Objectives: This study aimed to evaluate and compare the effect of plasma treatment versus conventional treatment on the micro shear bond strength (μSBS), surface roughness, and wettability of three different CAD/CAM materials. Materials and methods: Sixty cylindrical specimens (5 mm diameter ×3 mm height) were prepared from three different CAD/CAM materials: Group A: Zirconia, Group B: Lithium disilicate, and Group C: Resin nano-ceramic. Each group was subdivided into two subgroups according to surface treatment used: Subgroup I: Conventional treatment, zirconia was sandblasted with Al2O3, while lithium disilicate and resin nano-ceramic were etched with hydrofluoric acid. Subgroup II: Plasma treatment, the surface of each material was tr

Objective of the study was to rate and analyze the physical fitness of female students from Iraq and Russia to find similarities, differences and regularities. Sampled for the study were 44 female non-sporting students: 20 students from Pedagogical University in Bagdad; and 24 students from Russian State University of Physical Education, Sport, Youth and Tourism in Moscow. The study was designed to obtain the joints flexibility, coordination, speed-strength and static endurance rates. The Iraqi students were tested with higher coordination abilities than their Russian peers, whilst the latter were ranked higher in the speed-strength, shoulder joints and spine flexibility tests, albeit lower than their Iraqi peers in the hip flexibility test

The research aims to get acquainted with the evaluation of the reality of the application of the curriculum axis from among the eight Iraqi academic accreditation standards in a sample of governmental and private universities and colleges in Iraq and to identify the main and secondary reasons for it as well as to provide proposed mechanisms and procedures to help reduce gaps, If the research problem is represented in the weak availability of the requirements of the curriculum axis in universities and colleges (the study sample) due to the weak documentation and successful implementation of them and interest in them is still below the level of ambition, In order to arrive at scientific facts, the researchers adopted the comparativ

the effecth of some chemicals on growth of two azotobacter chroococcum and aniline caused significant increase of growth

   The present research was conducted to synthesis Y-Zeolite by sol-gel technique using MWCNT (multiwalled carbon nanotubes) as crystallization medium to get a narrow range of particle size distribution with small average size compared with ordinary methods. The phase pattern, chemical structure, particle size, and surface area were detected by XRD, FTIR, BET and AFM, respectively. Results shown that the average size of Zeolite with and without using MWCNT were (92.39) nm and (55.17) nm respectively .Particle size range reduced from (150-55) nm to (130-30) nm. The surface area enhanced to be (558) m²/g with slightly large pore volume (0.231) km³/g was obtained. Meanwhile, degree of crystallization decrease

By using vacuum evaporation, thin films of the (CdS)0.75-(PbS)0.25 alloy have been deposited to form a nanocrystalline composite. Investigations were made into the morphology, electrical, optical and I-V characteristics of (CdS)0.75-(PbS)0.25 films asdeposited and after annealing at various temperatures. According to AFM measurements, the values of grain sizes rise as annealing temperatures rise, showing that the films' crystallinity has been increased through heat treatment. In addition, heat treatment results in an increase in surface roughness values, suggesting rougher films that could be employed in more applications. The prepared films have direct energy band gaps, and these band gaps increase with the increase in the degrees

   The present research was conducted to synthesis Y-Zeolite by sol-gel technique using MWCNT (multiwalled carbon nanotubes) as crystallization medium to get a narrow range of particle size distribution with small average size compared with ordinary methods. The phase pattern, chemical structure, particle size, and surface area were detected by XRD, FTIR, BET and AFM, respectively. Results shown that the average size of Zeolite with and without using MWCNT were (92.39) nm and (55.17) nm respectively .Particle size range reduced from (150-55) nm to (130-30) nm. The surface area enhanced to be (558) m2/g with slightly large pore volume (0.231) km3/g was obtained. Meanwhile, degree of crystallization decreased to 120%.