A variety of liquid crystals comprising heterocyclics 1,3,4-oxadiazol ring [III], aminooxazol [IV]a, and aminothiazol [IV]b were synthesized through a number of steps, beginning of the reaction of 3, 3'- dimethyl - [1, 1'-biphenyl] -4, 4'- diamin, ethyl monochloroacetate and sodium acetate to synthesize diacetate compound[I]. The diester reacted with hydrazine hydrate(N2H4-H2O) to give dihydrazide compound [II], then reacted with Pyruvic acid and phosphorous oxychloride to produce diketone compound [III]. The last compound was reacted with urea and thiourea to give aminooxazol and aminothiazol respectively. The synthesized compounds actually characterized and determined the structures by melting points, FT-IR and 1H-NMR spectroscopies. By u

A successful synthesis of SBA-15 with semi-spherical morphology and suitable texture properties was achieved using hydrothermal technique. Sodium silicate, derived from silica sand from Iraq, was used as a silica precursor, and Pluronic p123 triblock copolymer was used as a template with a strong acid media (pH < 1). The effect of adding (1–3) g of either polyvinyl alcohol (PVA), Polyvinyl pyrrolidone (PVP -k30), or Sodium dodecyl sulfate (SDS) dispersant agents on the texture properties of the synthesized SBA-15 was studied. The SBA-15 sample underwent various characterization techniques, including X-ray diffraction (XRD), Fourier transform infrared (FTIR), atomic force microscopy (AFM), nitrogen adsorption-desorption using Br

Hydrogen sulfide (H₂S) gas sensor based on cobalt–manganese spinel oxide MnCo₂O₄ thin films that were prepared by chemical precipitation and green synthesis methods. Structural, morphological, and compositional characterizations of MnCo₂O₄ thin films were performed using XRD, FE-SEM, EDS, and AFM. It was found through XRD patterns that MnCo₂O₄ was formed in a cubic spinel structure for both methods; however, the chemically precipitated thin films possessed better crystallinity and larger crystallite sizes, whereas the green-synthesized films exhibited slightly lower crystallinities and smaller sizes, as evidenced by the broader peaks observed. In addition, FE-SEM and AFM images revealed that the MnCo₂O₄ films prepared by

Silver Indium Aluminum Selenium AgIn1xAlxSe2 AIAS for x=01 thin films was deposited by thermal evaporation at RT and different︣︢︡ ︠︣1thickness 100 150 and 200 nm on the glass Substrate and p2Si wafer to produce AIAS/p3Si heterojunctionsolarcell4 Structural optical electrical and photovoltaicproperties6 are investigated for the samples XRD analysis reveals that all the deposited AIAS films show polycrystalline structure without any change due to increase of thickness Average diameter and roughness calculated from AFM images shows an increase in its value with increasing thickness The optical absorbance and transmittance for samples are measured using a spectrometer type UV Visible 1800 spectra1photometer to study the energy6gap The

ZnO thin films have been prepared by pulse laser deposition technique at room temperatures (RT). These films were deposited on GaAs substrate to form the ZnO/GaAs heterojunction solar cell. The effect of annealing temperatures at ( RT,100, 200)K on structural and optical properties of ZnO thin films has been investigated. The X-ray diffraction analysis indicated that all films have hexagonal polycrystalline structure. AFM shows that the grains uniformly distributed with homogeneous structure. The optical absorption spectra showed that all films have direct energy gap. The band gap energy of these films decreased with increasing annealing temperatures.  From the electrical properties, the carriers have n-type conductivity.  From