This article includes designed and synthesized for bent-shaped liquid crystal molecules starting from 5,5-diethylpyrimidine-2,4,6(1H,3H,5H)-trione and two moles of chloroacetylchloride in N, N-dimethyl formamide (DMF) and triethylamine (TEA) to product compound [I] ,then reacted the later compound with two moles of 4-hydroxybenzonitrile to yield nitrile compound [II]. Likewise, reaction 5,5-diethylpyrimidine-2,4,6(1H,3H,5H)-trione and two moles of ethylchloroacetate with fused sodium acetate in ethanol to create an ester compound [III], and then the later compound was reacted with two moles of hydrazine hydrate in ethanol to obtained hydrazide acid compound [IV]. After that, the compound [IV] reacted with two moles of ethyl acetoacetate in

Samples prepared by using carbon black as a filler material and phenolic resin as a binder. The samples were pressed in a (3) cm diameter cylindrical die to (250)MPa and treated thermally within temperature range of (600-1000)oC for two and three hours. Physical properties tests were performed, like density, porosity, and X-ray tests. Moreover vicker microhardness and electric resistivity tests were done. From the results, it can be concluded that density was increased while porosity was decreased gradually with increasing temperature and treating time. In microhardness test, it found that more temperature and treating time cause more hardness. Finally the resistivity was decreased in steps with temperature and treating time. It can be c

The aim of this research is to employ starch as a stabilizing and reducing agent in the production of CdS nanoparticles with less environmental risk, easy scaling, stability, economical feasibility, and suitability for large-scale production. Nanoparticles of CdS have been successfully produced by employing starch as a reducing agent in a simple green synthesis technique and then doped with Sn in certain proportions (1%, 2%, 3%, 4%, and 5%).According to the XRD data, the samples were crystallized in a hexagonal pattern, because the average crystal size of pure CdS is 5.6nm and fluctuates in response to the changes in doping concentration 1, 2, 3, 4, 5 %wt Sn, to become   4.8, 3.9, 11.5, 13.1, 9.3 nm respectively. An increase in crystal

In study of effective bioactive compounds, we have synthesized the Co((ІІ), Mn(ІІ), Fe(ІІ), Cu(ІІ), Ni(ІІ), and Zn(ІІ) complexes of the Schiff base derived from trimethoprim and2'-amino-4-chlorobenzophenone and characterized by spectroscopic (NMR, IR, Mass, UV–vis,), analytical, TGA studies and magnetic data .The solution electronic spectral study suggests the stoichiometry of the synthesized complexes and Elemental analysis detected the square planer and octahedral geometry of the compounds. The prepared metal complexes presented promoted efficiency versus the screened bacterial (Escherichia Coli and Staphylococcus aureus) antibacterial efficacy against (Staphylococcus aureus, Salmonella spp., E. coli, Vibrio spp., Pseudomona

In study of effective bioactive compounds, we have synthesized the Co((ІІ), Mn(ІІ), Fe(ІІ), Cu(ІІ), Ni(ІІ), and Zn(ІІ) complexes of the Schiff base derived from trimethoprim and2'-amino-4-chlorobenzophenone and characterized by spectroscopic (NMR, IR, Mass, UV–vis,), analytical, TGA studies and magnetic data .The solution electronic spectral study suggests the stoichiometry of the synthesized complexes and Elemental analysis detected the square planer and octahedral geometry of the compounds. The prepared metal complexes presented promoted efficiency versus the screened bacterial (Escherichia Coli and Staphylococcus aureus) antibacterial efficacy against (Staphylococcus aureus, Salmonella spp., E. coli, Vibrio spp., Pseud

The present work includes the preparation and characterization of{Co(II) , Ni(II), Pd(II), Fe(III) , Ru(III),Rh(III), Os(III) , Ir(III) , Pt(IV) and VO(IV)}complexes of a new ligand 4-[(1-phenyl-2,3-dimethyl-3-pyrozoline-5-one)azo]-N,N-dimethylanline (PAD). The product (PAD) was isolated,studies and characterized by phsical measurements,i.e., (FT-IR), (UV) Spectroscopy and elemental analysis(C.H.N). The prepared complexes were identified and their structural geometric were suggested in solid state by using flame atomic absorption, elemental analysis(C.H.N), (FT-IR) and (UV-Vis) Spectroscopy, as well as magnetic susceptibility and conductivity measurements . The study of the nature of the complexes formed in( ethanolic solution) following t

This research aims to investigate and evaluate a reactive powder concrete (RPC) cast using economical materials. Its mechanical properties were investigated and evaluated by studying the effects of using different cement and silica fume contents and locally steel fibers aspect ratios as reinforcement for this concrete. A compressive strength of about 155.2MPa, indirect tensile strength of 16.0MPa, modulus of elasticity of 48.7GPa, flexural strength of 43.5MPa, impact energy of 3294.4kN.m and abrasion loss 0.59%  have been achieved for reinforced RPC contains  910 kg/m³ cement content, silica fume content 185 kg/m³ of cement weight and fiber volume fraction 2%. The water absorption values w

Copper is a cheaper alternative to various noble metals with a range of potential applications in the field of nanoscience and nanotechnology. However, copper nanoparticles have major limitations, which include rapid oxidation on exposure to air. Therefore, alternative pathways have been developed to synthesize metal nanoparticles in the presence of polymers and surfactants as stabilizers, and to form coatings on the surface of nanoparticles. These surfactants and polymeric ligands are made from petrochemicals which are non- renewable. As fossil resources are limited, finding renewable and biodegradable alternative is promising.The study aimed at preparing, characterizing and evaluating the antibacterial properties of copper nanoparticle

Oxazine and quinazoline has a very important in organic chemistry especially in hetero cyclic fields. this research consist the preparation of 4H,4'H-2,2'-bibenzo[d][1,3]oxazine-4,4'-dione compound (1) from di acid chloride with 2-aminobenzoic acid in pyridine as solvent to give compound (2) 3,3'-diamino-2,2'- biquinazoline-4,4'(3H,3'H)-dione .compound 2 include free amino group .this compound was reacted with maleic and phthalic anhydride for synthesized of cyclic imide compounds (3,4).another reaction for compound 2 with some substituted aromatic aldehyde for prepared of some novel Schiff bases (5-9) contains quinazoline ring. compound 1 was treated with sulfathiazole and sulfadiazine for synthesized of sulfa compounds contains sulf