A new family of nematic liquid crystal dendrimers derived from 3,5-dihydroxybenzoic acid were synthesized. The synthesis of the dendrimers compounds shows the influence of the dendritic core on the mesomorphic properties. The liquid crystalline properties were studied by polarizing optical microscopy (POM) equipped with a hot stage, the structures of the synthesized compounds characterized using FTIR and 1HNMR spectroscopy.

         Melatonin is a potent scavenger of reactive oxygen species or free radicals like superoxide and hydroxyl radicals. The oxidation of hemoglobin to methemoglobin (meth-Hb) by oxidizing compounds has been widely studied. The present work was designed to evaluate the ability of different concentrations of melatonin to inhibit nitrite–induced oxidation of hemoglobin. Blood samples were obtained from apparently healthy individuals from which erythrocyte hemolysate was prepared. Different concentrations of melatonin (10^-9-1.0 mg/ml) were incubated for 10 min with the hemolysate, then to the resultant mixture 1 ml of sodium nitrite (final concentration 0.6 mM) was added, and the

          Aleppo bentonite was investigated to remove ciprofloxacin hydrochloride from aqueous solution. Batch adsorption experiments were conducted to study the several factors affecting the removal process, including contact time, pH of solution, bentonite dosage, ion strength, and temperature. The optimum contact time, pH of solution and bentonite dosage were determined to be 60 minutes, 6 and 0.15 g/50 ml, respectively. The bentonite efficiency in removing CIP decreased from 89.9% to 53.21% with increasing Ionic strength from 0 to 500mM, and it increased from 89% to 96.9% when the temperature increased from 298 to 318 K. Kinetic studies showed that the pseudo second-order model was the best in describing  the adsorption sys

This article includes designed and synthesized for bent-shaped liquid crystal molecules starting from 5,5-diethylpyrimidine-2,4,6(1H,3H,5H)-trione and two moles of chloroacetylchloride in N, N-dimethyl formamide (DMF) and triethylamine (TEA) to product compound [I] ,then reacted the later compound with two moles of 4-hydroxybenzonitrile to yield nitrile compound [II]. Likewise, reaction 5,5-diethylpyrimidine-2,4,6(1H,3H,5H)-trione and two moles of ethylchloroacetate with fused sodium acetate in ethanol to create an ester compound [III], and then the later compound was reacted with two moles of hydrazine hydrate in ethanol to obtained hydrazide acid compound [IV]. After that, the compound [IV] reacted with two moles of ethyl acetoacetate in

Background: Leukemia is a broad term given to a group of malignant diseases characterized by diffuse replacement of bone marrow with proliferating leukocyte precursors. Chemotherapy has been increasingly used to treat malignant conditions. The systemic sequelae as a result of these immunosuppressive techniques induce many oral and dental complications. This study was conducted to evaluate the effect of chemotherapy on oral health status and activity of salivary alkaline phosphates enzyme in patients with acute lymphocytic leukemia. Materials and methods: The study groups included 28 patients with acute lymphocytic leukemia; they were under chemotherapy, aged 20-25 year old. The control group includes healthy subjects matching with study

Abstract In this paper the effect of light exposure duration on Anthracene solution in chloroform is studied. It is found that: the Anthracene solution change its color when it is exposed to light, and that its relative quantum efficiency, Φ, decreases as the light exposure duration, t, increases and this govern by following empirical equation:- Φ = 0.7918-0.0762 In (t)

Corrosion experiments were carried out to investigate the effect of several operating parameters on the corrosion rate and corrosion potential of carbon steel in turbulent flow conditions in the absence and presence of sodium benzoate inhibitor using electrochemical polarization technique. These parameters were rotational velocity (0 - 1.57 m/s), temperature (30oC – 50oC), and time. The effect of these parameters on the corrosion rate and inhibition efficiency were investigated and discussed. It was found that the corrosion rate represented by limiting current increases considerably with increasing velocity and temperature and that it decreased with time due to the formation of corrosion product layer. The corrosion potential shifted t

Introduction: Implant stability is usually measured with resonance frequency analysis (RFA) and damping capacity assessment (DCA). This study aimed to measure primary and secondary stabilities using 3 devices that are based on these methods, namely; RFA (Osstell^®) and DCA (Periotest^® and AnyCheck^®) to assess the correlations of the measurements obtained by these devices and the correlations between implant stability and insertion torque. Material and Methods: This observational prospective study included 35 dental implants. The implant stability was measured using the 3 devices. Mann–Whitney U

In this paper, a polymer-based composite material was prepared by hand Lay-up method consisting of epoxy resin as a base material reinforced by magnesium oxide powder once and silicon dioxide powder again and with different weight ratios (3, 6, 9 and 12) wt %. The three-point bending test was performed in normal conditions and after immersion in sulfuric acid. The results showed that the bending value decreased with the increase of the weighted ratio of the reinforcement material (MgO, SiO2). The Bending of samples reinforced by SiO2 was found to be less than the bending of samples reinforced by particles (MgO). For example, the bending of the SiO2 sample (0.32 mm) at the weighted ratio (3%) and for the MgO (0.18mm) sample at the weight

Mechanical and thermal properties of composites, consisted of unsaturated polyester resin, reinforced by different kinds of natural materials (Orange peels and Date seeds) and industrial materials (carbon and silica) with particle size 98 µm were studied. Various weight ratios, 5, 10, and 15 wt. % of natural and industrial materials have been infused into polyester. Tensile, three-point bending and thermal conductivity tests were conducted for the unfilled polyester, natural and industrial composite to identify the weight ratio effect on the properties of materials. The results indicated that when the weight ratio for polyester with date seeds increased from 10% to 15%, the maximum Young’s modulus decreased by 54%. When the weight rat