In this work, varying compositions of SiO₂ micro filler were added
with the Polyvinyl Chloride (PVC) and samples have been prepared
using film casting technique. The results have been analyzed and
compared for PVC samples with (1 wt%, 3 wt%, 5 wt% and 10 wt%)
SiO2 micro filler. Mechanical characteristics such as tensile strength,
elongation at break and Young`s modulus were measured for all the
samples, where the tensile strength was increased from 8.39 Mpa for
purified PVC to 16 Mpa for 3% SiO₂/PVC composite. Also, thermal
conductivity measurement values illustrated that composite materials
have a good thermal insulation at 10 wt. %, thermal conductivity was
decreased from 0.1684 W/m.

Background: Poly (methylmethacrylate) is the most widely used material in denture fabrication. The characteristics of acrylic resin which support microorganism development can threaten the oral health of denture users. This study was assigned to prepareand incorporate Ag-Zn zeolite powder into heat cured denture base material as antimicrobial material and to investigate its effect on some properties of heat cured acrylic denture base materials. Materials and methods: Sliver –zinc zeolite was prepared by ion exchange method and characterized then incorporated into poly (methylmethacrylate) powder in0.5% by weight. Specimens were constructed and divided into 6 groups according to the using tests; each group was subdivided into 2 groups

The study was conducted to identify the toxicity of chromium on scenedesmus quadricauda algae alone and in the presence of nutrient metal (Nitrogen). Different concentrations of chromium (0.5, 1.5 , 2.5, 3.5 , 4.5mg/L) were used and the presence nitrogen is (5 ,10 ,50 ,100mg/L) on cultur media(chu-10) with used for cultivation of the algae in controlled conditions(25oC , light intensity 380 –?E/m2 /s. The results showed increasing in the toxicity of the metal when is alone , excess of concentrations an time of exposure. The growth rate decreased from 0.44 to 0.06 cell/ hour after 12 day of the biging of the experiment and of concentrate 4.5 mg/L of chromium. The intermediate active concentrations of the chromium(EC50) was increase

This study was conducted at the poultry research station to the office of Agricultural Research / Ministry of Agriculture / during the period 4/1/2016 to 5/5/2016 and 336 one-day-old Ross308 chicks were used, and fed on diets provided with dried dill (Anethum gravelens) at levels 0.4, 0.6 and 0.8% for treatments D2, D3 and D4, respectively, and they were compared with the control treatment D1. Each treatment included three replicates in each replicate contain 28 birds, in order to study the effect of adding different levels of dried dill plant on the productive performance and some characteristics of the carcass for broilers. The results showed a significant increase (p<0.05) in the average body weight at 5 weeks of age for the treatments (

This study was investigated the role of garlic extracts on the reproductive functions, via the development of immature male mice (25 days old) un l puberty. Immature male mice were divided into 3 groups (n=25). Group 1 "control" was daily administrated with tap water. Group 2 was daily administrated with cold aqueous garlic extract. Group 3 was daily administrated with hot aqueous garlic extract. Each group was randomly consisted of 5 subgroups (n=5/ subgroup) and administrated for different periods i.e, 1, 2, 3, 4 and 5 weeks respectively. Animals were scarified after 24 h from last treatment. Our findings elucidated that, cold and hot aqueous garlic extracts, when administrated at 25 days old (Immature period) have different impact dep

This study was carried out at Poultry Research Station, State Board of Agricultural Research, Ministry of Agriculture for the period from 27 September 2014 to 9 November 2014 to evaluate the Supplementation of different levels of Conjugated Linoleic Acid (CLA) on productive performance of broiler. Four hundred eighty chicks (Ross-308),one day old were randomly distributed to four dietary treatments for 42 days of age with 3 replicates/vtreatment (40 bird/replicate). Experimental treatments were as follow; T1 (Control diet) without supplement, while the treatment T2,T3 and T4  were Supplemented with 1, 1.5, 2 g CLA /kg diet  respectively. The results showed significant (P ≤ 0.05) increased in mean of body weight, weight gain, ave

Four local hemolysin producer bacterial isolates were selected, tow of them gram negative bacteria (Escherichia coli ,Pseudomonas aeruginosa ) and the other two were gram positive bacteria (Staphylococcus aureus , Bacillus cereus ). Minimum inhibitory concentration of the aqueous and alcoholic extracts of Punica granatum L. pericarp were determined towards the four bacterial isolates ,results obtaind showed that MICs of the aqueous extract were 200 mg/ml for E .coli and P. aeruginosa isolates while were 5 mg/ml and 2 mg/ml for B. cereus, S. aureus , respectively The MICs for the ethanolic extract were 50 mg/ml , 20 mg/ml ,1 mg/ml ,0.5 mg/ml for E. coli ,P. aeruginosa ,B. cereus ,S. aureus , respectively. The effect of Sub-MICs o

This study deals with the impact of leadership styles in its three main dimensions (democratic, autocratic, lenient) as an independent variable of the dimensions of functional combustion (emotional stress, inhumanity, personal achievement). The research sought to achieve a set of goals, the most prominent of which are: studying the reality of the researched organization to identify the leadership patterns used in its management and its impact on the phenomenon of functional combustion, Moreover, knowing the extent of support for these established patterns and their contribution to mitigating the phenomenon of functional combustion in the organization's environment, and testing the impact of these leadership patte

Background: This study was formulated to compare the effect of 5%hydrofluoric acid in comparison to 37%phosphoric acid with and without the application of silane on bond strength of composite to porcelain. Materials and Methods: Specimen preparation was divided in to two phases, metal-disks fabrication (8mm-diameter and 4mm-thickness) and ceramic veneering. Thirty two specimens were prepared, sandblasted with 50 μm aluminum oxide, and divided into four groups of eight samples. Groups I and III were etched with 37%phosphoric acid while groups II and IV were etched with 5%hydrofluoric acid; and groups I and II were silaneted while groups III and IV were not. Heliobond, and resin composite were applied to each specimen using a plastic transpa