In this paper, Activated Carbon was successfully prepared from local Iraqi material namely corns stalks .Zinc chloride ZnCl2 was used as activating agent with different concentrations (20%, 40%, 60%) for 72 hours. followed by carbonization at 450 C for (2) hour. UV-Spectrophotometer used for measuring absorbance of methylene blue solutions before and after adsorption. the maximum amount adsorbed for methylene blue material of the prepared activated Carbon was studied by Langmuir adsorption isotherm. Other characteristics of the resulting activated Carbon also discussed, such as pH, Moisture Content and ash content. Finally Activated carbon prepared in this work has good properties compared to the standard samples in such a way it could be

Atorvastatin calcium (ATR) is an antihyperlipidemic agent used for lowering blood cholesterol levels. However, it is very slightly soluble in water with poor oral bioavailability, which interferes with its therapeutic action. It is classified as a class II drug according to Biopharmaceutical Classification System (low solubility and high permeability).

Three strain of Bacillus cereus were obtained from soil sours Laboratories of Biology Department/ College of Science/ University of Baghdad. The bacteria secreted extracellular xylanase in liquid cultur the test ability of xylanase production from these isolates was studied semi quantitative and quantitative screening appeared that Bacillus cereus X3 was the highest xylanase producer. The enzyme was partial purification 191 fold from cultur by reached step by 4 U/mg proteins by ammonium sulfat precipitation 80%, Ion exchang DEAE-cellulos chromatography Characterization study of the partial purifation enzyme revealed that the enzyme had a optimum activity pH8 and activity was stable in the pH rang (8-10) for 30min. maximal activity was attai

Etodolac is choice of drug for pain and inflammation but has major side effects of gastric ulcers that are due to free carboxylic group. Etodolac belongs to the chemical class of non-selective COX-inhibitor but preferentially COX-2 inhibitor. Here the ester linked mutual prodrugs of etodolac with phytophenols like vanillin, carvacrol, umbelliferone, guaiacol, sesamol and syringaldehyde were synthesized. All the prodrugs were characterized by IR-spectroscopy, ¹H-NMR, ¹³C-NMR and mass spectrometry. Among the synthesized prodrugs, the Eto-van, Eto-umbe, Eto-sesa and Eto-syr showed improved analgesic and anti-inflammatory activity compared to etodolac. All the synthesized prodrugs showed less ulcerogenic side effects co

The synthesis of zeolite NaX from locally available kaolin has been studied. The operating conditions for zeolite NaX production from kaolin with good crystallinity were as follows; a gel formation step of metakaolin in alkaline medium in presence of additional silica to crystallize the zeolite was achieved at 60 oC for 1 hr,and with stirring. In ageing step of the reactants at room temperature for 5 days and crystallization step at 87±2 oC for 24 hr. The catalytic activity of catalyst prepared from local kaolin was studied by using cumene cracking as a model for catalytic cracking and compared with standard HY zeolite and HX zeolite catalysts. The activity test was carried out in a laboratory continuous flow unit with fixed bed reactor

Nanosponges (NS) of etodolac(ETO) was prepared using the emulsion solvent diffusion method ; the effects of drug: polymer ratio, the effect of level concentration of internal phase and stirring time and other variables that effect on the physical characteristics of NS were investigated and characterized, The selected formula was lyophilized then incorporated into hydrogel ; which also evaluated .The results show that the formulation that contain Drug: PVA:EC in ratio 1:3:2 is the best with smallest particle size 40.2±0.098 with polydispersibility0.005 and in vitro release 97.6±0.11%, , ETO NS Carbopol hydrogel produced a significant(p<0.05) improvement of the in vitro release than pure ETO hydrogel.

Synthesis three organic inhibitors for carbon steel corrosion: 2-(propylthio)-1H-benzo[d]imidazole (PTBI), 2-(allylthio)- 1H-benzo[d]imidazole (ATBI) and 2-(prop-2-ynylthio)-1H-benzo[d]imidazole (YTBI) were prepared from reaction of 2-mercapto benzimidazole with different alkyl halide. The melting point and TLC were used to confirm the purity of the inhibitors as well as using the [FTIR, 1H-NMR and 13C-NMR] for the identify structures. The synthesized inhibitors were examined by potentiostatic polarization measurement as corrosion inhibitors of carbon steel in acidic media [1M H2SO4 ].The polarization measurement results showed that the mixed type inhibitors. In addition, the efficiency of inhibitors (YTBI) were studied at different con