Hybrid architecture of ZnO nanorods/graphene oxide ZnO-NRs@GO synthesized by electrostatic self-assembly methods. The morphological, optical and luminescence characteristics of ZnO-NRs@GO and ZnO-NRs thin films have been described by FESEM, TEM, HRTEM, and AFM, which refers to graphene oxide have been coated ZnO-NRs with five layers. Here we synthesis ZnO-NRs@GO by simple, cheap and environmentally friendly method, which made it favorable for huge -scale preparation in many applications such as photocatalyst. ZnO-NRs@GO was applied as a photocatalyst Rodamin 6 G (R6G) dye from water using 532 nm diode laser-induced photocatalytic process. Overall degradation of R6G/ ZnO-NRs@GO was achieved after 90 minutes of laser irradiation while it ne

In addition to the primary treatment, biological treatment is used to reduce inorganic and organic components in the wastewater. The separation of biomass from treated wastewater is usually important to meet the effluent disposal requirements, so the MBBR system has been one of the most important modern technologies that use plastic tankers to transport biomass with wastewater, which works in pure biofilm, at low concentrations of suspended solids. However, biological treatment has been developed using the active sludge mixing process with MBBR. Turbo4bio was established as a sustainable and cost-effective solution for wastewater treatment plants in the early 1990s and ran on minimal sludge, and is easy to maintain. This

silver nanoparticle which synthesized by.

The magnetic properties of a pure Nickel metal and Nickel-Zinc-Manganese ferrites having the chemical formula Ni_0.1(Zn_0.4Mn_0.6)_0.9Fe₂O₄ were studied. The phase formation and crystal structure was studied by using x-ray diffraction which confirmed the formation of pure single spinel cubic phase with space group (Fd3m) in the ferrite. The samples microstructure was studied with scanning electron microstructure and EDX. The magnetic properties of the ferrite and nickel metal were characterized by using a laboratory setup with a magnetic field in the range from 0-500 G. The ferrite showed perfect soft spinel phase behavior while the nickel sample showed higher magnetic loss an

charge transfer complex formed by interaction between the p- aminodiphenylamine (PADPA) as electron donor with iodine as electron acceptor in ethanol at 250C as evidenced by color change and absorption. The spectrum obtained from complex PADPA – Iodine shows absorptions bands at 586 nm. All the variables which affected on the stability of complex were studies such as temperature, pH, time and concentration of acceptor. The linearity of the method was observed within a concentration rang (10–165) mg.L-1 and with a correlation coefficient (0.9996), while the molar absorbitivity and sandell sensitivity were (4643.32) L.mol-1.cm-1 and (0.0943) μg.cm-2, respectively. The adsorption of complex PADPA–I2 was studied using adsorbent surfaces

A simple and rapid spectrophotometric method for the determination of sulphite SO3-2 is described. The method is based on the rapid reduction of known amount of chromate CrO4-2 in the presence of sulphite in acidic medium of 2N H2SO4. The amount of excess of chromate was measured after it reactions with 1,5-diphenylcarbazide which finally gives a pink-violet, water soluble and stable complex, which exhibit a maximum absorption at 542 nm. Beer's law was obeyed in the concentration range from 0.004-6.0 µg of sulphite in a final volume of 25 ml with a molar absorbtivity of 4.64×104 l.mol-1.cm-1, Sandal's sensitivity index of 0.001724 ?g .cm-2 and relative standard deviation of ±0.55 - ±0.83 depending on the concentration level. The present

Abstract: In this research we study the of added NaCl with concentration (0.2, 0.02)M on the spectral of cationically charged dye (cresyl violet) and anionically charged surfactant (sodium dodecyl sulphate) with different concentration, the result show two peaks appearance the first attributed to micelle and the other formation of dye surfactant complex, in addition to the increase in the quantum efficiency of emission spectrum and shifted toward long wavelength (λmax=692.5nm-626nm).