Five N-substituted acrylamides were prepared by reaction of substituted aromatic primary amines with acryloyl chloride in the presence of triethyl amine. The synthesized acrylamides were allowed to introduce copolymerization reaction with three vinylic monomers including acrylonitrile, methyl acrylate and methyl methacrylate respectively to obtain eleven new copolymers having different physical properties which may used in different applications.

were prepared by condensation of 6-R-2amino bcnzothiazol with Salicyldehyde.These Schiff bases were found to reach with maleic anhydride and citraconic to give

Foliar application and seed soaking has been used as a means of supplying supplemental doses of nutrients, plant hormones, stimulants, and organic components. the effects of these applications have included yield increases, and improved drought tolerance, and enhanced crop quality, so A field experiment was carried out during spring seasons in 2019 and 2020 for styding Seed soaking and Foliar Application of Ascorbic acid, Citric acid and Humic acid on Growth, Yield and Active Components IN Maize. Randomized complete block design in split plots arrangement was used with three replicates. Main-plots were for seeds soaking with ascorbic, citric (100 mg l-1) frequently and humic at (1 ml l-1). Sub-plots were for vegetative parts nutrition with

Background: The base of the denture is largely responsible for providing the prosthesis with retention, stability, and support by being closely adapted to the oral mucosa. However; the process of bone resorption is irreversible and may lead to an inadequate fit of the prosthesis; this can be overcome by relining. Materials and methods: Acrylic based soft denture liner is prepared by preparing polymer from purified methylmethacrylate monomer with (10-2) initiator and (30%) dibutylphthalate plasticizer concentrations. Biological properties were evaluated in comparison with the control material through subcutaneous specimens' implantation in the New Zealand rabbits. Excisional biopsies were taken after (1, 3, days 1, 2, 3, 4 weeks) period. Mic

The 3-aminoacetophenone and 4-aminoantipyrine were used as ‎precursors to prepare new six ligands. The three new ligands (L1,L2 ‎and L3) were synthesis by reacting one mole of 3-aminoacetophenone ‎with one mole of (Acetyl chloride), (benzoyl chloride), (4-‎methoxybenzoyl chloride) and ammonium thiocyanat in acetone as a ‎solvent, they are:-‎ L1 (AAA) =[N-(3-acetylphenylcarbamothioyl)acetamide]‎ L2 (BAA) =[N-(3-acetylphenylcarbamothioyl)benzamide]‎ L3 (MAA) =[N-(3-acetylphenylcarbamothioyl)-4-methoxy benzamide]‎ Also three new derivatives of 4-aminoantipyrine were synthesis by ‎reacting one mole of 4-aminoantipyrine with one mole of (Acetyl ‎chloride), (benzoyl chloride), (4-methoxybenzoyl chloride) and ‎ammonium thio

New (pentulose-?-lactone-2,3-enedibenzoate barbituric acid) (L) have been synthesized by reaction of (5-C-dimethyl malonyl-pentulose-?-lactone-2,3-enedibenzoate) with urea in alkaline media (sodium methoxide). (Ca+2, Co+2, Ni+2, Cu+2, Zn+2, Cd+2 and Hg+2) complexes of (pentulose-?-lactone-2,3-enedibenzoate barbituric acid) (L) have been prepared and characterized by (1H and 13CNMR), FTIR, (U.V-Vis) spectroscopy, Atomic absorption spectrophotometer (A.A.S), Molar conductivity measurements and Magnetic moment measurements, and the following general formula has been given for the prepared complexes [MLCl2(H2O)].XH2O, where M = (Ca+2, Co+2, Ni+2, Cu+2, Zn+2, Cd+2, Hg+2), X = five molecules with (Cd+2) complex, L = (pentulose-?-lactone-2,3

PVC/Kaolinite composites were prepared by the melt intercalation method. Mechanical properties, thermal properties, flammability and water absorption percentage of prepared samples were tested. Mechanical characteristic such as tensile strength, elongation at break; hardness and impact strength (charpy type) were measured for all samples. It was found that the tensile strength and elongation at break of PVC composites decreased with increasing kaolinite loading. Also, the hardness of the composites increases with increase in filler content .The impact strength of the composites at the beginning increases at lower kaolinite loadings is due to the lack of kaolin adhesion to the matrix. However, at higher kaolin loadings. This severe agglom