Samples prepared by using carbon black as a filler material and phenolic resin as a binder. The samples were pressed in a (3) cm diameter cylindrical die to (250)MPa and treated thermally within temperature range of (600-1000)oC for two and three hours. Physical properties tests were performed, like density, porosity, and X-ray tests. Moreover vicker microhardness and electric resistivity tests were done. From the results, it can be concluded that density was increased while porosity was decreased gradually with increasing temperature and treating time. In microhardness test, it found that more temperature and treating time cause more hardness. Finally the resistivity was decreased in steps with temperature and treating time. It can be c

In this paper a thin films of selenium was prepare on substrates of n-Si by evaporation in a vacuum technique with thickness about 0.5μm. And then an annealing process was done on samples at two temperature (100 and 200) C ° in a vacuum furnace (10^-3 torr).
Some structural, optical and mechanical properties of prepared thin films were measured. Results showed that the prepared film was the crystallization, optical transmittance and micro hardness of the prepared thin films increased significantly after annealing.

    Ten species of whiteflies (Hemiptera, Aleyrodidae) representing six genera were studied from a collection from different localities in the middle of Iraq. These species are Acaudaleyrodes rachipora (Singh, 1931); Bemisia afer  (Priesner and Hosny,1934); Bemisia tabaci (Gennadius, 1889); Dialeurodes citri (Ashmead,1885); Dialeurodes kirkaldy (Kotinsky, 1907); Neomaskellia andropogonis Corbett, 1926;  Siphoninus phillyreae (Haliday, 1835); Trialeurodes ricini (Misra, 1924); Trialeurodes vapovariorum (Westwood,1856) and Trialeurodes irakeensis (Al-Malo and Abdul-Rassoul, 2000). Notes are given on their localities, date of c

This research dealt with study of cladistics taxonomy of  five  species related to the genus Rumex L. and Polygonum L. from family polygonaceae in Iraq by using Mesquite software V.2.75. This  research support strongly delimiting  the species P. aviculare L. and P. lapathifolia L.as suggested in floras publication while R. dentatus L. is setted in single group whereas R. vesicarius L. and R. conglomeratus Murray were included in the same group. Also, this study involved characteristics of shape, dimensions, color, and ornamentation of seeds and fruits as  the seed forms were ranging from lenticular to trigonous. In terms of size calculations,  the seeds of R. vesicarius  was recorded the higher range (4.0- 4.5) mm in length w

A new reversed phase- high performance liquid chromatographic (RP-HPLC) method with Ultraviolet-Visible spectrophotometry has been optimized and validated for the simultaneous extraction and determination of organic acids present in Iraqi calyces of Hibiscus Sabdraffia Linn. The method is based on using ultrasonic bath for extracting organic acids. Limit of detection in µg/ml of Formic acid, Acetic acid, Oxalic acid, Citric acid, Succinic acid, Tartaric acid, and Malic acid 126.8498×10-6, 113.6005×10-6, 97.0513×10-6, 49.7925×10-6, 84.0753×10-6, 92.6551×10-6, and 106.1633×10-6 ,respectively. The concentration of organic acids found in dry spacemen of calyces of Iraqi Hibiscus Sabdraffia Linn. under study: Formic acid, Acetic acid,

An antibacterial and antifungal piperonal-derived compound and its Rh(III), Pd(II), Pt(IV), and Cd(II) metal complexes were synthesized and characterized by spectroscopic methods, conductivity, metal analyses and magnetic moment measurements. The nature of the complexes formed in ethanolic solution was studied following the molar ratio method. From the spectral studies, octahedral geometry was suggested for rhodium (III) and platinum (IV) complexes, while a square planer structure was suggested for palladium (II) complex and a tetrahedral geometry for cadmium (II) complex. Structural geometries of these compounds were also suggested in gas phase by using hyperchem-8 program for the molecular mechanics and semi-empirical calculations.