In this research a local adsorbent was prepared from waste tires using two-step pyrolysis method. In the carbonization process, nitrogen gas flow rate was 0.2L/min at carbonization temperature of 500ºC for 1h. The char products were then preceded to the activation process at 850°C under carbon dioxide (CO2) activation flow rate of 0.6L/min for 3h. The activation method produced local adsorbent material with a surface area and total pore volume as high as 118.59m2 /g and 0.1467cm3/g, respectively. The produced . local adsorbent (activated carbon) was used for adsorption of lead from aqueous solution. The continuous fixed bed column experiments were conducted. The adsorption capacity performance of prepared activated carbons in this work

Background and aim: Pomegranate is a medicinal herb that can promote healing of periodontal tissue through differentiation of mesenchymal cells both in vivo and in vitro. Therefore, this study is to investigate the effect of oral supplementation of Punicagranatum L. peel extract on bone defect in rabbit. Methods: Forty five male rabbits were divided into 3 groups; group 1; baseline group(5 rabbits) left without bone defect. Group 2; study group (20 rabbits) with bone defect model that received daily 1ml of oral supplementation of pomegranate peel extract (PoPx). Group 3; control group (20 rabbits) with bone defect model that received distilled water. Bone defect was done into facial plate of lower right central incisor. Blood biopsies by

The present research aims to study the effect of friction stir welding (FSW) parameters on temperature distribution and tensile strength of aluminum 6061-T6. Rotational and traverse speeds used were (500,1000,1400 rpm) and (14,40,112 mm/min) respectively. Results of mechanical tests showed that using 500rpm and 14mm/min speed give the best strength. A three- dimensional fully coupled thermal-stress finite element model via ANSYS software has been developed. The Rate dependent Johnson-Cook relation was utilized for elasto-plastic work deformations. Heat-transfer is formulated using a moving heat source, and later used the transient temperature outputs from the thermal analysis to determine equivalent stresses in the welde

A study of the effects of the discharge (sputtering) currents (60-75 mA) and the thickness of copper target (0.037, 0.055 and 0.085 mm) on the prepared samples was performed. These samples were deposited with pure copper on a glass substrate using dc magnetron sputtering with a magnetic flux density of 150 gauss at the center. The effects of these two parameters were studied on the height, diameter, and size of the deposition copper grains as well as the roughness of surface samples using atomic force microscopy (AFM).The results of this study showed that it is possible to control the specifications of copper grains by changing the discharge currents and the thickness of the target material. The increase in discharge curre

This study aimed to isolate and identifye the growth of microorganisms and
their effect on pickled cucumber and cabbage, the study also investigated the effect of
garlic (in the form of segments, chopped or crushed) on the mentioned pickled –food
features . Furthermore, a sense based comparison is made between vinegar-preserved
samples and vinegar-garlic preserved ones.
The following results have been obtained:
1- The isolation of staph. aureus alone from the samples and the study of its physical
and biochemical features.
2- The fresh garlic (segments, chopped and crushed) with concentration of 5%, 7.5%,
and 10% showed a damaging percentage of 100% to bacterial growth of staph. Aureus
after 24 hours of inc

Background: Alginate impression material is the irreversible hydrocolloid material that is widely used in dentistry. The contact time between alginate and gypsum cast could have a detrimental effect on the properties of the gypsum cast. The objective of this study is to evaluate the impact of various contact time intervals of Alginate impressions & type III dental stone on surface properties of stone cast. Materials and Methods: Time intervals tested were 1hour, 6 hours and 9 hours. Surface properties of stone cast evaluated were surface detail reproduction, hardness and roughness. Surface detail reproduction was determined using cylindrical brass test block in accordance with ISO 1563. Surface roughness was measured by profilometer

In the last decades, using mineral admixture in concrete became very necessary to improve concrete properties and reduce CO₂ emissions associated with the cement production process. Subsequently, more sustainable concrete can be obtained.  Ternary blended cement containing two different types of mineral admixture can achieve ambitious steps in this trend. In this research, the synergic effects of mineral admixtures in ternary blended cement and its effects on concrete fresh properties, strength, durability, and efficiency factors of mineral admixture in ternary blended cement, were reviewed. The main conclusion reached after reviewing many literature pieces is that the concrete with ternary blended cement