In this study, the effect of ceramic coating on the performance and gases emission on diesel engine was investigated. A four-stroke, direct injected, single cylinder, diesel engine was tested at constant speed and at different load conditions without coating. Then, the inlet and exhaust valves faces were coated by about 500µm with ceramic materials. Ceramic layers were made of YttriaStabilized Zirconia (YSZ), and NiCrAl as a bond coat. The coating technique adapted in this work is the flame spray method. The engine with valves ceramiccoated research was tested for the same operation conditions of the engine (without coating). The results indicate a reduction in both fuel consumption by about 7.6% and particulate emissions by about (13

This research study the effect of Titanium dioxide on the tensile properties of
Polystyrene (PS) and Polycarbonate (PC) polymers. The stress – strain curve for pure PS
and pure PC, shows that Young modulus for PS is higher than Young modulus for PC,
because PS have higher ultimate strength than PC.
The addition of TiO2 to PS and PC will reduce the Young modulus and ultimate stress,
because the TiO2 particles will reduces or freeze the orientation of these molecular chain
and reduced the toughness of PC, while when the TiO2 were added to PS, the value of
toughness will be stabilized because TiO2 particles make these chains interlocked and the
mobility of the chains will be restrict.

Evaluate the acute and chronic toxicity of Ruta Chalepensis aerial part aqueous extract used in folk medicine in Iraq in Albino Wistar male and female rats. The study of chronic toxicity at the doses 100, 300 and 600mg/kg body weight in male and female rats for 90 days, recorded no mortality. Treated animals showed a normal weight change compared with control. The parameters of male fertility showed a significant decrease in the weight of testis, epididymis and seminal vesicle as well as a reduction in the number and the motility of spermatozoids at treated groups by the doses 300 and 600 mg/kg body weight compared to control group.

Hemogloin (Hb) and serum ferritin levels are used to assess anemia in pregnancy. Some studies referred to the influence of maternal age, body mass index (BMI) and parity on Hb and serum ferritin levels. The study aimed to examine the possible association of maternal Hb and serum ferritin with maternal age, parity, and BMI in a sample of pregnant women in Baghdad.

 Ninety healthy pregnant women, grouped in three equal groups according to the pregnancy trimester, and thirty apparently healthy non-pregnant women from Baghdad were enrolled in this observational study.  Blood and serum samples were obtained for the estimation of Hb and serum ferritin levels.

The pooled data of participants showed a n

Activated carbon prepared from date stones by chemical activation with ferric chloride (FAC) was used an adsorbent to remove phenolic compounds such as phenol (Ph) and p-nitro phenol (PNPh) from aqueous solutions. The influence of process variables represented by solution pH value (2-12), adsorbent to adsorbate weight ratio (0.2-1.8), and contact time (30-150 min) on removal percentage and adsorbed amount of Ph and PNPh onto FAC was studied. For PNPh adsorption,( 97.43 %) maximum removal percentage and (48.71 mg/g) adsorbed amount was achieved at (5) solution pH,( 1) adsorbent to adsorbate weight ratio, and (90 min) contact time. While for Ph adsorption, at (4) solution pH, (1.4) absorbent to adsorbate weight ratio, and (120 min) contact

Background: Dental erosion is a common oral condition which results due to consumption of high caloric and low pH acidic food such as carbonated drinks and fruit juices. It is expected that these food types can cause irreversible damage to dental hard tissues and early deterioration of the dental restorations. So, this study aimed to evaluate and compare the erosive potential effects of orange fruit juice and Miranda orange drink on the microhardness of an orthodontic composite material. Materials and methods: Thirty discs with a thickness of 2 mm and a diameter of 10 mm were prepared from orthodontic bonding composite. The prepared discs were equally divided into three groups (n=10). Microhardness analysis was carried out both prior to