The aim of present study is to determine the optimum parameters of friction stir welding process and known the most important parameter along with percentage contribution of each parameter which effect on tensile strength and joint efficiency of FS welded joint of  dissimilar aluminum alloys AA2024-T3 and AA7075-T73 of 3 mm thick plates by applied specific number of experiments using Taguchi method .AA2024 was placed on the advancing side and AA7075 on the retreating side. FSW was achieved under three different rotation speeds (898, 1200 and 1710) rpm, three different welding speeds (20, 45 and 69) mm\min , three different pin profiles (cylindrical, threaded cylindrical and cone) and tool tilt angle 2^◦. Taguchi method w

Developing routes to produce cellulose nanocrystals (CNCs) from high-lignin wood residues is essential for expanding sustainable nanocellulose feedstocks. In this work, Meranti (Shorea sp.) sawdust was valorized into CNCs by integrating ammonium persulfate (APS) pretreatment with subsequent sulfuric acid hydrolysis. To establish a severity map and define an operating window, APS pretreatment severity was systematically varied by adjusting APS concentration and the sawdust-to-APS (solid-to-liquid) ratio, and its influence on CNC structural properties was evaluated. APS pretreatment partially disrupted and oxidized the lignocellulosic matrix, enabling acid hydrolysis to liberate crystalline cellulose domains. XRD analysis confirmed th

Arcology is a new vision of urban design for densely populated settlements. It is referred to as the urban formation aimed at achieving the highest level of utilization in the least area of land to reduce human impact on the environment. Moreover, the integration of this formation with the environment will work to reduce energy consumption, and achieve an economy that is characterized by adaptation and self-sufficiency, leading towards sustainable urbanism. The current study deals with this new concept in sustainable urban design, in an attempt to investigate its impact on traditional urban formation and to make a comparison between them. The lack of a clear conception of the term ‘arcology’ and comparing it with the organic compact urb

This study involved the treatment of textile wastewater contaminated with direct blue 15 dye (DB15) using a heterogeneous photo-Fenton-like process. Bimetallic iron/copper nanoparticles loaded on bentonite clay were used as heterogeneous catalysts and prepared via liquid-phase reduction method using eucalyptus leaves extract (E-Fe/Cu@BNPs). Characterization methods were applied to resultant particles (NPs), including SEM, BET, and FTIR techniques. The prepared NPs were found with porous and spherical shapes with a specific surface area of particles was 28.589 m2/g. The effect of main parameters on the photo-Fenton-like degradation of DB15 was investigated through batch and continuous fixed-bed systems. In batch mode, pH, H2O2 dosage, DB15 c

Four metal complexes of Schi base ligand were prepared. To characterize both the ligand and the metal complexes, various techniques were employed, including elemental analysis, FT-IR spectroscopy, UV-Vis spectroscopy, molar conductivity measurements, magnetic moment determination, melting point, mass spectroscopy, 1H-NMR and 13C-NMR spectroscopy. The results showed that the metal complexes formed have the formula [M(L)2Cl2]Cl(n).H2O, where LD Schi base ligand and MDCr(III), Rh(III), Pt(IV) and Au(III), n D 1, 2. Based on spectroscopic analysis, coordination with metal ions involves the ’N’ donor atom of N atoms of the imine and the N-H amid group, and four complexes are suggested to have a six-coordinated octahedral structure. Molar c

Steel Reinforced Concrete (RC) frequently faces durability problems. In certain areas, Glass Fiber-Reinforced Polymer (GFRP) rebars are considered a non-corrodible substitute for steel reinforcement. Elevated temperatures have a significant impact on the mechanical characteristics and the adhesiveness of GFRP rebars to concrete, particularly when the polymeric matrix's glass transition temperature is approached or surpassed. Three simply supported reinforced concrete slabs were considered in the experimental program. Each specimen had identical dimensions of 1500×540×120 mm. For the fire resistance requirements, a 45 mm clear concrete cover and an exception of a 200 mm unexposed (cool) anchor zone at the ends were considered. The

Ag-doped NiO thin films were fabricated by dip coating and subsequently annealed at 373, 473, 573, and 673 K to elucidate the influence of annealing temperature on their structural, morphological, optical, and NO2-sensing characteristics. X-ray diffraction confirmed the formation of polycrystalline Ag/NiO films, with progressively improved crystallinity and larger crystallite size at elevated annealing temperatures. Atomic force microscopy revealed a homogeneous surface morphology with grain growth, with the average grain diameter increasing from 26.40 to 34.2 nm. Optical analysis showed high visible-region transmittance (65–70%) and a gradual reduction in the optical band gap from 2.75 to 2.07 eV with increasing annealing temperature. Ga