Objective(s): The aim of this study is to compare the impact strength of a heat cured denture-base acrylic resin
reinforced with metal wire and glass fibers.

Methodology: Forty five specimens were prepared from pink heat cure acrylic resin. Specimens were grouped into;
group-I (control group) which consists of 15 specimens with no reinforcement, group-II which consists of 15 specimens
reinforced with metal wire, and group-III consists of 15 specimens reinforced with glass fibers. Specimens were tested
by using charpy impact machine.

Results: The result showed that there was a highly significant difference in impact strength value among the testing
groups at (P < 0.001).

Conclusion: The impact str

In this study, the effect of the combination of micro steel fibers and additives (calcium hydroxide and sodium carbonate) on the size of cracks formation and healing them were investigated. This study aims to apply the use of self-healing phenomenon to repair cracks and to enhance the service life of the concrete structures. Micro steel fibers straight type were used in this research with 0.2% and 0.4% by volume of concrete. A weight of 20 and 30 kg/m³ of Ca(OH)₂ and 2 and 3 kg/m³ of Na₂CO₃ were used as a partial cement replacement. The results confirm that the concrete cracks were significantly self-healed up to 30 days re-curing. Cracks width up to 0.2 mm were comp

Variation orders are an on-going phenomenon in construction and industry projects worldwide, particularly in the province of Sulaimani, where the project's damage from cost and schedule overrun because of variation orders. However, the effect on project costs and time overrun of variation order has yet to be identified. This study evaluates the impact of variation orders on the cost and time off in the Sulaimani governorate. Two hundred twenty-eight projects from various construction sectors built between 2007-2012 were adopted to calculate the contract cost and schedule overruns due to variation orders. Data analysis was applied in the study were descriptive statistics. One-way ANOVA was also applied to determine w

Abstract:

              The hotel sector is one of the most vital sectors exposed to risks, and the authorities concerned with control must take their active and influential role in putting the hotel sector on the right track and compatible with the internationally approved approaches, and the importance of auditing the performance of the hotel sector in light of the (Covid-19) pandemic is embodied in the fact that it gives a clear and realistic picture to the management and regulatory bodies about the performance and activities of this sector and the shortcomings and deviations that must be addressed, and also helps government decision makers to ob

This research was conducted under Lath house canopy of a nursery circumstances, Baghdad University for season 2013 in order to study the effect of soak lemon seeds sour orange with different levels of licorice concentrations extract (0, 0.5, 2.5 and 4.5 g/l) for 24 hours in the percentage of germination and some recipes vegetative growth of seedlings .the results outweigh the bitter orange seedlings and focus soak for licorice extract 4.5 g / l significant superiority in most of the traits plant height, leaf number, root length, stem diameter, amounting to 31.077 cm, 14.46 paper / plant, 25.35 cm, 0.52 mm respectively, which showed significant differences for the treatment of comparison which gave lower values. Clear that the licorice ext

The effect of different Ti additions on the microstructure of Al-Ti alloy prepared by powder metallurgy was investigated. A certain amount of Ti (10wt%, 15wt%, and 20wt%) were added to aluminium and the tests like microhardness, density, scanning electron microscope (SEM), optical microscope (OM) and X-Ray Diffraction (XRD) were conducted to determine the influence of different Ti additives on the Al-Ti alloy properties and microstructure. The results show that the grains of α-Al changed from large grains to roughly spherical and then to small rounded grains with increasing Ti content, the micro-hardness of the alloy increases with increasing Ti, and XRD results confirm the formation of TiAl₃ intermetallic co