The experiment was conducted at the plant tissue culture laboratory of the Department of Horticulture and Garden Engineering College of Agricultural Engineering Sciences, University of Baghdad, in order to study the effect of some growth regulators on propagation an stimulation production of volatile oil compounds of rosemary plant Rosmarinus officinlis using two vegetative parts (apical and lateral buds). Factorial experiment was implemented in completely randomized design with twenty replications. The results indicated that culturing the apical meristem on the medium Murashige and Skoog (MS) media with 0.5 mg.l-1 (BA) with 0.1 mg.l-1 of NAA gave the highest response rate of 100%. As for the doubling stage, the levels of BAA and IAA (Indol

Background: In the Thermafil as a root canal obturation, system little is known about the effect that varying rates of insertion have on the adaptability of thermoplasticized GP and the amount of apical extrusion. Materials and methods: thirty simulated root canals were obturated with thermafil obturators and Apexit Plus sealer at three different insertion rates. The obturated canals were sectioned at three different levels, the sealer average film thickness for each section was calculated and the amount of apical extrusion for each canal was conducted. Results: the higher adaptability was seen with the faster insertion rate while the slower insertion rate showed fewer tendencies to cause apical extrusion. Conclusions: the intermediate i

This work has been done with using of epoxy resin mixed with Granite powder were weighted by percent volume (5,10,15, and 20)%and then mixed with epoxy polymer to compose polymer composite. Hand lay-up technique is used in fabrication of the composite samples. Hardness test was carried out for the proper samples in both normal condition and after immersion in HCL (1 M and 2 M) solutions for periods ranging up to 10 weeks. After comparing the results between the polymer and their composite, the hardness increased with increasing Granite weight percent, it was found that Hardness were greater for the composites before immersion compared with their values after immersion.

The research aims to know the effect of investment risks measured by the beta coefficient on the efficiency of stock pricing measured by the pricing error. The research was applied in the banks listed in the Iraq market for the period (2017-2020). That affects the value of the shares of the companies listed in it and the risks associated with it, as the risks are a dynamic process that changes over time depending on the variables that affect the general development of the economy, so these fluctuations should be taken into account to achieve maximizing returns and reducing risks and what is reflected in stock prices in the Iraqi markets Securities, through which the following question was asked: How does investment risk affect the efficienc

At atmospheric pressure and at a frequency of 9.1 kHz, a constructed magnetically stabilized tornado gliding arc discharge (MSGAD) system was utilized in this study to generate a non-thermal plasma with an alternating voltage source from 2,4,6,8 to 10 kV. Argon gas was used to generate the arc plasma with an adjustable flow rate using a flow meter regulator to stabilize the gas flow rate to 2 L/min. A gliding plasma discharge is achieved by a magnetic field for the purpose of a planned investigation. The influence of the magnetically stabilized tornado gliding arc discharge parameters such as magnetic field and applied voltage on microscopic tornado plasma parameters was studied. The electron temperature1was measured using a Boltzmann plot

NiO0.99Cu0.01 films have been deposited using thermal evaporation
technique on glass substrates under vacuum 10-5mbar. The thickness
of the films was 220nm. The as -deposited films were annealed to
different annealing temperatures (373, 423, and 473) K under
vacuum 10-3mbar for 1 h. The structural properties of the films were
examined using X-ray diffraction (XRD). The results show that no
clear diffraction peaks in the range 2θ= (20-50)o for the as deposited
films. On the other hand, by annealing the films to 423K in vacuum
for 1 h, a weak reflection peak attributable to cubic NiO was
detected. On heating the films at 473K for 1 h, this peak was
observed to be stronger. The most intense peak is at 2θ = 37