In this work, Titanium oxide thin films doped with different concentration of CuO (0,5,10, 15,20) %wt were prepared by pulse laser deposition(PLD) technique on glass substrates at room temperature with constant deposition parameter such as : pulse (Nd:YAG), laser with λ=1064 nm, constant energy 800 mJ , repetition rate 6 Hz and No. of pulse (500). The structure , optical and electrical properties were studied . The results of X-ray diffraction( XRD) confirmed that the film grown by this technique have good crystalline tetragonal mixed anatase and rutile phase structure, The preferred orientation was along (110) direction for Rutile phase. The optical properties of the films were studied by UV-VIS spectrum in the range of (360-1100)

The optical energy gap(Eopt) and the width of the tails of localized states in the band gap (?E) for Se:2%Sb thin films prepared by thermal co-evaporation method as a function of annealing temperature are studied in the photon energy range ( 1 to 5.4)eV.Se2%Sb film was found to be indirect transition with energy gap of (1.973,2.077, 2.096, 2.17) eV at annealing temperature (295,370,445,520)K respectively. The Eopt and ?E of Se:2%Sb films as a function of annealing temperature showed an increase in Eopt and a decrease in ?E with increasing the annealing temperature. This behavior may be related to structural defects and dangling bonds.

This work aimed to study the effect of laser surface treatment on the mechanical characteristics and corrosion behaviour of grey cast iron type A159. Many technical applications used conventional surface treatment, but laser surface hardening has recently been used to enhance the surface properties of many alloys. The mechanical characteristics, including microstructure, microhardness, and wear resistance of A159 grey cast iron, were studied, in addition to corrosion behaviour. The experimental laser parameters in this work were 0.9, 1.2, and 1.5 KW power with continuous wave carbon dioxide lasers with scanning speeds of 10 and 12 mm/s were used. The results found that phase-transitional alterations in microstructure were influenced by lase

Background: Diabetic mellitus (DM) is a collection of metabolic disorder identified by hyperglycemia. The heterogeneous etiology includes defects either in insulin secretion, or in insulin action, or the both. In addition to the distraction in carbohydrate, fat and protein metabolism. Inflammatory reaction that caused by many pro-inflammatory cytokines play a central role in the pathogenicity of T2DM, these cytokines can enhance insulin resistance which led to impaired glucose homeostasis. Subjects: The study included 75 patients (38 males and 37 females) suffering from T2DM with age mean ± SE 52.30 ± 1.60, and 70 individuals as healthy controls (35 males and 35 females) with age mean ± SE 48.88 ± 0.64. Evaluation of immunological marke

The goals of endodontic preparation were to shape and clean the space of the root canal and remove microorganisms, affected dentin and pulp, the apical foramen and the canal curve should be protected from being transported during endodontic canal preparation. The aim of this study was to evaluate the curve straightening of curved root canals and apical transportation after preparation with four rotary systems. Forty mesial roots of the lower 1st molars teeth only the mesiobuccal canals were used, these roots were immersed into cold clear acrylic , the teeth roots divided into four groups according to rotary system used for preparation of the canals (ten roots for each group):. group I: ProTaper Next rotary system, group II: IRaCe Plus rotar

The CuInSe2 (CIS) nanocrystals are synthesized by arrested precipitation from molecular precursors are added to a hot solvent with organic cap- ping ligands to control nanocrystal formation and growth. CIS thin films deposited onto glass substrate by spray - coating, then selenized in Ar- atmosphere to form CIS thin films. PVs were made with power conversion efficiencies of 0.631% as -deposited and 0.846% after selenization, for Mo coated, under AM 1.5 illumination. X-ray diffraction (XRD) and energy dispersive spectroscopy (EDS) analysis it is evident that CIS have the chalcopyrite structure as the major phase with a preferred orientation along (112) direction and the atomic ratio of Cu : In : Se in the nanocrystals is nearly 1 : 1 : 2

The adsorption process of 5-Fluorouracil (5FU) drugs on Aluminum nitride nanotubes surface (AlNNTs) have been evaluated through density functional theory (DFT). The DFT results show that the interaction of AlNNTs with the F atoms of 5FU drugs is strong due to the fact that the amount of adsorption energy was about − 29.65 kcal.mol−1. Conversely, the interaction of the 5FU through O atoms with the AlNNTs was weaker due to the lower value of adsorption energy. Also, based on the values of Gibbs free energy, the 5FU adsorption on the surfaces of AlNNTs was spontaneous. In addition, based on natural bond orbital (NBO) analysis, the direction of charge transfer was from fluorine’s σ orbitals of the drug to nitrogen’s and aluminum’s n*

The new multidentate Schiff-base (E)-6,6′-((1E,1′E)-(ethane-1,2-diylbis(azan-1-yl-1-ylidene))bis(methan-1-yl-ylidene))bis(4-methyl-2-((E)(pyridine-2-ylmethylimino)methyl)phenol) H2L and its polymeric binuclear metal complexes with Cr(III), Mn(II), Fe(II), Co(II), Ni(II), Cu(II), Zn(II), Cd(II) and Hg(II) are reported. The reaction of 2,6-diformyl-4-methyl-phenol with ethylenediamine in mole ratios of 2:1 gave the precursor 3,3′-(1E,1′E)-(ethane-1,2-diylbis(azan-1-yl-1ylidene))bis(methan-1-yl-1-ylidene)bis(2-hydroxy-5-methylbenzaldehyde) W. Condensation of the precursor with 2-(amino-methyl)pyridine in mole ratios of 1:2 gave the new N6O2 multidentate Schiff-base ligand H2L. Upon complex formation, the ligand behaves as a dibasic oct

New polydentate ligand namely bis(N-carboxylatoethyl)-0,0`-dipyridinium) L was synthesised from the reaction of 0,0`-dipyridine with ethyl chloropropionate. Polymeric complexes of general formulae [Cr2(L)(N3)0]Cl2.H2O, Na2[Ag2(L)(N3)0].H2O and [M2(L)(N3)0].nH2O, where (M= Mn(II), Fe(II), Co(II), Ni(II), Cu(II), Zn(II) and Cd(II); (where n = 2;1;1;1;4;1 and 1, respectively)) are reported. The mode of bonding and overall geometry of the complexes were determined through physico-chemical and spectroscopic methods. These studies revealed octahedral geometry complexes. Molecular structure for the complexes has been optimised by CS Chem 3D Ultra Molecular Modelling and Analysis Program and supported a six coordinate geometry.