Background: The PMMA polymer denture base materials are low in thermal and strength properties. The aim of the study was to investigate the change in glass transition temperature, E-Moudulus and coefficient of thermal expansion of acrylic denture base material by addition of Al2O3, TiO2 and SiO2nano-fillers in 5% by weight. Materials and methods: The type of polymerization is free radical bulk polymerization. one hundred twenty (120) specimens were prepared , the specimens were divided into four groups according to the material had been added (one control and three for Al2O3, TiO2 and SiO2nanocomposite) each group was subdivided in to three groups according to the test had been done on it, the degree of transition (Tg) was measured by The d

Sorption is a key factor in removal of organic and inorganic contaminants from their aqueous solutions. In this study, we investigated the removal of Xylenol Orange tetrasodium salt (XOTS) from its aqueous solution by Bauxite (BXT) and cationic surfactant hexadecyltrimethyl ammonium bromide modified Bauxite (BXT-HDTMA) in batch experiments. The BXT and BXT-HDTMA were characterized using FTIR, and SEM techniques. Adsorption studies were performed at various parameters i.e. temperature, contact time, adsorbent weight, and pH. The modified BXT showed better maximum removal efficiency (98.6% at pH = 9.03) compared to natural Bauxite (75% at pH 2.27), suggesting that BXT-HDTMA is an excellent adsorbent for the removal of XOTS from water. The equ

The experiment was conducted at the faculty of agriculture University of Ain Shams-Egypt, from January to March 2008, to study the effect of different levels of chromium yeast (cr-yeast) on broiler chickens on some physiological traits. A total of 450, one-day old unsexed chickens (Cobb) strain were used. The birds were randomly allocated to five treatments with 3 replicates each. The treatments were control (T1), without supplementation, T2, T3, T4 and T5 which were supplemented with 0.5, 1, 1.5 and 2 mg cr-yeast/kg diet respectively. Chromium yeast supplementation treatments caused a significant (p < 0.05) increase in plasma glucose levels, while supplemented Cr-yeast at levels of 1 (T3), 1.5 (T4), 2 (T5) mg/kg diet resulted in a signific

تعد المحاسبة بشكل عام علماً لكنها ليست من العلوم الصرفة وإنما من العلوم الإجتماعية مما يتطلب للتعامل مع المواضيع المحاسبية الأخذ بنظر الاعتبار الأشخاص المعنيين بالموضوع سواء كانوا المعدين للمخرجات المحاسبية أي المحاسبين، أو الاطراف ذوي المصالح المعنيين والمستفيدين من هذه المخرجات أي المستخدمين، ويعد المحاسب جزءاً من العملية الاجرائية نفسها وبهذا يكون دوره مزدوجاً يجمع بين كونه القائم بالبحث والقي

To achieve sustainability, use waste materials to make concrete to use alternative components and reduce the production of Portland cement. Lime cement was used instead of Portland cement, and 15% of the cement's weight was replaced with silica fume. Also used were eco-friendly fibers (copper fiber) made from recycled electrical. This work examines the impact of utilizing sustainable copper fiber with different aspect ratios (l/d) on some mechanical properties of high-strength green concrete. A high-strength cement mixture with a compressive strength of 65 MPa in line with ACI 211.4R was required to complete the assignment. Copper fibers of 1% by volume of concrete were employed in mixes with four different aspect ratios

CdO:NiO/Si solar cell film was fabricated via deposition of CdO:NiO in different concentrations 1%, 3%, and 5% for NiO thin films in R.T and 723K, on n-type silicon substrate with approximately 200 nm thickness using pulse laser deposition. CdO:NiO/n-Si solar cell photovoltaic properties were examined under 60 mW/cm2 intensity illumination. The highest efficiency of the solar cell is 2.4% when the NiO concentration is 0.05 at 723K.

This in vitro study evaluated the influence of chemomechanical caries removal solution on the surface topography of metal-ceramic feldspar porcelain (MAJOR ceramic) and All-ceramic feldspar porcelain (Vita Alpha) using light polarizing microscope. Forty specimens of MAJOR ceramic and forty specimens of Vita Alpha ceramic of (12mm diameter & 3mm height) were prepared .All specimens were polished with silicon polishing burs, cleaned, autoglazed and stored in 37°C before exposure to Carisolv. Thirty specimens of each material randomly exposed to Carisolv gel for 5, 10 and 20 minutes respectively, other ten specimens were not, to act as control group. All specimens were subjected to surface roughness test by profilometer and evalua