Some Factors determining the virulence of Escherichia coli ( E. coli ) isolates were studied ,of 25 isolates , 17(group A) uropathogenic E. coli ,6 (group B) infected gastrointestinal tract , 2 (group C) infected wound , beside these group we use the standard strain E. coli HB101 as control group. The twenty five isolates were tested for adherence capability to human buccal cavity epithelial cells by in vitro experiment . The results showed that all isolates have different adhesion capability with mean ranging from (14.35±11.39) to (33.80 ± 22.68) bacteria / epithelial cell It was noticed that isolates EU9, ES6, EW17 displayed high adhesive capability with mean value (33.80 ± 22.68), (32.60 ± 21.19), (29.90±22.50) bacteria /epithelial

The optimum cultural conditions for garamicidin production by local isolate B.brevis were studied.Best result was obtained when the isolate B.brevis was grown on media composed of 1%glucose as carbon source,1% ammonium chloride as a nitrogen source ,0.5% Dipotassium hydrogen orthophosphate as a phosphate source and after 48 hours of incubation at 30C .Garamicidin has been extracted and purified through acid precipition and then extracted by organic solvent (ether& acetone ).Using HPLC the garamicidin antibiotic showed three types A,B and C garamicidin .

This study was designed to determine the effect of bacterial contamination degree and type with Proteus mirabilis alone and Staphylococcus aureus alone and mixed of them species in ejaculation samples of fertile ram semen during storage quality. Semen was collected from six healthy mature rams using electro-ejaculator method, once a week, for the period 1/12/2022 to 1/2/2023. PH, motility (mass and individual), live sperm percentage and abnormal acrosomes of sperms were studied. Isolation and identification of Proteus mirabilis and Staphylococcus aureus species viable bacterial was recorded with routine bacterial detection work and molecular using PCR technique. Semen samples were divided into four groups: Group 1 (G1) was used as control w

Thin films of Nb2O5 have been successfully deposited using the DC reactive magnetron sputtering technique to manufacture NH3 gas sensors. These films have been annealed at a high temperature of 800°C for one hour. The assessment of the Nb2O5 thin films structural, morphological, and electrical characteristics was carried out using several methods such as X-ray diffraction (XRD), atomic force microscopy (AFM), energy-dispersive X-ray spectroscopy (EDS), Hall effect measurements, and sensitivity assessments. The XRD analysis confirms the polycrystalline composition of the Nb2O5 thin films with a hexagonal crystal structure. Furthermore, the sensitivity, response time, and recovery time of the gas sensor were evaluated for the Nb2O5 thin film

Cadmium sulfide and Aluminum doped CdS thin films were prepared by thermal evaporation technique in vacuum on a heated glass substrates at 373K. A comparison between the optical properties of the pure and doped films was made through measuring and analyzing the transmittance curves, and the effect of the annealing temperature on these properties were estimated. All the films were found to exhibit high transmittance in the visible/ near infrared region from 500nm to 1100nm.The optical band gap energy was found to be in the range 2.68-2.60 eV and 2.65-2.44 eV for CdS and CdS:Al respectively , with changing the annealing temperature from room temperature to 423K.Optical constants such as refractive index, extinction coefficient, and complex di

CdSe alloy has been prepared successfully from its high purity elements. Thin films of this alloy with different thicknesses (300,700)nm have been grown on glass substrates at room temperature under very low pressure (10-5)Torr with rate of deposition (1.7)nm/sec by thermal evaporation technique, after that these thin films have been heat treated under low pressure (10-2)Torr at (473,673)K for one hour. X-ray patterns showed that both CdSe alloy and thin films are polycrystalline and have the hexagonal structure with preferential orientation in the [100] and [002] direction respectively. The optical measurements indicated that CdSe thin films have allowed direct optical energy band gap, and it increases from (1.77- 1.84) eV and from

The increasing population growth resulting in the tremendous increase in consumption of fuels, energy, and petrochemical products and coupled with the depletion in conventional crude oil reserves and production make it imperative for Nigeria to explore her bitumen reserves so as to meet her energy and petrochemicals needs. Samples of Agbabu bitumen were subjected to thermal cracking in a tubular steel reactor operated at 10 bar pressure to investigate the effect of temperature on the cracking reaction. The gas produced was analyzed in a Gas Chromatograph while the liquid products were subjected to Gas Chromatography-Mass Spectrometry (GC-MS) analysis. Heptane was the dominant gas produced in bitumen cracking at all temperatures and the r

The corrosion behavior of carbon steel at different Temperatures and in water containing different sodium chloride
concentrations under 3 bar pressure has been investigated using weight loss method . The carbon steel specimens were
immersed in water containing (100,400,700,1000PPM) of NaCl solution and under temperature was increased from
(90-120ºC) under pressures of 3 bar. The results of this investigation indicated that corrosion rate increased with NaCl
concentrations and Temperature.

In the present work, pulsed laser deposition (PLD) technique was applied to a pellet of Chromium Oxide (99.999% pure) with 2.5 cm diameter and 3 mm thickness at a pressure of 5 Tons using a Hydraulic piston. The films were deposited using Nd: YAG laser λ= (4664) nm at 600 mJ and 400 number of shot on a glass substrate, The thickness of the film was (107 nm). Structural and morphological analysis showed that the films started to crystallize at annealing temperature greater than 400 oC. Absorbance and transmittance spectra were recorded in the wavelength range (300-
4400) nm before and after annealing. The effects of annealing temperature on absorption coefficient, refractive index, extinction coefficient, real and imaginary parts of d