Hall effect measurements have been made on a-As2Te3 thin films different thickness film in the range (200-350) nm. The Hall mobility in a-As2Te3 thin films decreases with increasing annealing temperature but the carrier concentration increases. When increasing the film thickness increases the Hall mobility decreases, while the carrier concentration increases.

The present study was conducted on the Iraqi Pin-tailed Sandgrouse (Pterocles alchata) to study the lung's morphological description and histological structure. This study was used 5 samples of adult male sandgrouse bird. The birds were dissected. The lungs were removed from the coelomic cavity, cleaned to remove impurities, and photographed to describe their morphological features. The samples were fixed using formalin (10%) solution for 36-48 hours and then preserved in alcohol (70%) to prepare the microscopic slides. The results showed that the lung of the Iraqi sandgrouse bird is red in color, has a trapezoidal shape and has three surfaces (costal, visceral, and vertebral). The costal surface shows ribs impressions that extend f

The research aims to measure the impact of envy on job stress because the topic of envy represents a negative emotion that exists at all organizational levels, which may cause stress in the work environment.

The Research problem is represented by the lack of perception of most of the faculty staff on the negative effects of envy on their well-being in the Technical College of Management - Baghdad, and what is the impact level of envy on their job stress.

To achieve this, the scale of envy was based on two dimensions (being envied, Envying others), While the job stress scale was based on seven dimensions (workload, conflict role, Family factors, work environment, work relationships

DBN Rashid, Rimak International Journal of Humanities and Social Sciences, 2020

In this work the effect of annealing temperature on the structure and the electrical properties of Bi thin films was studied, the Bi films were deposited on glass substrates at room temperature by thermal evaporation technique with thickness (0.4 µm) and rate of deposition equal to 6.66Å/sec, all samples are annealed in a vacuum for one hour. The X-ray diffraction analysis shows that the prepared samples are polycrystalline and it exhibits hexagonal structure. The electrical properties of these films were studied with different annealing temperatures, the d.c conductivity for films decreases from 16.42 ? 10-2 at 343K to 10.11?10-2 (?.cm)-1 at 363K. The electrical activation energies Ea1 and Ea2 increase from 0.031 to 0.049eV and

The stability and releasing profile of 2:1 core: wall ratio ibuprofen microcapsules prepared by aqueous coacervation (gelatin and acacia polymers coat) and an organic coacervation methods (ethyl cellulose and sodium alginate polymers coat) in weight equivalent to 300mg drug, were studied using different storage temperatures 40°C, 50°C ,60°C and refrigerator temperature 4°C in an opened and closed container for three months (releasing profile) and four months (stability study).It was found that, these ibuprofen microcapsules were stable with expiration dates of 4.1 and 3.1 years for aqueous and an organic method respectively.Aqueous prepared ibuprofen microcapsules were found more stable than those microcapsules prepared by or

Tin Oxide (SnO2) films have been deposited by spray pyrolysis technique at different substrate temperatures. The effects of substrate temperature on the structural, optical and electrical properties of SnO2 films have been investigated. The XRD result shows a polycrystalline structure for SnO2 films at substrate temperature of 673K. The thickness of the deposited film was of the order of 200 nm measured by Toulansky method. The energy gap increases from 2.58eV to 3.59 eV when substrate temperature increases from 473K to 673K .Electrical conductivity is 4.8*10-7(.cm)-1 for sample deposited at 473K while it increases to 8.7*10-3 when the film is deposited at 673K

The reliability of optical sources is strongly dependent on the degradation and device characteristics are critically dependent on temperature. The degradation behaviours and reliability test results for the laser diode device (Sony-DL3148-025) will be presented .These devices are usually highly reliable. The degradation behaviour was exhibited in several aging tests, and device lifetimes were then estimated. The temperature dependence of 0.63?m lasers was studied. An aging test with constant light power operation of 5mW was carried out at 10, 25, 50 and 70°C for 100hours. Lifetimes of the optical sources have greatly improved, and these optical sources can be applied to various types of transmission systems. Within this degradation range,