An acidic environment causes surface changes of resin composites. Filler particlesize and filler distribution also have a direct effect on these surface changes. This invitro study evaluated the influence of Pepsi Cola drink on the surface roughness ofComposan LCM and Composan Ceram over time. Sixteen disc shaped specimens(10mm diameter, 2mm thickness) of each resin composite were fabricated, therebyforming two groups (n= 8). Surface roughness (Ra) was analyzed after 24 hrs beforeexposure to beverage. The specimens were submitted to a five minutes immersion inPepsi Cola three times daily interrupted by immersion in deionized distilled water (37C˚). Surface roughness measurements were done at 10, 30, and 60 days intervals. Datawere

This article reviews the construction of organic solar cell (OSC) and characterized their optical and electrical properties, where indium tin oxide (ITO) used as a transparent electrode, “Poly (3-hexylthiophene- 2,5-diyl) P3HT / Poly (9,9-dioctylfluorene-alt-benzothiadiazole) F8BT” as an active layer and “Poly(3,4-ethylenedioxythiophene)-poly (styrene sulfonate)” PEDOT: PSS which is referred to the hole transport layer. Spin coating technique was used to prepared polymers thin film layers under ambient atmosphere to make OSC.  The prepared samples were characterized after annealing process at (80 ͦ C) for (30 min) under non-isolated circumference. The results show a value of filling factor (FF) of (2.888), (0.233) and (0.28

Toxicity with advanced glycation end products (AGEs) is a major problem in uremic patients. Treatment with peritoneal dialysis (PD) exacerbates AGE formation as a result of bioincompatibility of the conventional peritoneal dialysis fluid (PDF). The presence of glucose degradation products (GDPs) in PDF is the main cause of its bioincompatibility. Carnosine is an endogenous dipeptide with a powerful antiglycation/antioxidant activity. In an attempt to improve PDF biocompatibility, we evaluated the effect of carnosine in human peritoneal mesothelial cells (HPMC) incubated with PDF or GDPs in vitro. Methods: HPMC were incubated for short or prolonged time with PDF in the presence or absence of carnosine. Similarly, HPMC were incubated in the s

Synthesis And Studies Of Complexes Of Some Elements With 2-Mercaptohiazole (2-HMBT)

Theligand4-[5-(2-hydoxy-phenyl)- [1,3,4- thiadiazole-2- ylimino methyl]-1,5-dimethyl -2-phenyl-1,2-dihydro-pyrazol-3-one [HL1] is prepared and characterized. It is reacted with poly(vinyl chloride) (PVC) in THF to form the PVC-L compounds ,PVC-L interacted with ions of transition metals to form PVC-L-MII complexes .All prepared compounds are characterized by FTIR spectroscopy, u.v-visible spectroscopy, C.H.N.S. analysis and some of them by 1HNMR

Five different bacterial isolates [ Vibrio cholera (Ogawa) , Vibrio cholera (Inaba) , Salmonella typhi , Salmonella paratyphi and ? Salmonella typhimurium ] were obtained from the Central Health Laboratory . Both sensitivity tests (MIC , MBC and wells method ) against these bacteria were performed by using the aqueous of leaves extract of Marjoram plant. The results cleared that the values of MIC for Vibrio cholera serotypes Ogawa and Inaba were 100 mg/ml , while the value of MBC was 200 mg/ml. The value of the Inhibition zone at 100 mg /ml concentration for both Ogawa and Inaba were 13 mm and 9 mm respectively. Our results showed that the three types of Salmonella didn’t show any inhibition zone at 200 mg/ml .

ABSTRACT Background: This study measured the effects of three parameters pH value, length of immersion and type of archwire on metal ions released from orthodontic appliances. Materials and Methods: Ninety maxillary halves simulated fixed orthodontic appliances that were immersed in artificial saliva of different pH values (6.75, 5 and 3.5) during 28 day period. Three types of archwires were used: stainless steel, nickel titanium and thermal activated nickel titanium. The quantity of nickel and chromium ions was determined with the use of atomic force spectrophotometer while iron ions by spectrophotometer. Each orthodontic set was weighted two times, before the ligation and immersion in the artificial saliva and after 28 days at the end of