In this research, titanium dioxide nanoparticles (TiO₂ NPs) were prepared through the sol-gel process at an acidic medium (pH3).TiO₂ nanoparticles were prepared from titanium trichloride (TiCl₃) as a precursor with Ammonium hydroxide (NH₄OH) with 1:3 ratio at 50 °C. The resulting gel was dried at 70 °C to obtain the Nanocrystalline powder. The powder from the drying process was treated thermally at temperatures 500 °C and 700 °C. The crystalline structure, surface morphology, and particle size were studied by using X-ray diffraction (XRD), Atomic Force Microscopy (AFM), and Scanning Electron Microscope (SEM). The results showed (anatase) phase of titanium dioxide with the average grain size

The fabrication of Solid and Hollow silver nanoparticles (Ag NPs) has been achieved and their characterization was performed using transmission electron microscopy (TEM), zeta potential, UV–VIS spectroscopy, and X-ray diffraction (XRD). A TEM image revealed a quasispherical form for both Solid and Hollow Ag NPs. The measurement of surface charge revealed that although Hollow Ag NPs have a zeta potential of -43 mV, Solid Ag NPs have a zeta potential of -33 mV. According to UV-VIS spectroscopy measurement Solid and Hollow Ag NPs both showed absorption peaks at wavelengths of 436 nm and 412 nm, respectively. XRD pattern demonstrates that the samples' crystal structure is cubic, similar to that of the bulk materials, with

Oil from Brassca campestris (local variety) was extracted with hexane using Soxhlet. The extracted oil was characterized and its antimicrobial activity was determined as well. The content of extracted oil was 40% with 0.5% of volatile oil .Oil was immiscible with polar solvent such as ethanol, acetone and water, while it was easily miscible with chloroform due to its hydrophobicity. The result of organoleptic tests revealed that the oil is clear yellow in color and odorless with acceptable taste. The oil was stable at 4 -25 C? for a month. Refractive index (RI) of oil was 1.4723 with density of 0.914, [both at 4-25 C?]. Boiling point 386 C?. Infra red spectroscopy (IR) indicated the presence of different chemical groups (C=C

In context of this paper we prepare high purity powder ZnO nanostructures by chemical method at low temperature solution and study the effect off annealing at high temperature, ZnO nanoparticles have been successfully synthesized by chemical method at 0Cᵒ solution. In this method, suddenly reaction is occurred between zinc acetate solution and sodium hydroxide solution at 0Cᵒ, annealing temperature of powder product surfactant plays an important role in morphological changes. The nanostructures have been characterized by X-ray diffraction (XRD), Scanning Electron Microscope (SEM), differential scanning calorimetry(DSC) and UV-visible .analysis Effect of annealing temperatures on the morphology , structure and optical properties is di

ABSTRACT: In this research SnO2 thin films have been prepared by using hot plate atmospheric pressure chemical vapor deposition (HPCVD) on glass and Si (n-type) substrates at various temperatures. Optical properties have been measured by UV-VIS spectrophotometer, maximum transmittance about (94%) at 400 0C. Structure properties have been studied by using X-ray diffraction (XRD) , its shows that all films have a crystalline structure in nature and by increasing growth temperature from(350-500) 0C diffraction peaks becomes sharper and grain size has been change. Atomic force microscopy (AFM) uses to analyze the morphology of the Tine Oxides surface structure. Roughness & Root mean square for different temperature have been investigated. The r

Probiotics are live microbes that give many health benefits to human beings and animals, the most studied and commonly used probiotics are Gram-positive bacteria; lactobacilli and bifidobacteria. At nowadays, Lactobacillus spp. constitute more than two-thirds of the total numbers of probiotic species. The present study aimed to characterize Lactobacillus that locally isolated from human mouth and feces as probiotics. A total of three Lactobacillus isolates; Lactobacillus fermentum Lb2, Lactobacillus rhamnosus Lb9, and Lactobacillus paracasei Lb10 were investigated in respect to acid and bile salts tolerance, antibiotics susceptibility, and cell surface hydrophobicity in vitro using bacterial adhesion to hydrocarbons method. In compa

Lactococcus lactis ssp. lactis isolated from raw milk was used for titanium dioxide (TiO2) nanoparticles biosynthesis. Biosynthesized TiO2 nanoparticles were characterized using UV-vis spectroscopy, Atomic Force Microscopy (AFM) (1.97 nm), X-ray diffraction (XRD) appa-ratus, Field Emission Scanning Electron Microscopy (FE-SEM), Energy dispersive X-ray anal-ysis (EDX) spectra and Fourier Transform Infrared Spectroscopy (FTIR). Result was 408.21 cm-1 that belong to anatase Titania. L. lactis ssp. Lactis isolates had the ability to synthesize TiO2 nanoparticles, the characterization results presented that the biosynthesized nanoparti-cles were at wavelength (344-347) nm; approving the formation of anatase phase of TiO2 NPs; spherical c

Meloxicam is a non-steroidal anti-inflammatory drug. It is practically insoluble in water. It is associated with gastrointestinal side effects at high doses on long  term treatment. The aim of this investigation to formulate and evaluate gellified nanoemulsion of meloxicam as a topical dosage form to enhance meloxicam therapeutic activity and reduce systemic side effect.

The pseudo ternary phase diagrams were made, including  the oil mixture which is composed of almond oil and peppermint oil at a ratio (1:2), variable surfactant mixture (S mix) which are tween 80 and ethanol at ratios of (1:1, 2:1, 3:1, and 4:1) and double distilled water. Slow dripping of double distilled water to the combination  of the oil mixtu

SUMMARY. – Absorption, flourescence, quantum yield and lifetime of rhodamine B in chloroform, methanol and dimethyl sulfoxide were measured. A comparison was done of these quantities with those for solid solutions, which are obtained by mixing constant volume proportions of dye at a concentration of 1×10–4M/l with different volume proportions from the concentrated solution of polymer in chloroform and dimethyl sulfoxide. The results showed that the addition of polymer to liquid concentrated solutions (1×10–4M/l) of rhodamine B dye from expecting, which leads to development of active medium for laser dye at high concentration, increase the spectra shift toward high energies, and the luminescence quantum yield but decreasing radiative