Iron-Epoxy composite samples were prepared by added
different weight percentages (0, 5, 10, 15, and 20 wt %) from Iron
particles in the range of (30-40μm) as a particle size. The contents
were mixed carefully, and placed a circular dies with a diameter of
2.5 cm. Different mechanical tests (Shore D Hardness, Tensile
strength, and Impact strength ) were carried out for all samples. The
samples were immersed in water for ten weeks, and after two weeks
the samples were take-out and drying to conducting all mechanical
tests were repeated for all samples. The hardness values increased
when the Iron particle concentration increased while the Impact
strength is not affected by the increasing of Iron particles
c

The research aimed to use HIIT exercises, and to know the effect of HIIT exercises on some physiological and physical indicators of the young badminton players, and to identify the degree of competition anxiety and the performance of some offense skills among the young badminton players. The research community (the young badminton players), the research sample and its selection method (the research sample was chosen by the intentional method (8) badminton player from the Athwari Club), the scientific method (the experimental method with pre and post tests), measurement tools: physiological tests (high and low blood pressure) , pulse, and physical exams (explosive force of arms and legs) and the offense skills and the scale of competit

The research aimed to use HIIT exercises, and to know the effect of HIIT exercises on some physiological and physical indicators of the young badminton players, and to identify the degree of competition anxiety and the performance of some offense skills among the young badminton players. The research community (the young badminton players), the research sample and its selection method (the research sample was chosen by the intentional method (8) badminton player from the Athwari Club), the scientific method (the experimental method with pre and post tests), measurement tools: physiological tests (high and low blood pressure) , pulse, and physical exams (explosive force of arms and legs) and the offense skills and the scale of competition an

The nonlinear optical properties response of nematic liquid crystal (6CHBT) and the impact of doping with two kinds of nanoparticles; Fe₃O₄ magnetic nanoparticles and SbSI ferroelectric nanoparticles have been studied using the non-linear dynamic method through z-scan measurement technique. This was achieved utilizing CW He-Ne laser. The pure LC and magnetic LC nanoparticle composite samples had a maximum absorption while the ferroelectric LC nanoparticle composite had a minimum absorption of the incident light. The nonlinear refractive index was positive for the pure LC and the rod-like ferronematic LC composite samples, while it was negative for the ferroelectric LC composite. The studying of the nonlinear optical

This research aims to study the effect of microwave furnace heat on the mechanical properties and fatigue life of aluminum alloy (AA 2024-T3). Four conditions were used inside microwave furnace (specimens subjected to heat as dry for 30 and 60min. and specimens subjected to heat as wet (water) for 30 and 60 min.), and compared all results with original alloy (AA 2024-T3). Tensile, fatigue, hardness and surface roughness tests were used in this investigation. It is found that hardness of dry conditions is higher than wet conditions and it increases with increasing of time duration inside microwave furnace for dry and wet conditions. Also, tensile strength has the same behavior of hardness, but it increases with decreasing

The aim of the present research is concerned with study the effect of UV radiation on the optical properties at wavelengths 254, 365 nm of pure PC and anthracene doping PC films prepared using the cast method for different doping ratio 10-60 mL. Films of pure PC and anthracene doping PC were aged under UV radiation for periods of up to 360 h. It found that the effect of UV radiation at wavelength 254 nm on the optical properties is great than the effect of UV radiation at wavelength 365 nm. Also, it found that the optical energy gap of pure PC and anthracene doping PC films is stable against radiation.

Nanoparticles of copper sulfide have been prepared by simple reaction between using copper nitrate with different concentrations ratio 0.1, 0.3, and 0.5 mM, thiourea by a simple chemical route. The prepared Nano powders have been deposited onto glass substrates by casting method at 60°C. The structure of the product Nano- films has been studied by x-ray diffraction, where the patterns showed that all the samples have a hexagonal structure of covellite copper sulfide with the average crystalline sizes 14.07- 16.51 nm. The morphology has been examined by atomic force microscopy, and field emission scan electron microscopy. The AFM images showed particles with almost spherical and rod shapes with average diameter sizes of 49.11- 90.64 nm.

The research aims to achieve a set of objectives, the most important of which is determining the extent to which the auditors of the research sample in the Federal Bureau of Financial Supervision adhere to the requirements of the quality control system according to the Iraqi Audit Manual No. The federal financial / research sample with the quality control system according to the Iraqi audit guide No. 7), and the researcher seeks to test the main research hypothesis and sub-hypotheses, and to achieve this, a questionnaire was designed by (Google Form) and distributed electronically to the elements of the research sample, Through the statistical package program (SPSS), the results of the questionnaire were analysed. In light of the applied