In this work, The effect of annealing treatment at different temperatures (373, 423 and 473) K and chemical treatment with talwen at different immersion time (40, 60 and 80) min on structural and optical properties of the bulk heterojunction (BHJ) blend copper phthalocyanine tetrasulfonic acid tetrasodium salt/poly dioxyethylenethienylene doped with polystyrenesulphonic acid (CuPcTs/PEDOT:PSS) thin films were investigated. The films were fabricated using spin coating technique. X-ray diffraction (XRD) measurements displayed only one peak at 2θ =4.5o corresponding to (001) direction which has dhkl larger than for standard CuPcTs. The dhkl increase then decrease with increasing annealing temperature and
the time of chemical treatment w

This study was aimed to study the effect of adding transglutaminase (TGase) on the mechanical and reservation properties of the edible films manufactured from soybean meal protein isolate (SPI) and whey protein isolate(WPI). The results showed an improvement in the properties with increase in the WPI ratios. Thickness of the SPI films amounted 0.097 mm decreased to 0.096 mm for the WPI: SPI films at a ratio of 2:1, when TGase was added decreased to 0.075 mm. While the tensile strength increased from 7.64 MPa for SPI films to eight MPa for the WPI: SPI films at a ratio of 2:1, when TGase was added increased to 11.04 MPa. Also, the elongation of the WPI: SPI films at a ratio of 2:1 presence of the TGase decreased to 40.6% compared wit

The pure and Sb doped GeSe thin films have been prepared by thermal flash evaporation technique. Both the structural and optical measurement were carried out for as deposited and annealed films at different annealing temperatures.XRD spectra revealed that the all films have one significant broad amorphous peak except for pure GeSe thin film which annealed at 573 K, it has sharp peak belong to orthorhombic structure nearly at 2θ=33o . The results of the optical studies showed that the optical transition is direct and indirect allowed. The energy gap in general increased with increasing annealing temperature and decreased with increase the ratio of Sb dopant. The optical parameters such as refractive index, extinction coefficient and r

The pure and Sb doped GeSe thin films have been prepared by thermal flash evaporation technique. Both the structural and optical measurement were carried out for as deposited and annealed films at different annealing temperatures.XRD spectra revealed that the all films have one significant broad amorphous peak except for pure GeSe thin film which annealed at 573 K, it has sharp peak belong to orthorhombic structure nearly at 2θ=33o. The results of the optical studies showed that the optical transition is direct and indirect allowed. The energy gap in general increased with increasing annealing temperature and decreased with increase the ratio of Sb dopant. The optical parameters such as refractive index, extinction coefficient and real and

            In this study, pure SnO₂ Nanoparticles doped with Cu were synthesized by a chemical precipitation method. Using SnCl₂.2H₂O, CuCl₂.2H₂O as raw materials, the materials were annealed at 550°C for 3 hours in order to improve crystallization. The XRD results showed that the samples crystallized in the tetragonal rutile type SnO₂ stage. As the average SnO₂ crystal size is pure 9nm and varies with the change of Cu doping (0.5%, 1%, 1.5%, 2%, 2.5%, 3%),( 8.35, 8.36, 8.67, 9 ,7, 8.86)nm respectively an increase in crystal size to 2.5% decreases at this rate and that the crystal of SnO₂ does not change with the introduction of Cu, and S

Condensation of 1,2- dibromo ethane with para hydroxy benzoic acid gave 1,2-Ethane-bis- 4-oxybenzoic [1]. This Compound was converted with the thionyl chloride to give 1,2-Ethane-bis- 4-oxybenzoyl chloride [2]. Reaction of compound [2] with thiosemicarbizades gave 1,2-Ethanebis[4-oxybenzoyl-thiosemicarbazide] [3] and opteined 1,2-Ethane-bis[3-mercapto-5-phenoxy- 1,2,4-triazole] [4] from treatment compound [3] with NaOH (4%) .The new compounds 1,2- Ethane-bis[3-(substituted thioacyl)-4-(substituted acyl)-5 phenoxy-1,2,4-triazole] [5a-d] and 1,2- Ethane-bis[3-(substituted alkylthio)-5 phenoxy-1,2,4-trizole] [5e-f] derived from compound [4] were synthesized and characterized by physical and spectral data. All the compounds [4], [5a-d] and [5e-

Complexes of Lanthanide ione Ln(III) =La(III) , Ce(III),Pr(III) and Nd(III) withligands of nicotinamide (na) and Benzimidazole (BIMD) have been prepared withgeneral formula [M(na)3(BIMD)3](NO3) where :M = Ln(III) = La(III) , Ce(III) , Gd(III) , Nd(III) .Na = nicotinamide = C7H6N2OBIMD = Benzimidazole = C7H6N2All compounds have been characterized by spectroscopic methods [FT-IR , UV-VIS ,AAS] , microanalysis (C.H.N) Along with conductivity measurements , solubility ,melting point , theroitical measurment by using chem office 3D prog .Model (2000) .Frome the above data the proposed moleculer structure for all complexes with its ionsis octahydral geometries

Five membered heterocyclics derivatives were synthesized in this work by three routes. The first route includes the synthesis of N-benzoic acid 1,2,3,-triazole derivatives (3),(4) by diazotation of methyl-2-amino benzoate and treating the resulted salt (1) with sodium azide and ethyl acetoacetate or acetyl acetone, respectively. In the second route, derivatives of pyrazole (8) pyrazolin-5-one (9), (10) were prepared by the reaction of the salt (1) with some active methylene compounds to give the corresponding hydrazones derivatives (5-7) which then they were treated with hydrazine hydrate. The third route afforded the synthesis of three derivatives (12), (15a), (15b) of thiazolidinone by two different methods. AII compounds were confirmed b