ِabstract:In this research we prepared nanofibers by electrospinning from poly (Vinyl Alcohol) /TiO2. The spectrum of the solution (Emission) was studied and found to be at 772 nm, several process parameters were such as concentration of TiO2 , and the effect of distance from nozzle tip to the grounded collector (gap distance). The result of the lower concentration of, the smaller the diameter of nanofiber is. Increasing the gap distance will affect nanofibers diameter.

A metal-assisted chemical etching process employing p-type silicon wafers with varied etching durations is used to produce silicon nanowires. Silver nanoparticles prepared by chemical deposition are utilized as a catalyst in the formation of silicon nanowires. Images from field emission scanning electron microscopy confirmed that the diameter of SiNWs grows when the etching duration is increased. The photoelectrochemical cell's characteristics were investigated using p-type silicon nanowires as working electrodes. Linear sweep voltammetry (J-V) measurements on p-SiNWs confirmed that photocurrent density rose from 0.20 mA cm^-2 to 0.92 mA cm^-2 as the etching duration of prepared SiNWs increased from 15 to 30 min. The

The objective of the current research was to develop the posaconazole (PCZ) loaded NS into the carbopol 934 polymeric gel for prolonged drug release and improved topical delivery; seven different nanosponge formulations of PCZ were formulated using the emulsion solvent diffusion method using various amounts of polymer (ethylcellulose, EC). The aqueous and dispersed phases were prepared using polyvinyl alcohol (PVA) and dichloromethane. The prepared nanosponges (NS) were studied for particle size, structural appearance, and in vitro drug release. Furthermore, the selected formula was formulated as hydrogel and was evaluated for physical characteristics, drug content, and in-vitro drug release. Morphological studies revealed irregular

This study aimed to develop a stable nanosuspension of repaglinide and improve its dissolution, using the Nano-precipitation method, involving a different concentration of a stabilizer, different co-stabilizers and different solvents. Employment of a systemic approach to optimize the formulation parameters, including stabilizer concentration, solvent choice and co-stabilizer election. Soluplus® (SOL) was used as the primary stabilizer for this research, polyvinyl alcohol (PVA), poloxamer 188 (PXM 188), tween 80 (TW80), and polyvinyl pyrrolidine (PVP k30) were investigated as co-stabilizers to prevent particle agglomeration and ensure long-term stability. In addition to ethanol as a primary solvent, acetone and chloroform were used

In this study, derivatives of polyvinyl alcohol (PVA) grafted with phthalic anhydride (PhA) and dyes were prepared to produce polymeric materials of PVA-g-PhA, PVA-g-PhA-anthocyanin, PVA-g-PhA-bromophenol blue, and PVA-g-PhAthymol blue. The materials were characterised by FTIR and 1 H NMR spectroscopies. The crystallinity of the polymers was evaluated with powder X-ray difraction, and the thermal stability by thermogravimetric analysis (TGA). The synthetic procedure for the polymeric materials entailed the formation of esters. The FTIR spectra of the polymers confrmed their formation since the ester carbonyl group stretch was observed at approximately 1691–1716  cm−1 in each material. NMR spectroscopy confrmed the addition of t

In this research Bi2S3 thin films have been prepared on glass substrates using chemical spray pyrolysis method at substrate temperature (300oC) and molarity (0.015) mol. Structural and optical properties of the thin films above have been studied; XRD analysis demonstrated that the Bi2S3 films are polycrystalline with (031) orientation and with Orthorhombic structure. The optical properties were studied using the spectral of the absorbance and transmission of films in wavelength ranging (300-1100) nm. The study showed that the films have high transmission within the range of the visible spectrum. Also absorption coefficient, extinction coefficient and the optical energy gap (Eg) was calculated, found that the film have direct ener

This work investigates the properties of polyvinyl alcohol (PVA) nanocomposite films with varying multi-walled carbon nanotube (MWCNT) content, ranging from 2 to 8 wt.%. The films were prepared using a solution casting method and characterized using UV-visible spectroscopy, optical microscopy, X-ray diffraction, and tensile tests. The prepared PVA/MWCNT nanocomposite films exhibited optical band gap values ranging from 3.5 eV to 5.3 eV. XRD analysis confirmed the semi-crystalline nature of these nanocomposites. Mechanical properties, including hardness, yield strength, ultimate tensile strength, and Young's modulus, were enhanced by increasing MWCNT content by up to 8%. Contact angle measurements showed an increase in hydrophobicity with in

Hydrogen sulfide removal catalyst was prepared chemically by precipitation of zinc bicarbonate at a controlled pH. The physical and chemical catalyst characterization properties were investigated. The catalyst was tested for its activity in adsorption of H₂S using a plant that generates the H₂S from naphtha hydrodesulphurization and a unit for the adsorption of H₂S. The results comparison between the prepared and commercial catalysts revealed that the chemical method can be used to prepare the catalyst with a very good activity.

It has observed that the hydrogen sulfide removal over zinc oxide catalyst follows first order reaction kinetics with activation energy of 19.26 kJ/mole and enthalpy and e