SAPO-11 is synthesized from silicoaluminophosphate in the presence of di-n-propylamine as a template. The results show that the sample obtained has good crystallinity, 396m2/g BET surface area, and 0.35 cm3/g pore volume. The hydroisomerization activity of (0.25)Pt (1)Zr (0.5)W/SAPO-11 catalyst was determined using n-decane and base oil. All hydroisomerization experiments of n-decane were achieved at a fixed bed plug flow reactor at a temperature range of 200-275°C and  LHSV 0.5-2h-1.  The results show that the n-decane conversion increases with increasing temperature and decreasing LHSV, the maximum conversion of 66.7 % was achieved at temperature 275°C and LHSV of 0.5 h-1. Meanwhile, the same catalyst was used to improve base oil spec

   SAPO-11 is synthesized from silicoaluminophosphate in the presence of di-n-propylamine as a template. The results show that the sample obtained has good crystallinity, 396m²/g BET surface area, and 0.35 cm³/g pore volume. The hydroisomerization activity of (0.25)Pt (1)Zr (0.5)W/SAPO-11 catalyst was determined using n-decane and base oil. All hydroisomerization experiments of n-decane were achieved at a fixed bed plug flow reactor at a temperature range of 200-275°C and  LHSV 0.5-2h^-1.  The results show that the n-decane conversion increases with increasing temperature and decreasing LHSV, the maximum conversion of 66.7 % was achieved at temperature 275°C and LHSV of 0.5 h^-1

The m-consecutive-k-out-of-n: F linear and circular system consists of n sequentially connected components; the components are ordered on a line or a circle; it fails if there are at least m non-overlapping runs of consecutive-k failed components. This paper proposes the reliability and failure probability functions for both linearly and circularly m-consecutive-k-out-of-n: F systems. More precisely, the failure states of the system components are separated into two collections (the working and the failure collections); where each one is defined as a collection of finite mutual disjoint classes of the system states. Illustrative example is provided.

Aluminum doped zinc selenide ZnSe/n-Si thin films of (250∓20 nm) thickness with (0.01, 0.02 and 0.03), are depositing on the two type of substrate (glass and n-Si) to manufacture (ZnSe/n-Si) solar cell through using thermal vacuum evaporation procedure. physical and optoelectronic properties were examined for the samples. X-Ray and AFM techniques are using to study the structure properties. The energy band gap of as-deposited ZnSe thin films for changed dopant ratio were ranging from (2.6-2.68 eV). The results of Hall effect show that pure and doping films were (p-type), and the concentration carriers and the carriers mobility increases with increase Al-dopant ratio. The (C-V) have shown that the heterojunction were of abrupt type. In add

4-Amino-N-(5-methyl-isaxazol-3-yl)-benzenesulfonamide was synthesized by reacting the diazonium salt of sulfamethoxazole with 3-amino phenol. Complexes of Ni(II), Pd(II), Au(III), and Pt(IV) were produced and characterized by atomic absorption, elemental microanalysis, infrared spectroscopy, liquid chromatography–mass spectroscopy, thermogravimetric analysis, different scanning calorimetry, and ultraviolet–visible spectroscopy. Furthermore, the conductivity and magnetic properties were quantified. According to the analytical studies, all complexes were found to possess a 1:2 metal–ligand ratio and were non-electrolytes, except the Au(III) complex electrolyte, which had a 1:1 metal:ligand ratio. The biological activities of some of the

يهدف هذا البحث الى التطرق الى صورة العربي كما يعرضها ادب اليافعين العبري في رواية " نادية " للكاتبة العبرية " كاليلا رون فيدر " . والتي تعد من الاديبات العبريات اللواتي تطرقن بصورة مباشرة الى موضوع ما خلف الجدار ، والصراع العربي – الإسرائيلي وانعكاساته على المجتمع الإسرائيلي بصورة عامة والمجتمع العربي بصورة خاصة . ينقسم هذا البحث إلى ثلاثة فصول، تطرق الفصل الأول  إلى "ادب اليافعين"، و تاريخه ، مميزاته والفئ

Background: Endodontically treated teeth have low resistance to fracture against occlusal forces. The strengthening effect of bonded esthetic onlay restoration on weakened tooth has been reported. This study aimed to assess the fracture resistance of endodontically treated premolars restored with composite with and without cuspal coverage by using direct and indirect techniques. Indirect technique done by CAD/CAM system (computer aided design –computer aided manufacturer) and laboratory processing. Material and methods: Forty human extracted maxillary premolars of approximately comparable sizes were divided into four groups: Group (A): Ten endodontically treated teeth directly filled with Filtek Z250xt without cuspal coverage. Group

Background: This study was conducted to assess the effects of various beverages on the shear bond strength of light-cured orthodontic composite used to bond stainless steel orthodontic brackets on human teeth and to determine the site of bonding failure of this material. Materials and Methods: Fifty extracted human premolars were selected and randomly divided into five equal groups each with 10 teeth according to the beverage type (Control, One Tiger, Milk, Green tea and Coffee). After bonding, the teeth were immersed in specific beverages for 5 minutes twice daily with equal intervening intervals then washed and stored in distilled water at 37º C for the reminder of the day. The process was carried out for 30 days. The samples were then

Background: Pit and fissure sealant have been considered an outstanding adjunct to oral health care in the decrease of occlusal caries onset and low progression. The aims of this in vitro study were to evaluate the marginal microleakage of three different types of fissure sealants (SDI, Tg and tetric N-flow) by time interval, one day and 45 days, in the presence or absence of bonding agent among maxillary and mandibular teeth. Materials and methods: Seventy two sound human maxillary and mandibular first premolar teeth were collected which were free from obvious carious lesions. The teeth were randomly divided into two main equal groups, group (1) and group (2), each group consists of (36) teeth involving equal numbers of maxillary and mandi