GH and IGF-2 were examined histologically in the present study on adult hens to learn more about the organs’ responses to GH and IGF-2. Cardiac protein synthesis is stimulated by GH and IGF-2, according to microscopic examination. The recent research found a considerable amount of adipose tissue in the cardiac muscle bundles, which is linked to the metabolic process. In addition, GH and IGF-2 were shown to promote protein synthesis and mitosis in liver and gizzard tissues, according to the research. In addition, the apoptosis, regeneration, and secretory activity of gizzard glands are increased by the aforementioned hormones.

The current research reports the preparation and fabrication of the silver paste conductor which is employed as a soldering material for electro – optical components ohmic interconnections. The prepared paste possesses electrical characteristics identical to the ohmic connectors as its observable from resistance – temperature variation. Moreover, the I – V characteristics obeys Ohm’s law and this dependency was further confirmed by the nearly constant capacitance measurements with voltage and frequency. A noticeable improvement in electrical conductivity, compared to the pure silver paste sample, was noted for samples prepared by mixing predetermined weight ratios of brass and copper. Furthermore, stability of electrical resistan

Abstract

Backgrounds: Jaundice occurs in most newborn due to increased bilirubin concentration. Jaundice is observed during the first week after birth in approximately 60% of term neonates. A high level of bilirubin is neurotoxic and may cause neonatal kernicterus, auditory neuropathy or death.

Objectives: to compare the Rh group compatibility, serum bilirubin (total and direct), serum albumin and several liver enzymes between physiological and pathological neonatal jaundice

Materials and Methods: A cross sectional study for one hundred neonates with jaundice divided into group 1: 50 newborns with physiological jaundice, Group 2: 50 newborns with

A Schiff base ligand (L) was synthesized via condensation of N-( 1-naphthyl) ethylenediamine dihydrochloride with phthalaldehyde. The ligand was characterized by FT-IR, UV–Vis, 1H NMR, mass spectrometry, and elemental analysis (C, H, N). Five metal complexes (Co(II), Ni(II), Cu(II), Zn(II), and Cd(II)) were prepared with the ligand in a 1:1 (M:L) ratio using an aqueous ethanol solution. The complexes were characterized by FT-IR, UV–Vis, mass spectrometry, and elemental analysis (C, H, N). Additionally, 1H NMR spectroscopy was employed for Cd(II) complex. Antimicrobial activity of the ligand and its metal complexes against pathogenic bacteria (K. pneumoniae, E. coli, S. aureus, and S. epidermidis) and fungus (C. albicans) were evaluated

Structural and optical properties of CdO and CdO0.99Cu0.01 thin
films were prepared in this work. Cadmium Oxide (CdO) and
CdO0.99Cu0.01semiconducting films are deposited on glass substrates
by using pulsed laser deposition method (PLD) using SHG with Qswitched
Nd:YAG pulsed laser operation at 1064nm in 6x10-2 mbar
vacuum condition and frequency 6 Hz. CdO and CdO0.99Cu0.01 thin
films annealed at 550 C̊ for 12 min. The crystalline structure was
studied by X-ray diffraction (XRD) method and atomic force
microscope (AFM). It shows that the films are polycrystalline.
Optical properties of thin films were analyzed. The direct band gap
energy of CdO and CdO0.99Cu0.01 thin films were determined from
(αhυ)1/2 v

       Most of the cinema and television production relies on the use of modern digital technologies, which today become the as ideal as the artistic expressive style that sends aesthetic values ​​through the use of electronic elements of the language of cinema and television to achieve aesthetic dazzling, and design the digital production for the purpose of persuasion, as well as the use of digital effects and graphics to activate the aesthetic pleasure. The research tries to subject all these aspetcs to study and apply them to a modern sample in order to get the results that confirm this technical and artistic aesthetic synergy that leads to the emergence of a cinema and television achievement the leas

The influence of pre- shot peening and welding parameters on mechanical and metallurgical properties of dissimilar and similar aluminum alloys AA2024-T3 and AA6061-T6 joints using friction stir welding have been studied. In this work, numbers of plates were equipped from sheet alloys in dimensions (150*50*6) mm then some of them were exposed to shot peening process before friction stir welding using steel ball having diameter 1.25 mm for period of 15 minutes. FSW joints were manufactured from plates at three welding speeds (28, 40, 56 mm/min) and welding speed 40mm/min was chosen at a rotating speed of 1400 rpm for welding the dissimilar pre- shot plates. Tow joints were made at rotational speed of 1000 rpm and welding speed of 40m/min f