Porcelain is one of the most important ceramic materials with a wide range of traditional and technical applications. Since most mixtures of porcelain have a high sintering temperature, bentonite has been added in this research to improve the characteristics of sintering and burning. The porcelain mixture consisted of the following Iraqi raw materials: 30% wt kaolin, 30 wt% non-plastic clay (grog), 10% wt sodium feldspar, 10 wt% potassium feldspar and 20 wt% flint. After the mechanical mixing process and transfer the powder mixture to the slurry by adding distilled water, then different weight percentage of the sodium bentonite(0, 2.5, 5, 7.5 and 10) wt% was added. The specimens were prepared by using the solid casting m

Alginate from Large brown seaweeds act as natural polymer has been investigated as polymer and has been added to concrete in different percentages ( 0% , 0.5% , 1% and 1.5% ) by the cement weight and the study show the effect of using alginate biopolymer admixtures on  some of the fresh properties of the concrete (slump &  the density  fresh) also in the hardened state (  Compressive strength , Splitting tensile strength  and Flexural strength ) at 28 days. The mix proportion was (1:2.26:2.26) (cement: sand: gravel) respectively and at constant w/c equal to 0.47. The results indicate that the use of alginate as a percent of the cement weight possess a positive effect on fresh properties of co

In This research a Spectroscopic complement and Thermodynamic properties for molecule PO2 were studied . That included a calculation of potential energy . From the curve of total energy for molecule at equilibrium distance , for bond (P-O), the degenerated of bond energy was (4.332eV) instate of the vibration modes of ( PO2 ) molecule and frequency that was found active in IR spectra because variable inpolarization and dipole moment for molecule. Also we calculate some thermodynamic parameters of ( PO2 ) such as heat of formation , enthalpy , heat Of capacity , entropy and gibb's free energy Were ( -54.16 kcal/mol , 2366.45 kcal/mol , 10.06 kcal /k/mol , 59.52 k

Background: Enterococcus faecalis (E. faecalis) is a prototypical resistant bacterium in root canal infections and a leading cause of endodontic treatment failure. German chamomile (Matricaria chamomilla) flower extract has been used as a traditional medicine to treat infections. The aim of this study was to investigate the antimicrobial efficacy of chamomile extract on the removal of E. faecalis root canal biofilm. Materials and Methods: Chamomile flower extract was prepared and subjected to detailed chemical analysis. For the in vitro biofilm model, human mandibular premolars (n=48) with 18-20mm working length were used. Root canal preparation was performed using the ProTaper® Next system. Each sample was split longitudinally and reassem

A new azo (LH) ligand was prepared by coupling reaction between, diazonium salt of Sulfamethoxazole, and 8-hydroxyquinoline in a process called diazotization process resulting in azo-ligand [4-((8-hydroxyquinolin-7-yl)- N(4-methylisoxazol-3-yl) benzene sulfonamide]. The azo ligand was identified by using spectroscopic techniques to detect and characterize the formation of ligand and complexes of Ni2+, Pt4+, Pd2+, and Rh3+ metal ions, and to determine the chelating behavior of ligand and also its bind position. All complexes have a [1:1] [M-ligand] ratio and all complexes are nonelectrolytes and most of the complexes have octahedral geometry, while Pd2+complex gave square planer geometry and Ni2+ complex indicate tetrahedral geometry. Therma

Abstract: The international community now places significant emphasis on achieving zero carbon emissions, requiring both new researchers and experienced policymakers to prioritise this goal. This article examines the effects of carbon taxes, carbon cap and trade, renewable energy (RE) production and consumption, and economic growth (EG) on carbon emission reduction in the United States, Japan, Canada, and Australia. The study collected secondary data from the World Development Indicators (WDI) secondary source spanning the years 1991 to 2022. The study examines the relationship between variables using the cross-sectionally augmented autoregressive distributed lag (CS-ARDL) approach. The findings indicate that carbon taxes, carbon cap and tr

This research investigates the adsorption isotherm and adsorption kinetics of nitrogen from air using packed bed of Li-LSX zeolite to get medical oxygen. Experiments were carried out to estimate the produced oxygen purity under different operating conditions: input pressure of 0.5 – 2.5 bar, feed flow rate of air of 2 – 10 L.min^-1 and packing height of 9-16 cm. The adsorption isotherm was studied at the best conditions of input pressure of 2.5 bar, the height of packing 16 cm, and flow rate 6 Lmin^-1 at ambient temperature, at these conditions   the highest purity of oxygen by this system 73.15 vol % of outlet gas was produced. Langmuir isotherm was the best models representing the experimental data., and the m