Zeolite Y nanoparticles were synthesized by sol - gel method. Dffirent samples using two silica sources were prepared.
Sodium metasilicate (Na2SiO3) (48% silica) and silicic acid silica (H2SiO3) (75% silica) were employed as silica
source and aluminum nitrate (Al(NO3)3.9H2O) was the aluminum source with tetrapropylammonium hydroxide
(TPAOH) as templating agent.
The synihesized-samples were characterized by X-ray diffraction, showed the requirement of diffirent aging time for
complete crystallization to be achieved. Transmission Electronic Microscope (TEM) images, showed the particles were
in the same range of 30 - 75 nm. FT-IR spectroscory, showed the synthesized samples having the zeolite Y crystal
properties. The i

Silver selenide telluride Semiconducting (Ag2Se0.8Te0.2) thin films were by thermal evaporation at RT with thickness350 nm at annealing temperatures (300, 348, 398, and 448) °K for 1 hour on glass substrates .using X-ray diffraction, the structural characteristics were calculated as a function of annealing temperatures with no preferential orientation along any plane. Atomic force microscopy (AFM) and X-ray techniques are used to analyze the Ag2SeTe thin films' physical makeup and properties. AFM techniques were used to analyze the surface morphology of the Ag2SeTe films, and the results showed that the values for average diameter, surface roughness, and grain size mutation increased with annealing temperature (116.36-171.02) nm The transm

This study wass carried out to investigate the incedence of powdery mildew disease on ornamental plants (Nasturtium) Tropaeolum majus L. caused by Oidiopsis haplophylli in some nurseries of Baghdad area and in fields at college of Agriculture /University of Baghdad. This study was conducted in tow succesive seasons of 2011-2012 (April and May). The survey indicated that the Mildew disease existe in the following nurseries (Al-Adhamiya 97.5% ,Palestine street 93.8%, Zayouna 86.0%, and 100% in two fields at college of Agriculture. It has been found that the disease severity was developed in Agriculture college fields successively from 12-4-2011 to 20-5-2011 and from 12-4-2012 to 20-5-2012 (18.0–98.0 % and 22.7–96.0% )for the two sea

Tin dioxide doped silver oxide thin films with different x content (0, 0.03, 0.05, 0.07) have been prepared by pulse laser deposition technique (PLD) at room temperatures (RT). The effect of doping concentration on the structural and electrical properties of the films were studied. Atomic Force Measurement (AFM) measurements found that the average value of grain size for all films at RT decrease with increasing of AgO content. While an average roughness values increase with increasing x content. The electrical properties of these films were studied with different x content. The D.C conductivity for all films increases with increasing x content. Also, it found that activation energies decrease with increasing of AgO content for all films.

The technical of Flame Thermal Spray had been used in producing a cermet
composite based on powders of stabilized zirconium oxide containing amount of
Yatteria oxide (ZrO2- 8Y2O3) reiforced by minerals powders of bonding material
(Ni-Cr- Al- Y) in different rates of additions (25, 35, 50) on stainless steel base type
(304) after preparing it by the way of Grit Blasting.
Before heat treatment, the coated cermet layers were characterized for porosity
and electric resistivity. All samples were heat treated in vacuum furnace at different
temperature and times. The physical tests had been operated after heat treatment
and gave best results especially porosity, which found to be reduced dramatically
and producing hig

This work involves separating and studying the aminoacylase-1 (ACY1) of amniotic fluid from healthy pregnant, mainly one peak with higher activity has been isolated by DEAE-Cellulose ion exchange from the proteinous supernatant produced by deposition of proteins using ammonium sulfate  (65%) after dialysis. The purification folds reaching to 19 folds also gave one protein peak when injected into the gel filtration column, a high ACY1 purity was obtained, with 38 folds of purification. It was found that the molecular weight of the isolated ACY1 was up to 46698 Dalton when using gel chromatography technique.The effect of ACY1 isolate was studied on rats with oxidative stress caused by lead acetate(LA) at 40 mg / kg body weight and compare

In this work, ZnS thin films have been deposited by developed laser deposition technique on glass substrates at room temperature. After deposition process, the films were annealed at different temperatures (200ºC , 300 ºC and 400ºC ) using thermal furnace.The developed technique was used to obtain homogeneous thin films of ZnS depending on vaporization of this semiconductor material by continuous CO2 laser with a simple fan to ensure obtaining homogeneous films. ZnS thin films were annealed at temperature 200ºC, 300 ºC and 400ºC for (20) minute in vacuum environment. Optical properties of ZnS thin film such as absorbance, transmittance, reflectance, optical band gap, refractive index extinction coefficient and absorption coefficien