, films have been annealed in vacuum at (373, and 473)K, for one hour. The crystal structure of fabricated alloys and as deposited thin films had been examined by XRD analysis, which confirms the formation of tetragonal phase in [112] direction, and no secondary phases are founded. The shifting of main polycrystalline peak (112) to lower Bragg’s angle as compared to Cu2ZnSnSe4 angle refers to incorpora