Background: Thermocycling simulates the temperature dynamics in the oral environment. This in vitro study done to measure and compare the effect of thermocycling on the shear bond strength of stainless steel and sapphire brackets bonded to human enamel teeth using light cured orthodontic adhesive and debonded at various time, and to measure adhesive remnant index after debonding. Materials and Methods: one-hundred-twenty extracted upper first premolars for orthodontic reason were used in this study; depending on weather thermocycled or not, the sample was divided into two main groups, then within each group 30 teeth were used for stainless-steel brackets (Bionic®) and for sapphire brackets (Pure®). Both groups were subdivided into three

Objective: The aim of this study was to evaluate the effect of pumice, burning investment material
and black sand on the surface roughness of heat cure acrylic resin.
Methodology: Sixty specimens were prepared from pink heat cure acrylic resin, the specimens
where grouped into; 20 specimens which polished with pumice and water (control group); 20
specimens which polished with investment material (after burning it) and water; and 20 specimens
which polished with black sand and water. The average surface roughness of specimens after
polishing procedure had been determined by profilometer (surface roughness tester).
Results: Through the application of ANOVA and LSD tests, the result of this study showed that there
wa

Curcumin is a yellow pigment produced from the rhizomes of the Curcuma longa plant and a primary chemo preventive component of turmeric is used as a spice and food coloring ingredient. Curcumin has a large number of pharmacological activities, such as anticancer, anti-diabetic, antioxidant, anti-infectious, and anti-inflammatory properties.Investigation of the geno-protective effect of curcumin on methotrexate induces chromosomal aberrations of spleen and bone marrow cells. In this study, 32 mice were used and divided into four groups (eight mice at each group) as follows: Group1 (negative control): Dimethyl sulfoxide was given intraperitoneally to mice every day for ten days.Group2 (positive control): Mice were received a single do

Background: The most widely used material for fabrication of denture base is poly methyl methacrylate, despite its popularity, the main problems associated with it as a denture base material are poor strength particularly under fatigue failure inside the patient mouth, impact failure outside the patient mouth, which are the main causes for fracture of denture, several studies was done to increase mechanical properties of denture base. The present study was conducted to evaluate and compare the effect of addition single walled carbon nanotubes in different concentrations to polymethyl methacrylate on some mechanical properties (surface hardness, surface roughness, impact strength and transverse strength). Materials and methods: Forty eight

This study has been carried out in the Station of Poultry Researches which is affiliated to the General Office of Agricultural Researches / Ministry of Agriculture during the period from 01/04/2018 to 14/05/2018 there are 300 one day old chick of type (Ross 308) used in this study, and has been fed on diets which green tea powder (Camellia sinensis) has been added to it with the levels 0.5 , 1 , 1.5 , 2 g/kg as a feed for the treatments T 2 , T 3 , T 4 and T 5 respectively and compared to the control treatment T 1 which is devoid of addition, every treatment included three replicates each one has 20 birds in order to study the effect of adding a various levels of green tea powder (Camellia sinensis) to the diet on the productive performance

Polyacrylamide Solutions of different concentrations (0.2, 0.4, 0.6, 0.8, 1.0 %) of Ag nanoparticles and ZnO nanoparticles were prepared, the viscosities and surface tension were measured for all solutions, where measurements indicated an increase in these properties with increased concentration, where the relative viscosity of polyacrylamide/zinc nanoparticles increased from 1.275 to 2.243, and the relative viscosity of polyacrylamide/silver nanoparticles increased from 1.178 to 1.934. Viscosity is significant parameters during electrospinning process. While the surface tension of the polyacrylamide/zinc nanoparticles has changed from 0.0343 Nm-1 to .0.0.0 Nm-1 and changed from .0.000Nm-1 to.0.0.0 Nm-1. Also the constants KH and KK were

The effect of some environment faetor (different temperature and relative humidity) on the biology of the old world- screw worm, were studied under laboratory condition, the result showed that non of the eggs hatched at 15°c and under dried eondition which relative humidity between 20-40%, also result showed that the mature larvae needs one days to become pupa since it leaves the larval died at the temperature ranged between 25-40°C at different humidity rates. While it needs 3 days under lower temperature and different humidity to become pu^, on the other hand the results showed that either low temperature and dried condition or high temperature at different humidity rates cause non of pupa became adult. While low temperature (15-20) °c

Objective: To evaluate and compare the effect of mechanical surface treatment (groove, aluminum oxide particles)
with 45 degree bevel type of joint on tensile bond strength of acrylic specimens repaired by two curing methods
(microwave and water both).
Methodology: Eighty specimens (80) were prepared from pink heat cure acrylic resin. They were divided into two
main groups (40 specimen repaired by microwave energy and 40 specimens repaired by water bath method).Each
group can be divided into four subgroups of ten according to the surface treatment. The control group A was left
intact, group B received no surface treatment, group C and D received surface treatment by (groove, 50 m aluminum
oxide particles). Specimens

Background: Marginal adaptation is critical for long – term success of crown and bridge restoration. Computer aided design / computer aided manufacture (CAD/ CAM) system is gaining more importance in the fabrication of dental restoration. Objective: The aim of this study is to evaluate the effect of crystallization firing on the vertical marginal gap of IPS. emax CAD crowns which fabricated with two different CAD/CAM systems .Materials and Methods: Twenty IPS e.max CAD crowns were fabricated. We had two major groups (A, B) (10 crowns for each group) according to the CAD/CAM system being used: Group A: fabricated with Imes - Icore CAD/CAM system; Group B: fabricated with In Lab Sirona CAD/CAM system. Each group was subdivided into two s