An acidic environment causes surface changes of resin composites. Filler particlesize and filler distribution also have a direct effect on these surface changes. This invitro study evaluated the influence of Pepsi Cola drink on the surface roughness ofComposan LCM and Composan Ceram over time. Sixteen disc shaped specimens(10mm diameter, 2mm thickness) of each resin composite were fabricated, therebyforming two groups (n= 8). Surface roughness (Ra) was analyzed after 24 hrs beforeexposure to beverage. The specimens were submitted to a five minutes immersion inPepsi Cola three times daily interrupted by immersion in deionized distilled water (37C˚). Surface roughness measurements were done at 10, 30, and 60 days intervals. Datawere

The nanocompsite of alumina (Al₂O₃) produced a number of beneficial effects in alloys. There is increasing in resistance of materials to surface related failures , such as the mechanical properties , fatigue and stress corrosion cracking .The experimental results observed that the adding of reinforced  nanomaterials  type Al₂O₃  enhanced the   HB hardness, UTS, 0.2 YS and ductility of 2014 Al/Al₂O₃ nano composites . the analysis of experiments, indicated that The maximum enhancement was observed at 0.4 wt.% Al₂O₃. The ultimate improvement percentage were 15.78% HB hardness, 18.1% (UTS), 12.86% (

Experimental tests were carried to control lost circulation in the Khabaz oil field using different types of LCMs including Nano-materials. A closed-loop circulation system was built to simulate the process of lost circulation into formations. Two dolomite plugs were used from different depths of the formation of Azkand in Khabaz oil field. The experimentations were carried out to study the effect of different types of LCMs, cross-linked copolymer (FLOSORB CE 300 S), SiO₂ NP, and Fe₂O₃ NP, on mud volume losses as a function of time.

The rheological measurements of the nanoparticles-reference mud system showed that both of the SiO₂ NP and Fe₂O₃ NP w

In this paper, numerical and experimental studies on the elastic behavior of glass fiber reinforced ‎polymer (GFRP) with stiffeners in the GFRP section's web (to prevent local buckling) are presented. ‎The GFRP profiles‎ were connected to the concrete deck slab by shear connectors. Two full-scale simply supported ‎composite beams (with and without stiffeners) were tested under impact load (three-point load) to ‎assess its structural response. The results ‎proved that the maximum impact force, maximum ‎deflection, damping time, and ‎damping ratio of the composite beam were affected by the GFRP ‎stiffeners‎. The experimental results indicated that the damping ratio and deflection were diminished compare

This work analyzes the impact of MgO nanoparticles on the properties of an epoxy resin solution with uniform structure and particular degree of cure synthesized by the reaction of epoxy resin and pyromellitic dianhydride. Various concentrations of epoxy/MgO nanocomposites were fabricated by mechanical mixing, ultrasonication-based dispersion and casting processes. FTIR results have shown clear differences in the vibrations of C-H, epoxide rings, and main amine N-H groups. This confirms the interaction between MgO particles and the epoxy polymer matrix. X-ray diffraction analysis detected prominent peak at 18.35 degrees, along with additional ones at 43.44 degrees and 62.56 degrees, associated with the (200) and (220) planes of MgO crystal,

Fresh water production from saline or waste water utilizing solar stills is the secured future approach in water industry with low cost and no environmental pollution accompanied with low productivity. In this work, the effect of inserting different available materials in a passive Single Slope Solar SSS stills on their productivity is accomplished. Side by side tests are performed on a conventional still, and three SSS stills inserted with carbon filter media, Copper wire mesh, and Cellulose sheets. All these stills are symmetrical in dimensions with 0.5 m2 base area tested for 20mm water level. The stills have been manufactured, instrumented, and tested in July 2021 under DhiQar-Iraq climate conditions (latitude 31.2° N, longitude 46.34

Introduction:Visceral leishmaniasis (VL), also known as kala-azar, is a diffuse protozoan infection caused by Leishmania donovani complex. VL is principally caused by L. donovani and L. infantum (synonym L. chagasi in South America). The parasite targets the reticulo-endothelial system, with penetration of the spleen, liver, bone marrow and lymph nodes lead to organomegaly and pancytopenia. Organic pentavalent antimonials have been the first-line drugs for the therapy of leishmaniasis for the latest six decades, and clinical resistance to these drugs has emerged as a primary obstacle to successful treatment and control. Miltefosine has been shown to be higher or equivalent to presently approved essential medicines for at least one of viscer

This research foxed on the effect of fire flame of different burning temperatures (300, 400 and 500)oC on the compressive strength of reactive powder concrete (RPC).The steady state duration of the burning test was (60)min. Local consuming material were used to mixed a RPC of compressive strength around (100) MPa. The tested specimens were reinforced by (3.0) cm hooked end steel fiber of (1100) MPa yield strength. Three steel fiber volume fraction were adopted in this study (0, 1.0and 1.5)% and two cooling process were included, gradual and sudden. It was concluding that increasing burning temperature decreases the residual compressive strength for RPC specimens of(0%) steel fiber volume fraction by (12.16, 19.46&24.49) and (18.20, 27.77 &3