Background: This study was formulated to compare the effect of 5%hydrofluoric acid in comparison to 37%phosphoric acid with and without the application of silane on bond strength of composite to porcelain. Materials and Methods: Specimen preparation was divided in to two phases, metal-disks fabrication (8mm-diameter and 4mm-thickness) and ceramic veneering. Thirty two specimens were prepared, sandblasted with 50 μm aluminum oxide, and divided into four groups of eight samples. Groups I and III were etched with 37%phosphoric acid while groups II and IV were etched with 5%hydrofluoric acid; and groups I and II were silaneted while groups III and IV were not. Heliobond, and resin composite were applied to each specimen using a plastic transpa

Background: Psychological stress is considered the major etiological factor precipitating myofacial pain and temporomandibular disorders.It is known that stress induce various adaptational responses of physiologic systems. The process includes increase in the activity of the hypothalamic-pituitary-adrenal axis which promotes cortisol secretion. Salivary cortisol has been used as a measure of free circulating cortisol levels.The use of salivary biomarkers has gained increased popularity since collecting samples is non-invasive and painless. The aim of thisstudy was to evaluate the level of cortisol in saliva among sample of university students having myofacial pain, during the final exam period and whether this finding could have a significa

This research aims to identify the impact of Daniel's model on the development of critical thinking. In order to achieve this objective, the following hypotheses are formulated: 1. There is no statistically significant difference at the significance level (0.05) between the average differences in the posttest scores of the experimental group taught according to Daniel's model and the control group taught according to the traditional method in the measure of critical thinking. 2. There is no statistically significant difference at the significance level (0.05) between the average differences in the preand post-tests scores of the experimental group taught according to Daniel's model in the measure of critical thinking. The current research i

In this paper, a miniaturized 2 × 2 electro-optic plasmonic Mach– Zehnder switch (MZS) based on metal–polymer–silicon hybrid waveguide is presented. Adiabatic tapers are designed to couple the light between the plasmonic phase shifter, implemented in each of the MZS arms, and the 3-dB input/output directional couplers. For 6 µm-long hybrid plasmonic waveguide supported by JRD1 polymer (r33= 390 pm/V), a π-phase shift voltage of 2 V is obtained. The switch is designed for 1550 nm operation wavelength using COMSOL software and characterizes by 2.3 dB insertion loss, 9.9 fJ/bit power consumption, and 640 GHz operation bandwidth

In this research, Mn-doped TiO2 thin films were grown on glass, Si and OIT/glass substrates by R.F magnetron sputtering technique with thicknesses (250 nm) using TiO2:Mn target under Ar gas pressure and power of 100 Watt. Through the results of X-ray diffraction, the prepared thin films are of the polycrystallization type after the process of annealing at 600°C for two hour The average crystalline size were 145.32, 280.97 and 261.23 nm for (TiO2:Mn) thin film on glass, Si and OIT/glass substrates respectively, while the measured surface roughness is between 0.981nm and 1.14 nm. The fabricated (TiO2:Mn) thin film on glass sensors have high sensitivity for hydrogen( H2 reducing gas) compared to the sensitivity for hydrogen gas on Si and OIT/

In this work, the effect of variation of semi-angle of the conical part on the vibration characteristics of cylindrical-conical coupled structure is investigated. The shell is made of polyester resin reinforced by continuous E-glass fibers. The case is analyzed experimentally and numerically for orthotropic shell structures. The experimental program is conducted by exciting the fabricated structure by an impact hammer and monitoring the response using an attached accelerometer for different semi-angles of the conical part.
Software named SIGVIEW is used to perform the signal processing on the acquired signal in order to measure the natural frequencies and the corresponding mode shapes. The numerical investigation is achieved using ANS

The present research was conducted to reduce the sulfur content of Iraqi heavy naphtha by adsorption using different metals oxides over Y-Zeolite. The Y-Zeolite was synthesized by a sol-gel technique. The average size of zeolite was 92.39 nm, surface area 558 m²/g, and pore volume 0.231 cm³/g. The metals of nickel, zinc, and copper were dispersed by an impregnation method to prepare Ni/HY, Zn/HY, Cu/HY, and Ni + Zn /HY catalysts for desulfurization. The adsorptive desulfurization was carried out in a batch mode at different operating conditions such as mixing time (10,15,30,60, and 600 min) and catalyst dosage (0.2,0.4,0.6,0.8,1, and 1.2 g). The most of the sulfur compounds were removed at 10 min for all catalyst ty

    The objective of this study was to investigate the effect of Royal jelly RJ on morphology and motility of mice sperms. Sperms were collected from the cauda region of the  epididymis of each 10 mice from the treatment and control groups. Direct activation techniques and evaluation of sperm morphology were carried out. Dhino microscope was used for sperm measurement. The inspection was carried out in Salamatic laboratory for pathological analysis in 2015.The result revealed that all of the sperm function parameters registered significant activation  in the treatment group. There was a significant increase in both the percentage of the sperm motility grade A and the progressive motility (A+B) of the treatment gr