The polymer was used to inhibit the corrosion of copper metal in salt media in different concentrations at room temperature using potentiometric polarization measurement. The polymer was prepared by mixing (0.1 M) 4-Hydroxy aniline (C6H7NO) with (0.25M) of ammonium persulfate as the initiator using the electro-deposition technique. The polymer’s results showed that copper in (3.5%) NaCl had good corrosion resistance. The findings demonstrate that the %IE for polymer-induced copper corrosion is 89.32% at 10 ppm concentration as a result of the 4-hydroxy aniline polymer’s adsorption from salt solution on the surface of copper metal. The numbers from the polarization method and the acquired standard data agree well. The coated copper by po

The polymer was used to inhibit the corrosion of copper metal in salt media in di erent concentrations at room temperature using potentiometric polarization measurement. The polymer was prepared by mixing (0.1 M) 4-Hydroxy aniline (C6H7NO) with (0.25M) of ammonium persulfate as the initiator using the electro-deposition technique. The polymer’s results showed that copper in (3.5%) NaCl had good corrosion resistance. The ndings demonstrate that the %IE for polymer-induced copper corrosion is 89.32% at 10 ppm concentration as a result of the 4-hydroxy aniline polymer’s adsorption from salt solution on the surface of copper metal. The numbers from the polarization method and the acquired standard data agree well. The coated copper by poly

The effect of adding different volume of coumarin dye (5, 15, 25 and 35) ml on optical properties of Poly (Methyl Meth Acrylate) was studied. Films of pure PMMA and PMMA with different volume of coumarin dye (5, 15, 25 and 35) ml were prepared using the casting technique. Transmission and absorption of the films were measured by using UV-VIS spectrometer technique type (100 Conc), in order to assess the type of transmission which was found an indirect transition. An optical energy gap of pure PMMA is (4.95e v) and after adding coumarin with volume (25, 35) ml, the energy gap for PMMA decrease by (0.05) compere to pure PMMA films and addition energy gap appear equal to (4.1 e v). It was found that the absorption coefficient, extinction coeff

Non-Small Cell Lung Cancer (NSCLC) accounts for about 84% of all lung cancer types diagnosed so far. Every year, regardless of gender, the NSCLC targets many communities worldwide. 5-Fluorouracil (5-FU) is a uracil-analog anticancer compound. This drug tends to annihilate multiple tumour cells. But 5-FU's most significant obstacle is that it gets very easily metabolized in the blood, which eventually leads to lower anticancer activity. Therfore a perfect drug delivery system is needed to overcome all the associated challenges.

In this experiment, an attempt was made to prepare 5-FU loaded poly lactic-co-glycolic acid  nanoparticles using solvent evaporation method and subsequently observed the effect of molecular weight of poly l

Three new polyphosphates were synthesized in good yields by reacting diethylenetriamine with the appropriate phosphate ester in ethanol under acidic conditions. The polyphosphate structures were determined using FT-IR and 1H-NMR spectroscopies, and their elemental compositions were confirmed by EDX spectroscopy. Polyphosphates were added to poly(vinyl chloride) (PVC) at low concentrations to fabricate thin films. The PVC films were irradiated with ultraviolet light for long periods, and the effect of polyphosphates as the photostabilizer was investigated by determining changes in the infrared spectra (intensity of specific functional group peaks), reduction in molecular weight, weight loss, and surface morphology. Minimal changes we

This research is addressing the effect of different ferrocene concentration (0.00, 2.15x10-3, 4.30x10-3, 8.60x10-3, and 12.9x10-3) on the bulk free radical polymerization of methyl methacrylate monomer in benzene using benzoyl peroxide as initiator. The polymerization was conducted at 60º C under free oxygen atmosphere. The resulting polymers were characterized by FTIR. The results were compared with the presence and absence of ferrocene at 10% conversion. The %conversion was 3.04% with no ferrocene present in the polymerization medium and its increase to 9.06 with a first lowest ferrocene concentration added, i.e. 2.15 x10-3mol/l. This was positively reflected on the poly(methyl methacrylate) molecular weight measured by viscosity techniq

The research work involve preparation of activated carbon from Plant corn grain dry in the presence of some additive Residual of poly ethelenetereaphthalate.and the anather way Carbonization was conducted by mixing a known weight of the feedstock with variable quantity of the additive and fixed ratio of Potassium hydroxide. Carbonization completed using fusion in solid state in the absence of solvents. Feedstock and mainly Remnants of poly ethelenetereaphthalate were decompose thermally in a Small chains containing to naphthoxide radicals, these radicals can be connected with the Chains of activated carbon aiming to increase polarity ,This was found from the reaction it self . this research has been studying the product sample was eva

The Reversed Phase High Performance Liquid Chromatography (RP-HPLC) has been used for the separation of Poly aromatic hydrocarbons(PAHs) by using column Reprosil 100 C 18 which was found to be a suitable one for this purpose. The result showed that using mobile phase of (Acetonitrile-water) Reversed Phase HPLC , flow rate of (1.2 ml/min) , column temperature (30CËš) and wave length of (254nm), give a complete separation with a good resolution . The total separation time was less than 20 min. The result of the study showed that the vegetables of Baghdad city were polluted by poly aromatic hydrocarbons(PAHs) in different places where samples taken because of drainage of the heavy water ,industrial trash and trash of oil colanders. -

Films of pure Poly (methyl methacrylate) (PMMA) doped by potassium iodide (KI) salt with percentages (1%) at different thickness prepared by casting method at room temperature. In order to study the effect of increasing thickness on optical properties, transmission and absorption spectra have been record for five different thicknesses(80,140,210,250,320)µm. The study has been extended to include the changes in the band gap energies, refractive index, extinction coefficient and absorption coefficient with thickness.