From the sustainability point of view a combination of using water absorption polymer balls in concrete mix produce from Portland limestone cement (IL) is worth to be perceived. Compressive strength and drying shrinkage behavior for the mixes of concrete prepared by Ordinary Portland Cement (O.P.C) and Portland limestone cement (IL) were investigated in this research. Water absorbent polymer balls (WAPB) are innovative module in producing building materials due to the internal curing which eliminates autogenous shrinkage, enhances the strength at early age, improve the durability, give higher compressive strength at early age, and reduce the effect of insufficient external curing. Polymer balls (WAPB) had been used in the mixes of thi

The factorial analysis method consider a advanced statistical way concern in different ways like physical education field and the purpose to analyze the results that we want to test it or measure or for knowing the dimensions of some correlations between common variables that formed the phenomenon in less number of factors that effect on explanation , so we must depend use the self consistent that achieved for reaching that basic request. The goal of this search that depending on techntion of self consistent degree guessing for choosing perfect way from different methods for (orthogonal & oblique) kinds in physical education factor studies and we select some of references for ( master & doctoral) and also the scientific magazine and confere

Background: It has been established that several filling techniques can affect apical leakage, which is responsible for 59% of endodontic failures. The primary goal of endodontic therapy is to create a tight seal that aids in repairing the periapical tissues, prevents apical periodontitis, and shields against root canal infection. The study aims to compare the apical sealing ability of epoxy resin based sealer  (AH plus), which is an epoxy-resin-based root canal sealer, GuttaFlow 2, which is a silicone-based root canal sealer, GuttaFlow bioseal is a bioactive glass-based root canal sealer, TotalFill HiFlow bioceramic (BC) sealer is a silicate-based root canal sealer (bioceramic sealer) using a single cone techn

Background: The aim of this study was to evaluate and compare the apical microleakage around retrograde cavities prepared with ultrasonic technique and filled with (Biodentineâ„¢) Materials and methods: 40 extracted single rooted human permanent maxillary teeth with mature apices were selected. The roots were prepared chemo-mechanically using k-files with crown-down technique and then obturated with lateral condensation gutta-percha technique. Teeth were divided into four main groups according to the cavity preparation method either manual or ultrasonic technique: Group A (n=10): A class I retrograde cavity at root end was prepared with traditional handpeice equipped and placement of Biodentine with manual condensation. Group B (n=10):

Background: The aim of this study was to evaluate and compare the apical microleakage around retrograde cavities prepared with ultrasonic technique and filled with (Biodentineâ„¢) Materials and methods: 40 extracted single rooted human permanent maxillary teeth with mature apices were selected. The roots were prepared chemo-mechanically using k-files with crown-down technique and then obturated with lateral condensation gutta-percha technique. Teeth were divided into four main groups according to the cavity preparation method either manual or ultrasonic technique: Group A (n=10): A class I retrograde cavity at root end was prepared with traditional handpeice equipped and placement of Biodentine with manual condensation. Group B (n=10):

The aim of this study is to understand the effect of addition carbon types on aluminum electrical conductivity which used three fillers of carbon reinforced aluminum at different weight fractions. The experimental results showed that electrical conductivity of aluminum was decreased by the addition all carbon types, also at low weight fraction of carbon black; it reached (4.53S/cm), whereas it was appeared highly increasing for each carbon fiber and synthetic graphite. At (45%) weight fraction the electrical conductivity was decreased to (4.36Scm) and (4.27Scm) for each carbon fiber and synthetic graphite, respectively. While it was reached to maximum value with carbon black. Hybrid composites were investigated also; the results exhibit tha