This study involves the design of 24 mixtures of fiber reinforced magnetic reactive powder concrete containing nano silica. Tap water was used for 12 of these mixtures, while magnetic water was used for the others. The nano silica (NS) with ratios (1, 1.5, 2, 2.5 and 3) % by weight of cement, were used for all the mixtures. The results have shown that the mixture containing 2.5% NS gives the highest compressive strength at age 7 days. Many different other tests were carried out, the results have shown that the carbon fiber reinforced magnetic reactive powder concrete containing 2.5% NS (CFRMRPCCNS) had higher compressive strength, modulus of rupture, splitting tension, str

One of the most essential components of asphalt pavements is the filler. It serves two purposes. First, this fine-grained material (diameter less than 0.075 mm) improves the cohesiveness of aggregate with bitumen. Second, produce a dense mixture by filling the voids between the particles. Aluminum dross (AD), which is a by-product of aluminum re-melting, is formed all over the world. This material causes damage to humans and the environment; stockpiling AD in landfills is not the best solution. This research studies the possibility of replacing part of the conventional filler with aluminum dross. Three percent of dross was used, 10, 20, and 30% by filler weight. The MarshallMix design method was adopted to obtain the op

Wet granulation method was used instead of conventional pan coating  or fluidized –bed coating technique to prepare enteric-coated diclofenac sodium granules, using ethanolic solution of Eudragit^TM L100 as coating, binding and granulating agent .Addition of PEG400 or di-n-butyl phthalate as a plasticizer was found to improve the enteric property of the coat.

Part of the resulted granules was filled in hard gelatin capsules (size 0), while the other part was compressed into tablets with and without disintegrant.

The release profile of these two dosage forms in 0.1N HCl (pH 1.2)for 2 hours, and in phosphate buffer (pH 6.8) for 45 minutes as well as the release kinetic were compared with that of the en

diasotiation compondnds sulphate upon with melting elemental aryl been used in his mouth for a while of studied

I attended some amides non grassy substitutes such as acrylic compounds Amaid Electron Amaid and Alsinamamaid interaction unsaturated acids such as acrylic acid or Ketronk ????????? with primary amines Malkhtlfah of acrylic monomers Alamayd

Well dispersed Cu2FeSnSe4 (CFTSe) nanofilms were synthesized by hot-injection method. The structural and morphological measurements were characterized using XRD (X-ray diffraction), Raman spectroscopy, SEM (scanning electron microscopy), and TEM (transmission electron microscopy). Chemical composition and optical properties of as-synthesized CFTSe nanoparticles were characterized using EDS (energy dispersive spectroscopy) and UV-Vis spectrophotometry. The average particle size of the nanoparticles was about 7-10 nm. The UV-Vis absorption spectra showed that the synthesized CFTS nanofilms have a band gap (Eg) of about 1.16 eV. Photo-electrochemical characteristics of CFTSe nanoparticles were studied and indicated their potential application

The MTX was converted to MTX nanoparticles by the modified method based on changing the pH gradually with exposure to ultrasound and shaking , changing the pH with exposure to ultrasound plays an significant role in the formation of nanoparticles, and this is shown in some previous studies. As the change in pH affects the nature of bonding between molecules, as well as the strength of bonding that depends on the change of electrical charges The exposure to ultrasound waves will greatly affect the breakdown of large particles into small particles that reach the level of nanoparticles. The MTX NPs formation was characterized by UV-Vis spectra analysis , Atomic force microscopy (AFM) analysis, Scanning electron microscope (SEM) and Fou

Due to economic reasons or need for environmental conservatism or also preserve the natural resources; there has been an increasing shift towards the use of reclaimed asphalt pavement (RAP) materials in the pavement construction industry. Therefore, use the Reclaimed Asphalt Pavement (RAP) has been enormously increased in pavement construction and has been become common practice in many countries. Nevertheless, this is a relatively new concept in Iraq, and has to be remarked that is not used RAP in the production of HMA and this valuable material is mostly degraded. For this purpose, the reclaimed materials were collected from deteriorated pavement segments. The components of asphalt mixtures consist of: two asphalt penetration grades (40-5

Tetradentate complexes type [M (HL) 2] were prepared from the reaction of 2-hydroxy -1, 2-diphynel-ethanone oxime [H2L] and KOH with ( Mn II, Fe II, Co II, Ni II , Cu II and Hg II ), in methanol with (2:1) metal: ligand ratio. The general formula for Cu II and Mn II complexes are [M (HL) 2 Cl.H2O] K, for Co II [Co (HL) 2. H2O] and [M (HL) 2] for the rest of complexes. All compounds were characterised by spectroscopic methods, I.R, U.V-Vis, H.P.L.C, atomic absorption and conductivity measurements chloride content. From the data of these measurements, the proposed molecular structures for Fe II and Hg II complexes are tetrahedrals, while Mn II and Cu II complexes are octahedrals, Ni II complex adopting square planar structure and the complex