In this study, experimental mortar combinations with 1% micro steel fibers, were examined to create geopolymer mortars. To test the effect of the fibers on the mortar's resistance, the geopolymer mortar was designed with various proportions of more environmentally friendly materials fly ash and slag. The percentage of fly ash by weight was 50, 60, and 70% of the slag. The best results were obtained when a 50:50 ratio of fly ash and slag were mixed with 1% micro steel fibers. The results showed that the mixtures containing fibers performed better in the considered tests (toughness index, ductility index, and resilience index). In the impact resistance test, the mixture contained 50% fly ash by weight of the slag with a temperature of

This work is concerned with the synthesis of two types of composites thin films (Sb2O3:WO3 and (Sb2O3:In2O3) with different concentrations (0.0,0.05,0.1, and 0.15). The prepared thin films are characterized with the use of the X-ray diffraction atomic force microscope AFM and UV-Vis–infrared spectrophotometer. The structural examination shows that both composite's thin films were polycrystalline with nano size with cubic phase as majority and orthorhombic phase as minority phase. The crystal size decreases from 34.6 to 24.7 and 21.7 nm for (Sb2O3:WO3) and (Sb2O3:In2O3) thin films, respectively. The average roughness shows non-regular growth by increasing the concentration of both oxides. The optical energy band gap shows a red shi

The objective of this study is to determination the content of some heavy metals (lead, cadmium, chromium) in colored tattoo stickers. twelve kinds of colored tattoo stikcers were collected from Baghdad markets, it was estimated heavy metals using atomic absorption spectrophotometer (Shimadzu A5000). The results indicated the concentrations of lead in all samples (1.61_1.00 mg / kg) and chromium in the three samples (0.85_0.97 mg / kg) while other samples are free of chromium , and cadmium. These elements are the components of printing inks and dyes in tattoo stickers, and this does not conform to the health and safety conditions for the packaging of food according to the organizations of the health and safety of

A rapid high sensitive and inexpensive economic method has been developed for the Determination of phenoxazine by using molecular spectrophotometry. The method is based on the oxidation of phenoxazine by potassium (meta)periodate in acidic medium. The oxidation conditions were selected to enhance the sensitivity and the stability of the pink colored species which shows an absorption maximum at 530 nm. The Beer’s law was obeyed for phenoxazine concentration range from 1 to 6 µg mL-1 with 0.003 µg mL-1 detection limit and provided variation coefficients between 0.4 to 1.7 %. This method was successfully applied for the determination of phenoxazine in aqueous samples

NiO nanoparticle synthesis by chemical method and characterized by XRD with crystal size 11.72
nm and grain size 13 nm from FESEM image also NiO micro used ,two NiO as an additive to evaluate the
possibility of producing photodegradable polymers, the practical application of solid-phase photocatalytic
degradation of polyvinyl chloride (PVC- NiO composite films) was investigated. PVC has a negative impact
on the environment since its polymer degrades slowly, yet it has a wide range of industrial applications and
the amount used shows no evidence of diminishing use. Thus, a synthesis of modified PVC- NiO micro and
nano has been studied with 0, 50, 100, 150, 200, 250, and 300 (hours) as irradiation time a

This work was conducted to determine the volumetric mass transfer coefficient (Ky.a) infixed bed adsorption using hexane-benzene mixture by adsorption onto a fixed bed of white silica gel. Benzene concentration was measured by gas chromatography. The effect of feed flow rate and initial concentration of benzene in hexane-benzene mixture on the volumetric mass transfer coefficient and on the adsorption capacity of silica gel was investigated.

In general, the volumetric mass transfer coefficient increases with increasing hexane flow rate, and with increasing initial concentration of benzene in the mixture. The ultimate value of (Ky.a) was at 53 ml/min of hexane flow rate with benzene initial concentration of (6.53 wt. %), and it wa

أجريت هذه الدراسة في محافظة النجف بالعراق لتحليل عينات بيولوجية من المدخنين وغير المدخنين. تم استخدام العينات، بما في ذلك مصل الدم والبول والشعر والأظافر، كمؤشرات حيوية لتحديد تركيزات اليورانيوم (UC) ونظائره (238U، 235U، و234U). وباستخدام طريقة التعرض الطبيعي، تم استخدام كاشف المسار النووي (CR-39، المملكة المتحدة) لقياس تركيزات اليورانيوم في العينات. تم جمع خمسة وسبعين عينة من مصل الدم والبول والشعر والأظافر للمد